One concern about the fixation of HA-coated implants is the possible disintegration of the surface, with the migration of HA granules into the joint space, producing third-body wear. We report a study of six revisions of HA-coated polyethylene RM cups at 9 to 14 years after successful primary arthroplasty. In all six hips, we found HA granules embedded in the articulating surface of the polyethylene, with abrasive wear of the cup and the metal femoral head. The cup had loosened in four hips and three showed severe osteolysis of the proximal femur. Third-body wear due to HA particles from implant coating may produce severe clinical problems with few early warning signs. Further clinical, radiological and histological observations are needed to determine the possible incidence of this late complication in the various types of coating of a variety of substrates

Aims. The aims of this study were to evaluate wear on the surface of cobalt-chromium (CoCr) femoral components used in total knee arthroplasty (TKA) and compare the wear of these components with that of ceramic femoral components. Methods. Optical profilometry was used to evaluate surface roughness and to examine the features created by the wear process in a knee wear simulator. We developed a method of measuring surface changes on five CoCr femoral components and quantifying the loss of material from the articular surface during the wear process. We also examined the articular surface of three ceramic femoral components from a previous test for evidence of surface damage, and compared it with that of CoCr components. Results. We found that the surface roughness of CoCr components rapidly increased during the first 1,000 wear cycles, then reached a steady state, but material loss from the surface continued at a rate of 1,778,000 μm. 3. per million cycles as carbides were removed from its matrix. These carbides formed third-body wear particles, leading to the formation of new scratches even as older scratches were worn away. In contrast, no scratching, loss of material, or other surface damage, when evaluated with one nanometer resolution, was found on the surface of the ceramic components after a 15 M wear cycle test. Conclusion. This study showed wear and loss of CoCr material from scratching and microabrasive wear in TKA. The material loss from the surface continued in a linear relationship with increasing cycles. We also found the absence of scratching and roughening of ceramic femoral components in simulated wear, suggesting an advantage in wear rate and avoiding metal sensitivity. This may have implications in the management of persistent pain after TKA. Cite this article: Bone Joint J 2021;103-B(6 Supple A):94–101

We carried out a histological study of a proximally hydroxyapatite (HA)-coated femoral component, retrieved after 9.5 years of good function. The HA coating had completely degraded. Bone was in direct contact with the titanium surface in all the areas which had been coated, with no interposing fibrous tissue. There were no signs of particles, third-body wear, adverse tissue reactions or osteolysis. Bone remodelling was evident by the presence of resorption lacunae; tetracycline labelling showed bone laid down six years after implantation. The loss of the HA-coating had no negative effect on the osseo-integration of the stem. We conclude that the HA coating contributes to the fixation of the implant and that its degradation does not adversely affect the long-term fixation

There are several techniques for the accurate measurement of the migration of components after arthroplasty some of which require the operative placement of tantalum balls. We have reviewed the position and migration of these markers in 64 patients after total hip arthroplasty. In 40% of cases, one or more balls was seen to be outside the proximal femur on the postoperative radiograph, although all were considered to be within the bone at operation. In two hips, one ball appeared to have migrated towards the joint, although none was seen within the joint. Misplacement was not related to the experience of the surgeon or the operative approach. Migration analysis which necessitates the insertion of tantalum balls requires careful technique to avoid a potential source of third-body wear. It should probably be used only for research in small series of patients

Our aim was to determine whether tantalum markers improved the accuracy and/or precision of methods for the measurement of migration in total hip replacement based on conventional measurements without mathematical correction of the data, and with Ein Bild Roentgen Analyse – Femoral Component Analysis (EBRA-FCA) which allows a computerised correction. Three observers independently analysed 13 series of roentgen-stereophotogrammetric-analysis (RSA)-compatible radiographs (88). Data were obtained from conventional measurements, EBRA-FCA and the RSA method and all the results were compared with the RSA data. Radiological evaluation was also used to quantify in how many radiographs the intraosseous position of the bone markers had been simulated. The results showed that tantalum markers improve reliability whereas they do not affect accuracy for conventional measurements and for EBRA-FCA. Because of the danger of third-body wear their implantation should be avoided unless they are an integral part of the method

We examined 86 polyethylene inserts, retrieved from total and unicompartmental knee prostheses after an average of 39.5 months in situ, grading them from 0 to 3 for seven modes of polyethylene degradation. Severe wear, with delamination or deformation, was observed in 51% of the implants, and was associated with time in situ, lack of congruency, thin polyethylene, third-body wear debris, and heat-pressed polyethylene. Significant under-surface cold flow was identified in some areas of unsupported polyethylene, and was associated with delamination in the load-bearing areas of thin inserts above screw holes in the underlying metal tray. We recommend the use of thicker polyethylene inserts, particularly in young, active patients and in designs with screw holes in the tibial baseplate. Thin polyethylene inserts which are at risk for accelerated wear and premature failure should be monitored radiographically at annual intervals

Aims

BoneMaster is a thin electrochemically applied hydroxyapatite (HA) coating for orthopaedic implants that is quickly resorbed during osseointegration. Early stabilization is a surrogacy marker of good survival of femoral stems. The hypothesis of this study was that a BoneMaster coating yields a fast early and lasting fixation of stems.

Aims

The aim of this study was to conduct the largest low contact stress (LCS) retrieval study to elucidate the failure mechanisms of the Porocoat and Duofix femoral component. The latter design was voluntarily recalled by the manufacturer.

Aims

In the 1990s, a bioactive bone cement (BABC) containing apatite-wollastonite glass-ceramic (AW-GC) powder and bisphenol-a-glycidyl methacrylate resin was developed at our hospital. In 1996, we used BABC to fix the acetabular component in primary total hip arthroplasty (THA) in 20 patients as part of a clinical trial. The purpose of this study was to investigate the long-term results of primary THA using BABC.

Aims

Hydroxyapatite coatings for uncemented fixation in total knee arthroplasty can theoretically provide a long-lasting biological interface with the host bone. The objective of this study was to test this hypothesis with propriety hydroxyapatite, peri-apatite, coated tibial components using component migration measured with radiostereometric analysis over two years as an indicator of long-term fixation.

Aims

It may not be possible to undertake revision total hip arthroplasty (THA) in the presence of massive loss of acetabular bone stock using standard cementless hemispherical acetabular components and metal augments, as satisfactory stability cannot always be achieved. We aimed to study the outcome using a reconstruction cage and a porous metal augment in these patients.

We reviewed the literature on the currently available choices of bearing surface in total hip replacement (THR). We present a detailed description of the properties of articulating surfaces review the understanding of the advantages and disadvantages of existing bearing couples. Recent technological developments in the field of polyethylene and ceramics have altered the risk of fracture and the rate of wear, although the use of metal-on-metal bearings has largely fallen out of favour, owing to concerns about reactions to metal debris. As expected, all bearing surface combinations have advantages and disadvantages. A patient-based approach is recommended, balancing the risks of different options against an individual’s functional demands.

Cite this article: Bone Joint J 2014;96-B:147–56.

We present a retrospective series of 170 cemented titanium straight-stem femoral components combined with two types of femoral head: cobalt-chromium (CoCr) alloy (114 heads) and alumina ceramic (50 heads). Of the study group, 55 patients (55 stems) had died and six (six stems) were lost to follow-up. At a mean of 13.1 years (3 to 15.3) 26 stems had been revised for aseptic loosening. The mean follow-up time for stable stems was 15.1 years (12.1 to 16.6).

Survival of the stem at 15 years was 75.4% (95% confidence interval (CI) 67.3 to 83.5) with aseptic failure (including radiological failure) as the end-point, irrespective of the nature of the head and the quality of the cement mantle. Survival of the stem at 15 years was 79.1% (95% CI 69.8 to 88.4) and 67.1% (95% CI 51.3 to 82.9) with the CoCr alloy and ceramic heads, respectively. The quality of the cement mantle was graded as a function of stem coverage: stems with complete tip coverage (type 1) had an 84.9% (95% CI 77.6 to 92.2) survival at 15 years, compared with those with a poor tip coverage (type 2) which had a survival of only 22.4% (95% CI 2.4 to 42.4). The poor quality of the cement mantle and the implantation of an alumina head substantially lowered the survival of the stem.

In our opinion, further use of the cemented titanium alloy straight-stem femoral components used in our series is undesirable.

As the number of younger and more active patients treated with total knee arthroplasty (TKA) continues to increase, consideration of better fixation as a means of improving implant longevity is required. Cemented TKA remains the reference standard with the largest body of evidence and the longest follow-up to support its use. However, cementless TKA, may offer the opportunity of a more bone-sparing procedure with long lasting biological fixation to the bone. We undertook a review of the literature examining advances of cementless TKA and the reported results.

Cite this article: Bone Joint J 2016;98-B:867–73.

Between 2002 and 2008, 130 consecutive ankles were replaced with an hydroxyapatite (HA) and titanium-HA-coated Ankle Evolutive System total ankle prosthesis. Plain radiographs were analysed by two independent observers. Osteolytic lesions were classified by their size and location, with cavities > 10 mm in diameter considered to be ‘marked’. CT scanning was undertaken in all patients with marked osteolysis seen on the plain radiographs.

Osteolytic lesions were seen on the plain films in 48 (37%) and marked lesions in 27 (21%) ankles. The risk for osteolysis was found to be 3.1 (95% confidence interval 1.6 to 5.9) times higher with implants with Ti-HA porous coating.

Care should be taken with ankle arthroplasty until more is known about the reasons for these severe osteolyses.

A retrospective review was performed of patients undergoing primary cementless total knee replacement (TKR) using porous tantalum performed by a group of surgical trainees. Clinical and radiological follow-up involved 79 females and 26 males encompassing 115 knees. The mean age was 66.9 years (36 to 85). Mean follow-up was 7 years (2 to 11). Tibial and patellar components were porous tantalum monoblock implants, and femoral components were posterior stabilised (PS) in design with cobalt–chromium fibre mesh. Radiological assessments were made for implant positioning, alignment, radiolucencies, lysis, and loosening. There was 95.7% survival of implants. There was no radiological evidence of loosening and no osteolysis found. No revisions were performed for aseptic loosening. Average tibial component alignment was 1.4° of varus (4°of valgus to 9° varus), and 6.2° (3° anterior to 15° posterior) of posterior slope. Mean femoral component alignment was 6.6° (1° to 11°) of valgus. Mean tibiofemoral alignment was 5.6° of valgus (7° varus to 16° valgus). Patellar tilt was a mean of 2.4° lateral (5° medial to 28° lateral). Patient satisfaction with improvement in pain was 91%. Cementless TKR incorporating porous tantalum yielded good clinical and radiological outcomes at a mean of follow-up of seven-years.

Cite this article: Bone Joint J 2014;96-B(11 Suppl A):87–92.

A modular layered acetabular component (metal-polyethylene-ceramic) was developed in Japan for use in alumina ceramic-on-ceramic total hip replacement. Between May 1999 and July 2000, we performed 35 alumina ceramic-on-ceramic total hip replacements in 30 consecutive patients, using this layered component and evaluated the clinical and radiological results over a mean follow-up of 5.8 years (5 to 6.5). A total of six hips underwent revision, one for infection, two for dislocation with loosening of the acetabular component, two for alumina liner fractures and one for component dissociation with pelvic osteolysis. There were no fractures of the ceramic heads, and no loosening of the femoral or acetabular component in the unrevised hips was seen at final follow-up. Osteolysis was not observed in any of the unrevised hips. The survivorship analysis at six years after surgery was 83%. The layered acetabular component in our experience, has poor durability because of unexpected mechanical failures including alumina liner fracture and component dissociation.

We describe the clinical and radiological results of 120 consecutive revision hip replacements in 107 patients, using the JRI Furlong hydroxyapatite-ceramic-coated femoral component. The mean age of the patients at operation was 71 years (36 to 92) and the mean length of follow-up 8.0 years (5.0 to 12.4). We included patients on whom previous revision hip surgery had taken place. The patients were independently reviewed and scored using the Harris hip score, the Western Ontario and McMaster Universities osteoarthritis index (WOMAC) and the Charnley modification of the Merle d’Aubigné and Postel score. Radiographs were assessed by three reviewers for the formation of new bone, osteolysis, osseointegration and radiolucent lines in each Gruen zone.

The mean Harris hip score was 85.8 (42 to 100) at the latest post-operative review. The mean WOMAC and Merle d’Aubigné and Postel scores were 34.5 and 14.8, respectively. The mean visual analogue score for pain (possible range 0 to 10) was 1.2 overall, but 0.5 specifically for mid-thigh pain. There were no revisions of the femoral component for aseptic loosening. There were four re-revisions, three for infection and one for recurrent dislocation. Radiological review of all the femoral components, including the four re-revisions showed stable bony ingrowth and no new radiolucent lines in any zone. Using revision or impending revision for aseptic loosening as an end-point, the cumulative survival of the femoral component at ten years was 100% (95% confidence interval 94 to 100). We present excellent medium- to long-term clinical, radiological and survivorship results with the fully hydroxyapatite-ceramic-coated femoral component in revision hip surgery.

Fracture of a ceramic component in total hip replacement is a rare but potentially catastrophic complication. The incidence is likely to increase as the use of ceramics becomes more widespread. We describe such a case, which illustrates how inadequate initial management will lead to further morbidity and require additional surgery. We present the case as a warning that fracture of a ceramic component should be revised to another ceramic-on-ceramic articulation in order to minimise the risk of further catastrophic wear.

We report a multicentre prospective consecutive study assessing the long-term outcome of the proximally hydroxyapatite (HA)-coated ABG II monobloc femoral component in a series of 1148 hips in 1053 patients with a mean age at surgery of 64.77 years (22 to 80) at a mean follow-up of 10.84 years (10 to 15.25). At latest follow-up, the mean total Harris hip score was 94.7 points (sd; 6.87; 49 to 100), and the mean Merle d’Aubigné–Postel score was 17.6 points (sd 1.12; 7 to 18). The mean total Engh radiological score score was 21.54 (sd 5.77; 3.5 to 27), with 95.81% of ‘confirmed ingrowth’, according to Engh’s classification. With aseptic loosening or pain as endpoints, three AGB II stems (0.26%) failed, giving a 99.7% survival rate (se 0.002; 95% confidence interval (CI) 0.994 to 1) at 14 years’ follow-up. The survival of patients ≤ 50 years of age (99.0% (se 0.011; 95% CI 0.969 to 1)) did not differ significantly from those of patients aged > 50 years (99.8% (se 0.002; 95% CI 0.994 to 1)). This study confirmed the excellent long-term results currently achieved with the ABG II proximally HA-coated monobloc stem.

Cite this article: Bone Joint J 2013;95-B:1610–16.

Alumina–alumina bearings are among the most resistant to wear in total hip replacement. Examination of their surfaces is one way of comparing damage caused by wear of hip joints simulated in vitro to that seen in explanted bearings. The aim of this study was to determine whether second-generation ceramic bearings exhibited a better pattern of wear than those reported in the literature for first-generation bearings. We considered both macro- and microscopic findings.

We found that long-term alumina wear in association with a loose acetabular component could be categorised into three groups. Of 20 specimens, four had ‘low wear’, eight ‘crescent wear’ and eight ‘severe wear’, which was characterised by a change in the physical shape of the bearing and a loss of volume. This suggests that the wear in alumina–alumina bearings in association with a loose acetabular component may be variable in pattern, and may explain, in part, why the wear of a ceramic head in vivo may be greater than that seen after in vitro testing.

This single-blinded randomised controlled trial investigated whether one design of mobile-bearing (MB) total knee replacement (TKR) has any advantage over a fixed-bearing (FB) design on long-term fixation as measured by radiostereometry. The amount of wear underneath the mobile bearing was also evaluated. A series of 42 knees was randomised to MB or FB tibial components with appropriate polyethylene inserts and followed for between ten and 12 years, or until the death of the patient. The polyethylene in the MB group was superior in that it was gamma-irradiated in inert gas and was calcium-stearate free; the polyethylene in the FB group was gamma-irradiated in air and contained calcium stearate. In theory this should be advantageous to the wear rate of the MB group. At final follow-up the overall mean migration was 0.75 mm (sd 0.76) in the MB group and 0.66 mm (sd 0.4) in the FB group, with the FB group demonstrating more posterior tilt and the MB group more internal rotation. In the FB group there was one revision for aseptic loosening, but none in the MB group. There were no significant differences in clinical or radiological scores.

For the MB group, the mean linear wear rate on the under-surface was 0.026 mm/year (sd 0.014). This was significantly smaller than the wear rate of 0.11 mm/year (sd 0.06) in the MB between femur and polyethylene (p < 0.001). Nevertheless, even in a best-case setting the mobile bearings of this TKR design had no apparent advantage in terms of fixation over the FB knee prosthesis at ten to 12 years. The wear underneath the mobile bearing was small and is unlikely to be clinically relevant.

An intra-operative splash is a common occurrence in elective knee and hip replacement surgery and can potentially transmit bloodborne diseases, with devastating consequences. This study aimed to quantify the risk of a splash and to assess its correlation with body mass index, duration of surgery and the volume of lavage fluid used.

Between December 2007 and April 2008, 62 consecutive patients (38 women, 24 men) undergoing an elective total knee or total hip replacement (TKR, THR) were recruited into the study (32 TKRs and 30 THRs) after appropriate consent.

A splash occurred in all 62 cases. A THR had a slightly higher risk of a splash than a TKR, but this was not statistically significant (p = 0.27). The correlation between body mass index, duration of surgery and the amount of pulse lavage used with a splash was r = 0.013, (non-significant), r = 0.52, (significant) and r = 0.92 (highly significant), respectively.

A high number of splashes are generated during a TKR and a THR. The simple visor mask fails to protect the surgeon, the assistant or the patient from the risk of a splash and reverse splash, respectively.

The Oxford unicompartmental knee replacement (UKR) was designed to minimise wear utilising a fully-congruent, mobile, polyethylene bearing. Wear of polyethylene is a significant cause of revision surgery in UKR in the first decade, and the incidence increases in the second decade. Our study used model-based radiostereometric analysis to measure the combined wear of the upper and lower bearing surfaces in 13 medial-compartment Oxford UKRs at a mean of 20.9 years (17.2 to 25.9) post-operatively.

The mean linear penetration of the polyethylene bearing was 1.04 mm (0.307 to 2.15), with a mean annual wear rate of 0.045 mm/year (0.016 to 0.099). The annual wear rate of the phase-2 bearings (mean 0.022 mm/year) was significantly less (p = 0.01) than that of phase-1 bearings (mean 0.07 mm/year).

The linear wear rate of the Oxford UKR remains very low into the third decade. We believe that phase-2 bearings had lower wear rates than phase-1 implants because of the improved bearing design and surgical technique which decreased the incidence of impingement. We conclude that the design of the Oxford UKR gives low rates of wear in the long term.

Coloured bone cements have been introduced to make the removal of cement debris easier at the time of primary and revision joint replacement. We evaluated the physical, mechanical and pharmacological effects of adding methylene blue to bone cement with or without antibiotics (gentamicin, vancomycin or both). The addition of methylene blue to plain cement significantly decreased its mean setting time (570 seconds (sd 4) vs 775 seconds (sd 11), p = 0.01), mean compression strength (95.4 MPa (sd 3) vs 100.1 MPa (sd 6), p = 0.03), and mean bending strength (65.2 MPa (sd 5) vs 76.6 MPa (sd 4), p < 0.001) as well as its mean elastic modulus (2744 MPa (sd 97) vs 3281 MPa (sd 110), p < 0.001). The supplementation of the coloured cement with vancomycin and gentamicin decreased its mean bending resistance (55.7 MPa (sd 4) vs 65.2 MPa (sd 5), p < 0.001).The methylene blue significantly decreased the mean release of gentamicin alone (228.2 µg (sd 24) vs 385.5 µg (sd 26), p < 0.001) or in combination with vancomycin (498.5 µg (sd 70) vs 613 µg (sd 25), p = 0.018) from the bone cement. This study demonstrates several theoretical disadvantages of the antibiotic-loaded bone cement coloured with methylene blue.

The long-term results of grafting with hydroxyapatite granules for acetabular deficiency in revision total hip replacement are not well known. We have evaluated the results of revision using a modular cup with hydroxyapatite grafting for Paprosky type 2 and 3 acetabular defects at a minimum of ten years’ follow-up. We retrospectively reviewed 49 acetabular revisions at a mean of 135 months (120 to 178). There was one type 2B, ten 2C, 28 3A and ten 3B hips. With loosening as the endpoint, the survival rate was 74.2% (95% confidence interval 58.3 to 90.1). Radiologically, four of the type 3A hips (14%) and six of the type 3B hips (60%) showed aseptic loosening with collapse of the hydroxyapatite layer, whereas no loosening occurred in type 2 hips. There was consolidation of the hydroxyapatite layer in 33 hips (66%). Loosening was detected in nine of 29 hips (31%) without cement and in one of 20 hips (5%) with cement (p = 0.03, Fisher’s exact probability test). The linear wear and annual wear rate did not correlate with loosening.

These results suggest that the long-term results of hydroxyapatite grafting with cement for type 2 and 3A hips are encouraging.

We reviewed the long-term results at ten to 12 years of 118 total hip replacements in 109 patients using a second-generation hemispherical cementless acetabular component (Reflection) designed to address the problem of backside wear. Five patients (five hips) died and six patients (seven hips) were lost to follow-up. The remaining 98 patients (106 hips) had a mean age of 62.9 years (34.0 to 86.2) A rate of revision for aseptic loosening of 0.9%, and predictable results were found with respect to radiological evidence of fixation, lack of pain, walking ability, range of movement and function. One component was revised for aseptic loosening, and of the 101 hips (95.2%) that did not have a revision, minor osteolytic lesions of the pelvis were seen in six (5.9%). Kaplan-Meier survival analysis for the total cohort of 118 hips revealed a 96.4% survival at both ten (95% confidence interval 90 to 98) and 12 years (95% confidence interval 86 to 98).

In 2004 we described the ten-year prospective results of 38 total hip replacements using the Furlong hydroxyapatite-ceramic-coated femoral component in 35 patients < 50 years old. We have now reviewed the surviving 35 arthroplasties in 33 patients at a mean of 16 years (10.3 to 19.9). The mean age of the surviving patients at the time of operation was 41.3 years (26.0 to 49.0). Of these, eight have undergone revision of their acetabular component for aseptic loosening. None of the femoral components has had revision for aseptic loosening giving a survival rate of 100% at 16 years (95% confidence interval 89% to 100%).

The Furlong hydroxyapatite-ceramic-coated femoral component gives excellent long-term survival in young and active patients.

Two Durasul highly crosslinked polyethylene liners were exchanged during revision surgery four and five years after implantation, respectively. The retrieved liners were evaluated macroscopically and surface analysis was performed using optical and electron microscopy. A sample of each liner was used to determine the oxidation of the material by Fourier transform infrared spectroscopy. Samples of the capsule were examined histologically.

The annual wear rate was found to be 0.010 and 0.015 mm/year, respectively. Surface analysis showed very little loss of material caused by wear. Histological evaluation revealed a continuous neosynovial lining with single multinucleated foreign-body giant cells. Our findings showed no unexpected patterns of wear on the articulating surfaces up to five years after implantation and no obvious failure of material.

It is unclear whether there is a limit to the amount of distal bone required to support fixation of supracondylar periprosthetic femoral fractures. This retrospective multicentre study evaluated lateral locked plating of periprosthetic supracondylar femoral fractures and compared the results according to extension of the fracture distal with the proximal border of the femoral prosthetic component.

Between 1999 and 2008, 89 patients underwent lateral locked plating of a supracondylar periprosthetic femoral fracture, of whom 61 patients with a mean age of 72 years (42 to 96) comprising 53 women, were available after a minimum follow-up of six months or until fracture healing. Patients were grouped into those with fractures located proximally (28) and those with fractures that extended distal to the proximal border of the femoral component (33).

Delayed healing and nonunion occurred respectively in five (18%) and three (11%) of more proximal fractures, and in two (6%) and five (15%) of the fractures with distal extension (p = 0.23 for delayed healing; p = 0.72 for nonunion, Fisher’s exact test). Four construct failures (14%) occurred in more proximal fractures, and three (9%) in fractures with distal extension (p = 0.51). Of the two deep infections that occurred in each group, one resolved after surgical debridement and antibiotics, and one progressed to a nonunion.

Extreme distal periprosthetic supracondylar fractures of the femur are not a contra-indication to lateral locked plating. These fractures can be managed with internal fixation, with predictable results, similar to those seen in more proximal fractures.

Second-generation metal-on-metal bearings were introduced as a response to the considerable incidence of wear-induced failures associated with conventional replacements, especially in young patients. We present the results at ten years of a consecutive series of patients treated using a metal-on-metal hip resurfacing. A distinct feature of the bearings used in our series was that they had been subjected to double-heat treatments during the post-casting phase of their manufacture. In the past these bearings had not been subjected to thermal treatments, making this a unique metal-on-metal bearing which had not been used before in clinical practice.

We report the outcome of 184 consecutive hips (160 patients) treated using a hybrid-fixed metal-on-metal hip resurfacing during 1996. Patients were invited for a clinicoradiological follow-up at a minimum of ten years. The Oxford hip score and anteroposterior and lateral radiographs were obtained. The mean age at operation was 54 years (21 to 75). A series of 107 consecutive hips (99 patients) who received the same prosthesis, but subjected to a single thermal treatment after being cast, between March 1994 and December 1995, were used as a control group for comparison.

In the 1994 to 1995 group seven patients (seven hips) died from unrelated causes and there were four revisions (4%) for osteolysis and aseptic loosening. In the 1996 group nine patients died at a mean of 6.9 years after operation because of unrelated causes. There were 30 revisions (16%) at a mean of 7.3 years (1.2 to 10.9), one for infection at 1.2 years and 29 for osteolysis and aseptic loosening. Furthermore, in the latter group there were radiological signs of failure in 27 (24%) of the 111 surviving hips.

The magnitude of the problem of osteolysis and aseptic loosening in the 1996 cohort did not become obvious until five years after the operation. Our results indicate that double-heat treatments of metal-on-metal bearings can lead to an increased incidence of wear-induced osteolysis.

The Oxford Unicompartmental Knee replacement (UKR) was introduced as a design to reduce polyethylene wear. There has been one previous retrieval study involving this implant, which reported very low rates of wear in some specimens but abnormal patterns of wear in others. There has been no further investigation of these abnormal patterns. The bearings were retrieved from 47 patients who had received a medial Oxford UKR for anteromedial osteoarthritis of the knee. None had been studied previously. The mean time to revision was 8.4 years (sd 4.1), with 20 having been implanted for over ten years. The macroscopic pattern of polyethylene wear and the linear penetration were recorded for each bearing. The mean rate of linear penetration was 0.07 mm/year. The patterns of wear fell into three categories, each with a different rate of linear penetration; 1) no abnormal macroscopic wear and a normal articular surface, n = 16 (linear penetration rate = 0.01 mm/year); 2) abnormal macroscopic wear and normal articular surfaces with extra-articular impingement, n = 16 (linear penetration rate = 0.05 mm/year); 3) abnormal macroscopic wear and abnormal articular surfaces with intra-articular impingement +/− signs of non-congruous articulation, n = 15 (linear penetration rate = 0.12 mm/year). The differences in linear penetration rate were statistically significant (p < 0.001).

These results show that very low rates of polyethylene wear are possible if the device functions normally. However, if the bearing displays suboptimal function (extra-articular, intra-articular impingement or incongruous articulation) the rates of wear increase significantly.

Because the femoral head/neck junction is preserved in hip resurfacing, patients may be at greater risk of impingement, leading to abnormal wear patterns and pain. We assessed femoral head/neck offset in 63 hips undergoing metal-on-metal hip resurfacing and in 56 hips presenting with non-arthritic pain secondary to femoroacetabular impingement. Most hips undergoing resurfacing (57%; 36) had an offset ratio ≤ 0.15 pre-operatively and required greater correction of offset at operation than the rest of the group. In the non-arthritic hips the mean offset ratio was 0.137 (0.04 to 0.23), with the offset ratio correlating negatively to an increasing α angle. An offset ratio ≤ 0.15 had a 9.5-fold increased relative risk of having an α angle ≥ 50.5°. Most hips undergoing resurfacing have an abnormal femoral head/neck offset, which is best assessed in the sagittal plane.

Polyethylene wear of acetabular components is a key factor in the development of periprosthetic osteolysis and wear at the articular surface has been well documented and quantified, but fewer data are available about changes which occur at the backside of the liner.

At revision surgery for loosening of the femoral component we retrieved 35 conventional modular acetabular liners of the same design. Linear and volumetric articular wear, backside volumetric change and the volume of the screw-head indentations were quantified. These volumes, clinical data and the results from radiological Ein Bild Röntgen Analyse migration analysis were used to identify potential factors influencing the volumetric articular wear and backside volumetric change.

The rate of backside volumetric change was found to be 2.8% of the rate of volumetric articular wear and decreased with increasing liner size. Migrated acetabular components showed significantly higher rates of backside volumetric change plus screw-head indentations than those without migration.

The backside volumetric change was at least ten times larger than finite-element simulation had suggested. In a stable acetabular component with well-anchored screws, the amount of backside wear should not cause clinical problems. Impingement of the screw-heads could produce more wear particles than those generated at the liner-shell interface. Because the rate of backside volumetric change is only 2.8% of the rate of volumetric articular wear and since creep is likely to contribute a significant portion to this, the debris generated by wear at the backside of the liner may not be sufficient to create a strong osteolytic response.

Hip simulators have been used for ten years to determine the tribological performance of large-head metal-on-metal devices using traditional test conditions. However, the hip simulator protocols were originally developed to test metal-on-polyethylene devices. We have used patient activity data to develop a more physiologically relevant test protocol for metal-on-metal devices. This includes stop/start motion, a more appropriate walking frequency, and alternating kinetic and kinematic profiles.

There has been considerable discussion about the effect of heat treatments on the wear of metal-on-metal cobalt chromium molybdenum (CoCrMo) devices. Clinical studies have shown a higher rate of wear, levels of metal ions and rates of failure for the heat-treated metal compared to the as-cast metal CoCrMo devices. However, hip simulator studies in vitro under traditional testing conditions have thus far not been able to demonstrate a difference between the wear performance of these implants.

Using a physiologically relevant test protocol, we have shown that heat treatment of metal-on-metal CoCrMo devices adversely affects their wear performance and generates significantly higher wear rates and levels of metal ions than in as-cast metal implants.

We investigated the rate of polyethylene wear of a cementless acetabular component at different periods of follow-up in order to test the hypothesis than an irrecoverable deformation process (creep) was followed by an initially low, but gradually increasing wear rate. We studied prospectively 93 uncemented total hip arthroplasties in 83 patients (mean age 50 years (22 to 63)) with a mean follow-up of 8.2 years (3 to 12). We measured the penetration of the femoral head from radiographs taken immediately after surgery at three, six and nine years, or at the latest follow-up.

The median wear rate was 0.17 mm per year in the first three years, a finding which we considered to be caused by creep. Thereafter, the rate of wear declined to 0.07 mm per year (four- to six-year period) and then increased to 0.17 mm per year (seven to nine years) and 0.27 mm per year (more than nine years), which we considered to be a reflection of genuine polyethylene wear. After the nine-year follow-up the wear rates were higher in patients with marked osteolysis. We found no relationship between the inclination angle of the acetabular component or femoral head orientation and the rate of wear. No acetabular component required revision.

We retrospectively identified 18 consecutive patients with synovial chrondromatosis of the shoulder who had arthroscopic treatment between 1989 and 2004. Of these, 15 were available for review at a mean follow-up of 5.3 years (2.3 to 16.5). There were seven patients with primary synovial chondromatosis, but for the remainder, the condition was a result of secondary causes. The mean Constant score showed that pain and activities of daily living were the most affected categories, being only 57% and 65% of the values of the normal side. Surgery resulted in a significant improvement in the mean Constant score in these domains from 8.9 (4 to 15) to 11.3 (2 to 15) and from 12.9 (5 to 20) to 18.7 (11 to 20), respectively (unpaired t-test, p = 0.04 and p < 0.0001, respectively). Movement and strength were not significantly affected. Osteoarthritis was present in eight patients at presentation and in 11 at the final review. Recurrence of the disease with new loose bodies occurred in two patients from the primary group at an interval of three and 12 years post-operatively. In nine patients, loose bodies were also present in the bicipital groove; seven of these underwent an open bicipital debridement and tenodesis.

We found that arthroscopic debridement of the glenohumeral joint and open debridement and tenodesis of the long head of biceps, when indicated, are safe and effective in relieving symptoms at medium-term review.

We have evaluated the results of total hip replacement in patients with congenital hip disease using 46 cemented all-polyethylene Charnley acetabular components implanted with the cotyloplasty technique in 34 patients (group A), and compared them with 47 metal-backed cementless acetabular components implanted without bone grafting in 33 patients (group B). Patients in group A were treated between 1988 and 1993 and those in group B between 1990 and 1995. The mean follow-up for group A was 16.6 years (12 to 18) and the mean follow-up for group B was 13.4 years (10 to 16).

Revision for aseptic loosening was undertaken in 15 hips (32.6%) in group A and in four hips (8.5%) in group B. When liner exchange was included, a total of 13 hips were revised in group B (27.7%). The mean polyethylene wear was 0.11 mm/yr (0.002 to 0.43) and 0.107 mm/yr (0 to 0.62) for groups A and B, respectively. Polyethylene wear in group A was associated with linear osteolysis, and in group B with expansile osteolysis.

In patients with congenital hip disease, when 80% cover of the implant can be obtained, a cementless acetabular component appears to be acceptable and provides durable fixation. However, because of the type of osteolysis arising with these devices, early exchange of a worn liner is recommended before extensive bone loss makes revision surgery more complicated.

It has been suggested that the wear of ultra-high molecular weight polyethylene (UHMWPE) in total hip replacement is substantially reduced when the femoral head is ceramic rather than metal. However, studies of alumina and zirconia ceramic femoral heads on the penetration of an UHMWPE liner in vivo have given conflicting results.

The purpose of this study was to examine the surface characteristics of 30 alumina and 24 zirconia ceramic femoral heads and to identify any phase transformation in the zirconia heads. We also studied the penetration rate of alumina and zirconia heads into contemporary UHMWPE liners. The alumina heads had been implanted for a mean of 11.3 years (8.1 to 16.2) and zirconia heads for a mean of 9.8 years (7.5 to 15).

The mean surface roughness values of the explanted alumina heads (Ra 40.12 nm and Rpm 578.34 nm) were similar to those for the explanted zirconia heads (Ra 36.21 nm and Rpm 607.34 nm). The mean value of the monoclinic phase of two control zirconia heads was 1% (0.8% to 1.5%) and 1.2% (0.9% to 1.3%), respectively. The mean value of the monoclinic phase of 24 explanted zirconia heads was 7.3% (1% to 26%).

In the alumina group, the mean linear penetration rate of the UMWPE liner was 0.10 mm/yr (0.09 to 0.12) in hips with low Ra and Rpm values (13.22 nm and 85.91 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.13 mm/yr (0.07 to 0.23) in hips with high Ra and Rpm values (198.72 nm and 1329 nm, respectively). This difference was significant (p = 0.041).

In the zirconia head group, the mean linear penetration rate of the UHMWPE liner was 0.09 mm/yr (0.07 to 0.14) in hips with low Ra and Rpm values (12.78 nm and 92.99 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.12 mm/yr (0.08 to 0.22) in hips with high Ra and Rpm values (199.21 nm and 1381 nm, respectively). This difference was significant (p = 0.039).

The explanted zirconia heads which had a minimal phase transformation had similar surface roughness and a similar penetration rate of UHMWPE liner as the explanted alumina head.

We carried out a prospective study of 118 hydroxyapatite-coated, cementless total knee replacements in patients who were ≤ 55 years of age and who had primary (92; 78%) or post-traumatic (26; 22%) osteoarthritis. The mean period of follow-up was 7.9 years (5 to 12.5). The Knee Society clinical scores improved from a pre-operative mean of 98 (0 to 137) to a mean of 185 (135 to 200) at five years, and 173 (137 to 200) at ten years. There were two revisions of the tibial component because of aseptic loosening, and one case of polyethylene wear requiring further surgery. There was no osteolysis or progressive radiological loosening of any other component. At 12 years, the overall rate of implant survival was 97.5% (excluding exchange of spacer) and 92.1% (including exchange of spacer).

Cementless total knee replacement can achieve excellent long-term results in young, active patients with osteoarthritis. In contrast to total hip replacement, polyethylene wear, osteolysis and loosening of the prosthesis were not major problems for these patients, although it is possible that this observation could change with longer periods of follow-up.