Aims

We conducted a prospective study of a delta ceramic total hip arthroplasty (THA) to determine the rate of ceramic fracture, to characterise post-operative noise, and to evaluate the mid-term results and survivorship.

Aims. Ceramic-on-ceramic (CoC) bearings in total hip arthroplasty (THA) are commonly used, but concerns exist regarding ceramic fracture. This study aims to report the risk of revision for fracture of modern CoC bearings and identify factors that might influence this risk, using data from the National Joint Registry (NJR) for England, Wales, Northern Ireland and the Isle of Man. Patients and Methods. We analysed data on 223 362 bearings from 111 681 primary CoC THAs and 182 linked revisions for bearing fracture recorded in the NJR. We used implant codes to identify ceramic bearing composition and generated Kaplan-Meier estimates for implant survivorship. Logistic regression analyses were performed for implant size and patient specific variables to determine any associated risks for revision. Results. A total of 222 852 bearings (99.8%) were CeramTec Biolox products. Revisions for fracture were linked to seven of 79 442 (0.009%) Biolox Delta heads, 38 of 31 982 (0.119%) Biolox Forte heads, 101 of 80 170 (0.126%) Biolox Delta liners and 35 of 31 258 (0.112%) Biolox Forte liners. Regression analysis of implant size revealed smaller heads had significantly higher odds of fracture (chi-squared 68.0, p < 0.001). The highest fracture risk was observed in the 28 mm Biolox Forte subgroup (0.382%). There were no fractures in the 40 mm head group for either ceramic type. Liner thickness was not predictive of fracture (p = 0.67). Body mass index (BMI) was independently associated with revision for both head fractures (odds ratio (OR) 1.09 per unit increase, p = 0.031) and liner fractures (OR 1.06 per unit increase, p = 0.006). . Conclusions. We report the largest independent study of CoC bearing fractures to date. The risk of revision for CoC bearing fracture is very low but previous studies have underestimated this risk. There is good evidence that the latest generation of ceramic has greatly reduced the odds of head fracture but not of liner fracture. Small head size and high patient BMI are associated with an increased risk of ceramic bearing fracture. Cite this article: Bone Joint J 2017;99-B:1012–19

Aims

To achieve the functional benefits of the direct anterior (DA) approach and the fixation benefits of cemented replacement, this study combined the two techniques posing the following questions: does the limited access of the DA approach adversely affect the cement technique?; and does such a cementing technique reduce the incidence of cementless complications?

Aims

The purpose of this study is to examine six types of bearing surfaces implanted at a single institution over three decades to determine whether the reasons for revision vary among the groups and how long it takes to identify differences in survival.

Ceramic bearings have several desirable properties, such as resistance to wear, hardness, and biocompatibility, that favour it as an articulating surface in hip arthroplasty. However, ceramic fracture remains a concern. We have reviewed the contemporary literature, addressing the factors that can influence the incidence of ceramic bearing surface fracture.

Cite this article: Bone Joint J 2019;101-B:897–901.

We compared the clinical and radiological outcomes of two cementless femoral stems in the treatment of patients with a Garden III or IV fracture of the femoral neck. A total of 70 patients (70 hips) in each group were enrolled into a prospective randomised study. One group received a short anatomical cementless stem and the other received a conventional cementless stem. Their mean age was 74.9 years (50 to 94) and 76.0 years (55 to 96), respectively (p = 0.328). The mean follow-up was 4.1 years (2 to 5) and 4.8 years (2 to 6), respectively. Perfusion lung scans and high resolution chest CTs were performed to detect pulmonary microemboli.

At final follow-up there were no statistically significant differences between the short anatomical and the conventional stems with regard to the mean Harris hip score (85.7 (66 to 100) versus 86.5 (55 to 100); p = 0.791), the mean Western Ontario and McMaster Universities Osteoarthritis Index (17 (6 to 34) versus 16 (5 to 35); p = 0.13) or the mean University of California, Los Angeles activity score (5 (3 to 6) versus 4 (3 to 6); p = 0.032). No patient with a short stem had thigh pain, but 11 patients (16%) with a conventional stem had thigh pain. No patients with a short stem had symptomatic pulmonary microemboli, but 11 patients with a conventional stem had pulmonary microemboli (symptomatic in three patients and asymptomatic in eight patients). One hip (1.4%) in the short stem group and eight (11.4%) in the conventional group had an intra-operative undisplaced fracture of the calcar. No component was revised for aseptic loosening in either group. One acetabular component in the short stem group and two acetabular components in the conventional stem group were revised for recurrent dislocation.

Our study demonstrated that despite the poor bone quality in these elderly patients with a fracture of the femoral neck, osseo-integration was obtained in all hips in both groups. However, the incidence of thigh pain, pulmonary microemboli and peri-prosthetic fracture was significantly higher in the conventional stem group than in the short stem group.

We reviewed the results of 84 total hip replacements performed with a short metaphyseal-fitting anatomical cementless femoral component in 84 unselected consecutive patients with a mean age of 78.9 years (70 to 88). The mean follow-up was 4.6 years (4 to 5). The mean pre-operative Harris hip score was 26 points (0 to 56), which improved to 89 (61 to 100) at the final follow-up. No patient had thigh pain. The mean pre-operative Western Ontario and McMaster Universities osteoarthritis index score was 61 points (48 to 75), which improved to 21 (6 to 46). The mean University of California, Los Angeles activity score was 5.5 points (3 to 7) at the final follow-up. Osseointegration was seen in all femoral and acetabular components. All hips had grade 1 stress shielding of the proximal femur. No acetabular or femoral osteolysis was identified.

These results demonstrate that a short metaphyseal-fitting femoral component achieves optimal fixation without diaphyseal anchorage in elderly patients.

Ceramic-on-ceramic bearings in hip replacement have low rates of wear and are increasingly being used in young adults. Our aim was to determine the incidence of audible phenomena or other bearing-related complications.

We retrospectively analysed 250 ceramic-on-ceramic hip replacements in 224 patients which had been implanted between April 2000 and December 2007. The mean age of the patients at operation was 44 years (14 to 83) and all the operations were performed using the same surgical technique at a single centre.

At a mean follow-up of 59 months (24 to 94), the mean Oxford hip score was 40.89 (11 to 48). There were six revisions, three of which were for impingement-related complications. No patient reported squeaking, but six described grinding or clicking, which was usually associated with deep flexion. No radiological evidence of osteolysis or migration of the components was observed in any hip.

The early to mid-term results of contemporary ceramic-on-ceramic hip replacement show promising results with few concerns in terms of noise and squeaking. Positioning of the acetabular component remains critical in regard to the reduction of other impingement-related complications.

Aims

Post-operative migration of cemented acetabular components as measured by radiostereometric analysis (RSA) has a strong predictive power for late, aseptic loosening. Also, radiolucent lines predict late loosening. Migration has been reduced by systemic bisphosphonate treatment in randomised trials of hip and knee arthroplasty. Used as a local treatment, a higher local dose of bisphosphonate can be achieved without systemic exposure. We wished to see if this principle could be applied usefully in total hip arthroplasty (THA).

The inherent challenges of total hip replacement (THR) in children include the choice of implant for the often atypical anatomical morphology, its fixation to an immature growing skeleton and the bearing surface employed to achieve a successful long-term result. We report the medium-term results of 52 consecutive uncemented THRs undertaken in 35 paediatric patients with juvenile idiopathic arthritis. The mean age at the time of surgery was 14.4 years (10 to 16). The median follow-up was 10.5 years (6 to 15). During the study period 13 THRs underwent revision surgery. With revision as an endpoint, subgroup analysis revealed 100% survival of the 23 ceramic-on-ceramic THRs and 55% (16 of 29) of the metal- or ceramic-on-polyethylene. This resulted in 94% (95% CI 77.8 to 98.4) survivorship of the femoral component and 62% (95% CI 41.0 to 78.0) of the acetabular component. Revision of the acetabular component for wear and osteolysis were the most common reasons for failure accounting for 11 of the 13 revisions.

The success seen in patients with a ceramic-on-ceramic articulation seems to indicate that this implant strategy has the potential to make a major difference to the long-term outcome in this difficult group of patients.

The aim of this study was to assess the effect of frictional torque and bending moment on fretting corrosion at the taper interface of a modular femoral component and to investigate whether different combinations of material also had an effect. The combinations we examined were 1) cobalt–chromium (CoCr) heads on CoCr stems 2) CoCr heads on titanium alloy (Ti) stems and 3) ceramic heads on CoCr stems.

In test 1 increasing torque was imposed by offsetting the stem in the anteroposterior plane in increments of 0 mm, 4 mm, 6 mm and 8 mm when the torque generated was equivalent to 0 Nm, 9 Nm, 14 Nm and 18 Nm.

In test 2 we investigated the effect of increasing the bending moment by offsetting the application of axial load from the midline in the mediolateral plane. Increments of offset equivalent to head + 0 mm, head + 7 mm and head + 14 mm were used.

Significantly higher currents and amplitudes were seen with increasing torque for all combinations of material. However, Ti stems showed the highest corrosion currents. Increased bending moments associated with using larger offset heads produced more corrosion: Ti stems generally performed worse than CoCr stems. Using ceramic heads did not prevent corrosion, but reduced it significantly in all loading configurations.

Cite this article: Bone Joint J 2015;97-B:463–72.

A moderator and panel of five experts led an interactive session in discussing five challenging and interesting patient case presentations involving surgery of the hip. The hip pathologies reviewed included failed open reduction internal fixation of subcapital femoral neck fracture, bilateral hip disease, evaluation of pain after metal-on-metal hip arthroplasty, avascular necrosis, aseptic loosening secondary to osteolysis and polyethylene wear, and management of ceramic femoral head fracture.

Symptomatic cobalt toxicity from a failed total hip replacement is a rare but devastating complication. It has been reported following revision of fractured ceramic components, as well as in patients with failed metal-on-metal articulations. Potential clinical findings include fatigue, weakness, hypothyroidism, cardiomyopathy, polycythaemia, visual and hearing impairment, cognitive dysfunction, and neuropathy. We report a case of an otherwise healthy 46-year-old patient, who developed progressively worsening symptoms of cobalt toxicity beginning approximately six months following synovectomy and revision of a fractured ceramic-on-ceramic total hip replacement to a metal-on-polyethylene bearing. The whole blood cobalt levels peaked at 6521 µg/l. The patient died from cobalt-induced cardiomyopathy. Implant retrieval analysis confirmed a loss of 28.3 g mass of the cobalt–chromium femoral head as a result of severe abrasive wear by ceramic particles embedded in the revision polyethylene liner. Autopsy findings were consistent with heavy metal-induced cardiomyopathy.

We recommend using new ceramics at revision to minimise the risk of wear-related cobalt toxicity following breakage of ceramic components.

Cite this article: Bone Joint J 2013;95-B:31–7.

Noise generation has been reported with ceramic-on-ceramic articulations in total hip replacement (THR). This study evaluated 208 consecutive Delta Motion THRs at a mean follow-up of 21 months (12 to 35). There were 141 women and 67 men with a mean age of 59 years (22 to 84). Patients were reviewed clinically and radiologically, and the incidence of noise was determined using a newly described assessment method. Noise production was examined against range of movement, ligamentous laxity, patient-reported outcome scores, activity level and orientation of the acetabular component. There were 143 silent hips (69%), 22 (11%) with noises other than squeaking, 17 (8%) with unreproducible squeaking and 26 (13%) with reproducible squeaking. Hips with reproducible squeaking had a greater mean range of movement (p < 0.001) and mean ligament laxity (p = 0.004), smaller median head size (p = 0.01) and decreased mean acetabular component inclination (p = 0.02) and anteversion angle (p = 0.02) compared with the other groups. There was no relationship between squeaking and age (p = 0.13), height (p = 0.263), weight (p = 0.333), body mass index (p = 0.643), gender (p = 0.07) or patient outcome score (p = 0.422). There were no revisions during follow-up. Despite the surprisingly high incidence of squeaking, all patients remain satisfied with their hip replacement.

Cite this article: Bone Joint J 2013;95-B:160–5.

We reviewed the literature on the currently available choices of bearing surface in total hip replacement (THR). We present a detailed description of the properties of articulating surfaces review the understanding of the advantages and disadvantages of existing bearing couples. Recent technological developments in the field of polyethylene and ceramics have altered the risk of fracture and the rate of wear, although the use of metal-on-metal bearings has largely fallen out of favour, owing to concerns about reactions to metal debris. As expected, all bearing surface combinations have advantages and disadvantages. A patient-based approach is recommended, balancing the risks of different options against an individual’s functional demands.

Cite this article: Bone Joint J 2014;96-B:147–56.

Bioengineering reasons for increased wear and failure of metal-on-metal (MoM) bearings in hip prostheses have been described. Low wear occurs in MoM hips when the centre of the femoral head is concentric with the centre of the acetabular component and the implants are correctly positioned. Translational or rotational malpositioning of the components can lead to the contact-patch of the femoral component being displaced to the rim of the acetabular component, resulting in a ten- to 100-fold increase in wear and metal ion levels. This may cause adverse tissue reactions, loosening of components and failure of the prosthesis.

It is accepted that resurfacing hip replacement preserves the bone mineral density (BMD) of the femur better than total hip replacement (THR). However, no studies have investigated any possible difference on the acetabular side.

Between April 2007 and March 2009, 39 patients were randomised into two groups to receive either a resurfacing or a THR and were followed for two years. One patient’s resurfacing subsequently failed, leaving 19 patients in each group.

Resurfaced replacements maintained proximal femoral BMD and, compared with THR, had an increased bone mineral density in Gruen zones 2, 3, 6, and particularly zone 7, with a gain of 7.5% (95% confidence interval (CI) 2.6 to 12.5) compared with a loss of 14.6% (95% CI 7.6 to 21.6). Resurfacing replacements maintained the BMD of the medial femoral neck and increased that in the lateral zones between 12.8% (95% CI 4.3 to 21.4) and 25.9% (95% CI 7.1 to 44.6).

On the acetabular side, BMD was similar in every zone at each point in time. The mean BMD of all acetabular regions in the resurfaced group was reduced to 96.2% (95% CI 93.7 to 98.6) and for the total hip replacement group to 97.6% (95% CI 93.7 to 101.5) (p = 0.4863). A mean total loss of 3.7% (95% CI 1.0 to 6.5) and 4.9% (95% CI 0.8 to 9.0) of BMD was found above the acetabular component in W1 and 10.2% (95% CI 0.9 to 19.4) and 9.1% (95% CI 3.8 to 14.4) medial to the implant in W2 for resurfaced replacements and THRs respectively. Resurfacing resulted in a mean loss of BMD of 6.7% (95% CI 0.7 to 12.7) in W3 but the BMD inferior to the acetabular component was maintained in both groups.

These results suggest that the ability of a resurfacing hip replacement to preserve BMD only applies to the femoral side.

There have been comparatively few studies of the incidence of osteolysis and the survival of hybrid and cementless total hip replacements (THRs) in patients younger than 50 years of age. We prospectively reviewed 78 patients (109 hips) with a hybrid THR having a mean age of 43.4 years (21 to 50) and 79 patients (110 hips) with a cementless THR with a mean age of 46.8 years (21 to 49). The patients were evaluated clinically using the Harris hip score, the Western Ontario and McMaster Universities (WOMAC) osteoarthritis score and the University of California, Los Angeles (UCLA) activity score. Radiographs and CT scans were assessed for loosening and osteolysis. The mean follow-up was for 18.4 years (16 to 19) in both groups.

The mean post-operative Harris hip scores (91 points versus 90 points), the mean WOMAC scores (11 points versus 13 points) and UCLA activity scores (6.9 points versus 7.1 points) were similar in both groups. The revision rates of the acetabular component (13% versus 16%) and the femoral component (3% versus 4%), and the survival of the acetabular component (87% versus 84%) and the femoral component (97% versus 96%) were similar in both groups.

Although the long-term fixation of the acetabular metallic shell and the cemented and cementless femoral components was outstanding, wear and peri-acetabular osteolysis constitute the major challenges of THR in young patients.