The early failure and revision of bimodular primary
total hip arthroplasty prostheses requires the identification of the
risk factors for material loss and wear at the taper junctions through
taper wear analysis. Deviations in taper geometries between revised
and pristine modular neck tapers were determined using high resolution
tactile measurements. A new algorithm was developed and validated
to allow the quantitative analysis of material loss, complementing
the standard visual inspection currently used. The algorithm was applied to a sample of 27 retrievals ( Cite this article:
Head-taper corrosion is a cause of failure in total hip arthroplasty (THA). Recent reports have described an increasing number of V40 taper failures with adverse local tissue reaction (ALTR). However, the real incidence of V40 taper damage and its cause remain unknown. The aim of this study was to evaluate the long-term incidence of ALTR in a consecutive series of THAs using a V40 taper and identify potentially related factors. Between January 2006 and June 2007, a total of 121 patients underwent THA using either an uncemented (Accolade I, made of Ti12Mo6Zr2Fe; Stryker, USA) or a cemented (ABG II, made of cobalt-chrome-molybdenum (CoCrMo); Stryker) femoral component, both with a V40 taper (Stryker). Uncemented acetabular components (Trident; Stryker) with crosslinked polyethylene liners and CoCr femoral heads of 36 mm diameter were used in all patients. At a mean folllow-up of 10.8 years (SD 1.1), 94 patients (79%) were eligible for follow-up (six patients had already undergone a revision, 15 had died, and six were lost to follow-up). A total of 85 THAs in 80 patients (mean age 61 years (24 to 75); 47 (56%) were female) underwent clinical and radiological evaluation, including the measurement of whole blood levels of cobalt and chrome. Metal artifact reduction sequence MRI scans of the hip were performed in 71 patients.Aims
Methods
This study reports the ten-year wear rates, incidence of osteolysis, clinical outcomes, and complications of a multicentre randomized controlled trial comparing oxidized zirconium (OxZr) versus cobalt-chrome (CoCr) femoral heads with ultra-high molecular weight polyethylene (UHMWPE) and highly cross-linked polyethylene (XLPE) liners in total hip arthroplasty (THA). Patients undergoing primary THA were recruited from four institutions and prospectively allocated to the following treatment groups: Group A, CoCr femoral head with XLPE liner; Group B, OxZr femoral head with XLPE liner; and Group C, OxZr femoral head with UHMWPE liner. All study patients and assessors recording outcomes were blinded to the treatment groups. The outcomes of 262 study patients were analyzed at ten years’ follow-up.Aims
Methods
The aim of this study was to evaluate the incidence of liner malseating in two commonly used dual-mobility (DM) designs. Secondary aims included determining the risk of dislocation, survival, and clinical outcomes. We retrospectively identified 256 primary total hip arthroplasties (THAs) that included a DM component (144 Stryker MDM and 112 Zimmer-Biomet G7) in 233 patients, performed between January 2012 and December 2019. Postoperative radiographs were reviewed independently for malseating of the liner by five reviewers. The mean age of the patients at the time of THA was 66 years (18 to 93), 166 (65%) were female, and the mean BMI was 30 kg/m2 (17 to 57). The mean follow-up was 3.5 years (2.0 to 9.2).Aims
Methods
To determine if primary cemented acetabular component geometry (long posterior wall (LPW), hooded, or offset reorientating) influences the risk of revision total hip arthroplasty (THA) for instability or loosening. The National Joint Registry (NJR) dataset was analyzed for primary THAs performed between 2003 and 2017. A cohort of 224,874 cemented acetabular components were included. The effect of acetabular component geometry on the risk of revision for instability or for loosening was investigated using log-binomial regression adjusting for age, sex, American Society of Anesthesiologists grade, indication, side, institution type, operating surgeon grade, surgical approach, polyethylene crosslinking, and prosthetic head size. A competing risk survival analysis was performed with the competing risks being revision for other indications or death.Aims
Methods
The aim of this study was to evaluate the performance of first-generation annealed highly cross-linked polyethylene (HXLPE) in cementless total hip arthroplasty (THA). We retrospectively evaluated 29 patients (35 hips) who underwent THA between December 2000 and February 2002. The survival rate was estimated using the Kaplan-Meier method. Hip joint function was evaluated using the Japanese Orthopaedic Association (JOA) score. Two-dimensional polyethylene wear was estimated using Martell’s Hip Analysis Suite. We calculated the wear rates between years 1 and 5, 5 and 10, 10 and 15, and 15 and final follow-up.Aims
Methods
The aim of our study was to investigate the effect of asymmetric crosslinked polyethylene liner use on the risk of revision of cementless and hybrid total hip arthroplasties (THAs). We undertook a registry study combining the National Joint Registry dataset with polyethylene manufacturing characteristics as supplied by the manufacturers. The primary endpoint was revision for any reason. We performed further analyses on other reasons including instability, aseptic loosening, wear, and liner dissociation. The primary analytic approach was Cox proportional hazard regression.Aims
Methods
The aim of this study was to determine if uncemented acetabular polyethylene (PE) liner geometry, and lip size, influenced the risk of revision for instability or loosening. A total of 202,511 primary total hip arthroplasties (THAs) with uncemented acetabular components were identified from the National Joint Registry (NJR) dataset between 2003 and 2017. The effect of liner geometry on the risk of revision for instability or loosening was investigated using competing risk regression analyses adjusting for age, sex, American Society of Anesthesiologists grade, indication, side, institution type, surgeon grade, surgical approach, head size, and polyethylene crosslinking. Stratified analyses by surgical approach were performed, including pairwise comparisons of liner geometries.Aims
Methods
Modular dual mobility (MDM) acetabular components are often used with the aim of reducing the risk of dislocation in revision total hip arthroplasty (THA). There is, however, little information in the literature about its use in this context. The aim of this study, therefore, was to evaluate the outcomes in a cohort of patients in whom MDM components were used at revision THA, with a mean follow-up of more than five years. Using the database of
a single academic centre, 126 revision THAs in 117 patients using a single
design of an MDM acetabular component were retrospectively reviewed. A total of 94 revision THAs in 88 patients with a mean follow-up of 5.5 years were included in the study. Survivorship was analyzed with the endpoints of dislocation, reoperation for dislocation, acetabular revision for aseptic loosening, and acetabular revision for any reason. The secondary endpoints were surgical complications and the radiological outcome.Aims
Methods
The aim of this study was to develop a novel computational model for estimating head/stem taper mechanics during different simulated assembly conditions. Finite element models of generic cobalt-chromium (CoCr) heads on a titanium stem taper were developed and driven using dynamic assembly loads collected from clinicians. To verify contact mechanics at the taper interface, comparisons of deformed microgroove characteristics (height and width of microgrooves) were made between model estimates with those measured from five retrieved implants. Additionally, these models were used to assess the role of assembly technique—one-hit versus three-hits—on the taper interlock mechanical behaviour.Aims
Methods
This study aimed to determine if macrophages can attach and directly affect the oxide layers of 316L stainless steel, titanium alloy (Ti6Al4V), and cobalt-chromium-molybdenum alloy (CoCrMo) by releasing components of these alloys. Murine peritoneal macrophages were cultured and placed on stainless steel, CoCrMo, and Ti6Al4V discs into a 96-well plate. Cells were activated with interferon gamma and lipopolysaccharide. Macrophages on stainless steel discs produced significantly more nitric oxide (NO) compared to their control counterparts after eight to ten days and remained elevated for the duration of the experiment.Aims
Methods
The aim of this study was to identify the effect of the manufacturing characteristics of polyethylene acetabular liners on the survival of cementless and hybrid total hip arthroplasty (THA). Prospective cohort study using linked National Joint Registry (NJR) and manufacturer data. The primary endpoint was revision for aseptic loosening. Cox proportional hazard regression was the primary analytical approach. Manufacturing variables included resin type, crosslinking radiation dose, terminal sterilization method, terminal sterilization radiation dose, stabilization treatment, total radiation dose, packaging, and face asymmetry. Total radiation dose was further divided into G1 (no radiation), G2 (> 0 Mrad to < 5 Mrad), G3 (≥ 5 Mrad to < 10 Mrad), and G4 (≥ 10 Mrad).Aims
Methods
The aim of this study was to evaluate fretting and corrosion in retrieved oxidized zirconium (OxZr; OXINIUM, Smith & Nephew, Memphis, Tennessee) femoral heads and compare the results with those from a matched cohort of cobalt-chromium (CoCr) femoral heads. A total of 28 OxZr femoral heads were retrieved during revision total hip arthroplasty (THA) and matched to 28 retrieved CoCr heads according to patient demographics. The mean age at index was 56 years (46 to 83) in the OxZr group and 70 years (46 to 92) in the CoCr group. Fretting and corrosion scores of the female taper of the heads were measured according to the modified Goldberg scoring method.Aims
Patients and Methods
The aim of this study was to determine whether there is a difference
in the rate of wear between acetabular components positioned within
and outside the ‘safe zones’ of anteversion and inclination angle. We reviewed 100 hips in 94 patients who had undergone primary
total hip arthroplasty (THA) at least ten years previously. Patients
all had the same type of acetabular component with a bearing couple
which consisted of a 28 mm cobalt-chromium head on a highly crosslinked
polyethylene (HXLPE) liner. A supine radiostereometric analysis
(RSA) examination was carried out which acquired anteroposterior
(AP) and lateral paired images. Acetabular component anteversion
and inclination angles were measured as well as total femoral head
penetration, which was divided by the length of implantation to
determine the rate of polyethylene wear.Aims
Patients and Methods
To present a surgically relevant update of trunnionosis. Systematic review performed April 2017.Aims
Materials and Methods
We sought to determine whether cobalt-chromium alloy (CoCr) femoral
stem tapers (trunnions) wear more than titanium (Ti) alloy stem
tapers (trunnions) when used in a large diameter (LD) metal-on-metal
(MoM) hip arthroplasty system. We performed explant analysis using validated methodology to
determine the volumetric material loss at the taper surfaces of
explanted LD CoCr MoM hip arthroplasties used with either a Ti alloy
(n = 28) or CoCr femoral stem (n = 21). Only 12/14 taper constructs
with a rough male taper surface and a nominal included angle close
to 5.666° were included. Multiple regression modelling was undertaken
using taper angle, taper roughness, bearing diameter (horizontal
lever arm) as independent variables. Material loss was mapped using
a coordinate measuring machine, profilometry and scanning electron
microscopy.Aims
Patients and Methods
Surgeons have commonly used modular femoral heads and stems from
different manufacturers, although this is not recommended by orthopaedic
companies due to the different manufacturing processes. We compared the rate of corrosion and rate of wear at the trunnion/head
taper junction in two groups of retrieved hips; those with mixed
manufacturers (MM) and those from the same manufacturer (SM). We identified 151 retrieved hips with large-diameter cobalt-chromium
heads; 51 of two designs that had been paired with stems from different
manufacturers (MM) and 100 of seven designs paired with stems from
the same manufacturer (SM). We determined the severity of corrosion
with the Goldberg corrosion score and the volume of material loss
at the head/stem junction. We used multivariable statistical analysis
to determine if there was a significant difference between the two
groups. Aims
Materials and Methods
Tribocorrosion at the head–neck taper interface
– so-called ‘taperosis’ – may be a source of metal ions and particulate
debris in metal-on-polyethylene total hip arthroplasty (THA). We examined the effect of femoral head length on fretting and
corrosion in retrieved head–neck tapers Head length was observed to affect fretting (p = 0.03), with
28 mm + 8 mm femoral heads showing greater total fretting scores
than all other head lengths. The central zone of the femoral head
bore taper was subject to increased fretting damage (p = 0.01),
regardless of head length or stem offset. High-offset femoral stems
were associated with greater total fretting of the bore taper (p
= 0.04). Increased fretting damage is seen with longer head lengths and
high-offset femoral stems, and occurs within a central concentric
zone of the femoral head bore taper. Further investigation is required
to determine the effect of increased head size, and variations in
head–neck taper design. Cite this article:
We report the five-year outcome of a randomised
controlled trial which used radiostereometric analysis (RSA) to assess
the influence of surface oxidised zirconium (OxZr, Oxinium) on polyethylene
wear A total of 120 patients, 85 women and 35 men with a mean age
of 70 years (59 to 80) who were scheduled for primary cemented total
hip arthroplasty were randomly allocated to four study groups. Patients
were blinded to their group assignment and received either a conventional
polyethylene (CPE) or a highly cross-linked (HXL) acetabular component
of identical design. On the femoral side patients received a 28
mm head made of either cobalt-chromium (CoCr) or OxZr. The proximal head penetration (wear) was measured with repeated
RSA examinations over five years. Clinical outcome was measured
using the Harris hip score. There was no difference in polyethylene wear between the two
head materials when used with either of the two types of acetabular
component (p = 0.3 to 0.6). When comparing the two types of polyethylene
there was a significant difference in favour of HXLPE, regardless
of the head material used (p <
0.001). In conclusion, we found no advantage of OxZr over CoCr in terms
of polyethylene wear after five years of follow-up. Our findings
do not support laboratory results which have shown a reduced rate
of wear with OxZr. They do however add to the evidence on the better
resistance to wear of HXLPE over CPE. Cite this article:
Oxidised zirconium (OxZi) has been developed
as an alternative bearing surface for femoral heads in total hip arthroplasty
(THA). This study has investigated polyethylene wear, functional
outcomes and complications, comparing OxZi and cobalt–chrome (CoCr)
as part of a three-arm, multicentre randomised controlled trial.
Patients undergoing THA from four institutions were prospectively
randomised into three groups. Group A received a CoCr femoral head
and highly cross-linked polyethylene (XLPE) liner; Group B received
an OxZi femoral head and XLPE liner; Group C received an OxZi femoral
head and ultra-high molecular weight polyethylene (UHMWPE) liner.
At five years, 368 patients had no statistically significant differences
in short-form-36 (p = 0.176 mental, p = 0.756 physical), Western
Ontario and McMaster Universities Osteoarthritis Index (p = 0.847),
pain scores
(p = 0.458) or complications. The mean rate of linear wear was 0.028
mm/year (standard deviation ( Cite this article: