Aims. Several short- and mid-term studies have shown minimal liner wear of highly cross-linked polyethylene (HXLPE) in total hip arthroplasty (THA), but the safety of using thinner HXLPE liners to maximize femoral head size remains uncertain. The objective of this study was to analyze clinical survival and radiological wear rates of patients with HXLPE liners, a 36 mm femoral head, and a small acetabular component with a minimum of ten years’ follow-up. Methods. We retrospectively identified 55 patients who underwent primary THA performed at a single centre, using HXLPE liners with 36 mm cobalt-chrome heads in acetabular components with an outer diameter of 52 mm or smaller. Patient demographic details, implant details, death, and all-cause revisions were recorded. Cox regression and Kaplan-Meier survival was used to determine all-cause and liner-specific revision. Of these 55 patients, 22 had a minimum radiological follow-up of seven years and were assessed radiologically for linear and volumetric wear. Results. Overall survival rate for all-cause revision was 94.5% (95% confidence interval (CI) 81.7% to 97.2%) at a mean follow-up of 12.8 years (10.9 to 18.7). Three patients were revised, none for liner wear, fracture, or dissociation. A total of 22 patients were included in the radiological analysis (mean follow-up 9.9 years (7.5 to 13.7)). Mean linear liner wear was 0.085 mm (95% CI -0.086 to 0.257) and the volumetric wear rate was 11.097 mm. 3. /year (95% CI -6.5 to 28.7). Conclusion. Using HXLPE liners with 36 mm heads in 52 mm acetabular components or smaller is safe, with excellent survival and low rates of linear and volumetric wear at medium-term follow-up. Patients did not require revision surgery for liner complications such as fracture, dissociation, or wear. Our results suggest that the advantages of using larger heads outweigh the potential risks of using thin HXLPE liners. Cite this article: Bone Joint J 2023;105-B(1):29–34

Aims. We aimed to investigate if the use of the largest possible cobalt-chromium head articulating with polyethylene acetabular inserts would increase the in vivo wear rate in total hip arthroplasty. Methods. In a single-blinded randomized controlled trial, 96 patients (43 females), at a median age of 63 years (interquartile range (IQR) 57 to 69), were allocated to receive either the largest possible modular femoral head (36 mm to 44 mm) in the thinnest possible insert or a standard 32 mm head. All patients received a vitamin E-doped cross-linked polyethylene insert and a cobalt-chromium head. The primary outcome was proximal head penetration measured with radiostereometric analysis (RSA) at two years. Secondary outcomes were volumetric wear, periacetabular radiolucencies, and patient-reported outcomes. Results. At two years, 44 patients in each group were available for RSA assessment. The median total two-year proximal head penetration was -0.02 mm (IQR -0.09 to 0.07; p = 0.548) for the largest possible head and -0.01 mm (IQR -0.07 to 0.10; p = 0.525) for 32 mm heads. Their difference was not statistically significant (p = 0.323). Neither group demonstrated a bedding-in period. The median steady-state volumetric wear rates were 6.1 mm. 3. /year (IQR -59 to 57) and 3.5 mm. 3. /year (-21 to 34) respectively, and did not differ between the groups (p = 0.848). There were no statistically significant differences in periacetabular radiolucencies or patient-reported outcomes. Conclusion. The use of the largest possible metal head did not increase vitamin E-doped cross-linked polyethylene wear compared with 32 mm heads at two years. Linear wear was negligible and volumetric wear rates were very low in both head size groups. There was a tendency towards higher values of volumetric wear in large heads that warrants longer-term evaluation before any definite conclusions about the association between head size and wear can be drawn. Cite this article: Bone Joint J 2021;103-B(7):1206–1214

We have reviewed 70 patients with bilateral simultaneous total hip arthroplasties to determine the rate of failure and to compare polyethylene wear and osteolysis between an implant with a cobalt-chrome head and Hylamer liner with that of a zirconia head and Hylamer liner. The mean thickness of the polyethylene liner was 11.0 mm (8.8 to 12.2) in the hip with a zirconia head and 10.7 mm (8.8 to 12.2) in that with a cobalt-chrome head. At follow-up at 6.4 years no acetabular or femoral component had been revised for aseptic loosening and no acetabular or femoral component was loose according to radiological criteria in both the cemented and cementless groups. The mean rate of linear wear and annual wear rate were highest in the 22 mm zirconia femoral head (1.25 mm (SD 1.05) and 0.21 mm (SD 0.18), respectively) and lowest in the 22 mm cobalt-chrome femoral head (0.70 mm (SD 0.39) and 0.12 mm (SD 0.07), respectively). The mean volumetric wear was highest in the 28 mm zirconia femoral head (730.79 mm. 3. ) and lowest in the 22 mm cobalt-chrome femoral head (264.67 mm. 3. ), but if the results were compared by size of the femoral head and type of material there was no statistical difference (p > 0.05). Sequential measurements of annual wear showed that the zirconia femoral head had a relatively higher rate of penetration than the cobalt-chrome head over the first three years; thereafter the rate of wear was reduced and compared favourably with that of cobalt-chrome heads. There was a statistically significant relationship between the wear of the polyethylene liner and the age of the patient, male gender and the degree of abduction angle of the cup, but not diagnosis, weight, hip score, range of movement, or amount of anteversion. Osteolysis was identified on both sides of the acetabulum in six patients (9%). Of 12 hips with acetabular osteolysis, six had a 28 mm cobalt-chrome femoral head and the remaining six a 28 mm zirconia head. Osteolysis was observed in zones 1A and 7A of the femur in two hips (3%) with a 28 mm zirconia head (cemented hip) and in four (6%) with a 28 mm cobalt-chrome femoral head (cementless hip). Our findings suggest that although the performance of a zirconia femoral head with a Hylamer liner was not statistically different from that of a cobalt-chrome femoral head and Hylamer liner, there was a trend for the zirconia head to be worse than the cobalt-chrome femoral head

Aims. The aim of this study was to determine whether there is a difference in the rate of wear between acetabular components positioned within and outside the ‘safe zones’ of anteversion and inclination angle. Patients and Methods. We reviewed 100 hips in 94 patients who had undergone primary total hip arthroplasty (THA) at least ten years previously. Patients all had the same type of acetabular component with a bearing couple which consisted of a 28 mm cobalt-chromium head on a highly crosslinked polyethylene (HXLPE) liner. A supine radiostereometric analysis (RSA) examination was carried out which acquired anteroposterior (AP) and lateral paired images. Acetabular component anteversion and inclination angles were measured as well as total femoral head penetration, which was divided by the length of implantation to determine the rate of polyethylene wear. Results. The mean anteversion angle was 19.4° (-15.2° to 48°, . sd. 11.4°), the mean inclination angle 43.4° (27.3° to 60.5°, . sd. 6.6°), and the mean wear rate 0.055 mm/year (. sd. 0.060). Exactly half of the hips were positioned inside the ‘safe zone’. There was no difference (median difference, 0.012 mm/year; p = 0.091) in the rate of wear between acetabular components located within or outside the ‘safe zone’. When compared to acetabular components located inside the ‘safe zone’, the wear rate was no different for acetabular components that only achieved the target anteversion angle (median difference, 0.012 mm/year; p = 0.138), target inclination angle (median difference, 0.013 mm/year; p = 0.354), or neither target (median difference, 0.012 mm/year; p = 0.322). Conclusion. Placing the acetabular component within or outside the ‘safe zone’ did not alter the wear rate of HXLPE at long-term follow-up to a level that risked osteolysis. HXLPE appears to be a forgiving bearing material in terms of articular surface wear, but care must still be taken to position the acetabular component correctly so that the implant is stable. Cite this article: Bone Joint J 2018;100-B:891-7

Aims

Modular dual-mobility (DM) articulations are increasingly used during total hip arthroplasty (THA). However, concerns remain regarding the metal liner modularity. This study aims to correlate metal artifact reduction sequence (MARS)-MRI abnormalities with serum metal ion levels in patients with DM articulations.

We retrieved 159 femoral heads at revision surgery to determine changes in surface configuration. Macroscopic wear of the head was observed in three bipolar hip prostheses as a result of three-body wear. There was a considerable change in surface roughness in the internal articulation of bipolar hip prostheses. Roughness in alumina heads was almost the same as that in new cobalt-chromium heads. The annual linear wear rate of polyethylene cups with alumina heads was less than that of cups with cobalt-chromium alloy heads. Polyethylene wear was increased in the prostheses which had increased roughness of the head

Aims

The primary aim of this trial was to compare the subsidence of two similar hydroxyapatite-coated titanium femoral components from different manufacturers. Secondary aims were to compare rotational migration (anteversion/retroversion and varus/valgus tilt) and patient-reported outcome measures between both femoral components.

Aims

In metal-on-polyethylene (MoP) total hip arthroplasty (THA), large metal femoral heads have been used to increase stability and reduce the risk of dislocation. The increased size of the femoral head can, however, lead to increased taper corrosion, with the release of metal ions and adverse reactions. The aim of this study was to investigate the relationship between the size of the femoral head and the levels of metal ions in the blood in these patients.

In this prospective, randomised study, we have compared the wear rate of cemented, acetabular polyethylene cups articulating with either a 22 mm or a 32 mm cobalt-chromium head. We evaluated 89 patients who had a total of 484 radiographs. The mean follow-up period was 71.4 months (SD 29.1). All the radiographs were digitised and electronically measured. The linear wear rate was significantly higher during the first two years and decreased after this period to a constant value. We suggest that this is partly due to a ‘run-in’ process caused by irregularities between surfaces of the cup and head and an initial plastic deformation of the polyethylene. The mean volumetric wear was 120.3 mm. 3. /year for the 32 mm head, which was significantly higher than the 41.5 mm. 3. /year for the 22 mm heads. The mean linear wear rate was not significantly different. We were, however, unable to find radiological signs of osteolysis in the patients who had higher wear rates

Aims

Dual mobility (DM) implants have been shown to reduce the dislocation rate after total hip arthroplasty (THA), but there remain concerns about the use of cobalt chrome liners inserted into titanium shells. The aim of this study was to assess the clinical outcomes, metal ion levels, and periprosthetic femoral bone mineral density (BMD) at mid-term follow-up in young, active patients receiving a modular DM THA.

Aims

In patients with a “dry” aspiration during the investigation of prosthetic joint infection (PJI), saline lavage is commonly used to obtain a sample for analysis. The aim of this study was to investigate prospectively the impact of saline lavage on synovial fluid analysis in revision arthroplasty.

Aims

To present a surgically relevant update of trunnionosis.

Aims

The aim of this study was to estimate the 90-day risk of revision for periprosthetic femoral fracture associated with design features of cementless femoral stems, and to investigate the effect of a collar on this risk using a biomechanical in vitro model.

Aims

The aim of this study was to evaluate fretting and corrosion in retrieved oxidized zirconium (OxZr; OXINIUM, Smith & Nephew, Memphis, Tennessee) femoral heads and compare the results with those from a matched cohort of cobalt-chromium (CoCr) femoral heads.

Aims

Osteolysis, secondary to local and systemic physiological effects, is a major challenge in total hip arthroplasty (THA). While osteolytic defects are commonly observed in long-term follow-up, how such lesions alter the distribution of stress is unclear. The aim of this study was to quantitatively describe the biomechanical implication of such lesions by performing subject-specific finite-element (FE) analysis on patients with osteolysis after THA.

Aims

Fretting and corrosion at the modular head/neck junction, known as trunnionosis, in total hip arthroplasty (THA) is a cause of adverse reaction to metal debris (ARMD). We describe the outcome of revision of metal-on-polyethylene (MoP) THA for ARMD due to trunnionosis with emphasis on the risk of major complications.

Aims

We present the ten-year data of a cohort of patients, aged between 18 and 65 years (mean age 52.7 years; 19 to 64), who underwent total hip arthroplasty. Patients were randomised to be treated with a cobalt-chrome (CoCr) femoral head with an ultra-high molecular weight polyethylene (UHMWPE), highly cross-linked polyethylene (XLPE) or ceramic-on-ceramic (CoC) bearing surface.

Aims

We present a case series of ten metal-on-polyethylene total hip arthroplasties (MoP THAs) with delayed dislocation associated with unrecognised adverse local tissue reaction due to corrosion at the trunnion and pseudotumour formation.

Aims

The widely used and well-proven Palacos R (a.k.a. Refobacin Palacos R) bone cement is no longer commercially available and was superseded by Refobacin bone cement R and Palacos R + G in 2005. However, the performance of these newly introduced bone cements have not been tested in a phased evidence-based manner, including roentgen stereophotogrammetric analysis (RSA).

The long-term results of grafting with hydroxyapatite granules for acetabular deficiency in revision total hip replacement are not well known. We have evaluated the results of revision using a modular cup with hydroxyapatite grafting for Paprosky type 2 and 3 acetabular defects at a minimum of ten years’ follow-up. We retrospectively reviewed 49 acetabular revisions at a mean of 135 months (120 to 178). There was one type 2B, ten 2C, 28 3A and ten 3B hips. With loosening as the endpoint, the survival rate was 74.2% (95% confidence interval 58.3 to 90.1). Radiologically, four of the type 3A hips (14%) and six of the type 3B hips (60%) showed aseptic loosening with collapse of the hydroxyapatite layer, whereas no loosening occurred in type 2 hips. There was consolidation of the hydroxyapatite layer in 33 hips (66%). Loosening was detected in nine of 29 hips (31%) without cement and in one of 20 hips (5%) with cement (p = 0.03, Fisher’s exact probability test). The linear wear and annual wear rate did not correlate with loosening.

These results suggest that the long-term results of hydroxyapatite grafting with cement for type 2 and 3A hips are encouraging.

We compared the incidence of pseudotumours after large head metal-on-metal (MoM) total hip arthroplasty (THA) with that after conventional metal-on-polyethylene (MoP) THA and assessed the predisposing factors to pseudotumour formation.

From a previous randomised controlled trial which compared large head (38 mm to 60 mm) cementless MoM THA with conventional head (28 mm) cementless MoP THA, 93 patients (96 THAs: 41 MoM (21 males, 20 females, mean age of 64 years, standard deviation (sd) 4) and 55 MoP (25 males, 30 females, mean age of 65 years, sd 5) were recruited after a mean follow-up of 50 months (36 to 64).

The incidence of pseudotumours, measured using a standardised CT protocol was 22 (53.7%) after MoM THA and 12 (21.8%) after MoP THA. Women with a MoM THA were more likely to develop a pseudotumour than those with a MoP THA (15 vs 7, odds ratio (OR) = 13.4, p < 0.001). There was a similar incidence of pseudotumours in men with MoM THAs and those with MoP THAs (7 vs 5, OR = 2.1, p = 0.30). Elevated cobalt levels (≥ 5 microgram/L) were only associated with pseudotumours in women with a MoM THA. There was no difference in mean Oxford and Harris hip scores between patients with a pseudotumour and those without.

Contrary to popular belief, pseudotumours occur frequently around MoP THAs. Women with a MoM THA and an elevated cobalt level are at greatest risk. In this study, pseudotumours had no effect on the functional outcome after either large head MoM or conventional MoP THA.

Cite this article: Bone Joint J 2015;97-B:1481–7.

We reviewed the results of 84 total hip replacements performed with a short metaphyseal-fitting anatomical cementless femoral component in 84 unselected consecutive patients with a mean age of 78.9 years (70 to 88). The mean follow-up was 4.6 years (4 to 5). The mean pre-operative Harris hip score was 26 points (0 to 56), which improved to 89 (61 to 100) at the final follow-up. No patient had thigh pain. The mean pre-operative Western Ontario and McMaster Universities osteoarthritis index score was 61 points (48 to 75), which improved to 21 (6 to 46). The mean University of California, Los Angeles activity score was 5.5 points (3 to 7) at the final follow-up. Osseointegration was seen in all femoral and acetabular components. All hips had grade 1 stress shielding of the proximal femur. No acetabular or femoral osteolysis was identified.

These results demonstrate that a short metaphyseal-fitting femoral component achieves optimal fixation without diaphyseal anchorage in elderly patients.

A modular femoral head–neck junction has practical advantages in total hip replacement. Taper fretting and corrosion have so far been an infrequent cause of revision. The role of design and manufacturing variables continues to be debated. Over the past decade several changes in technology and clinical practice might result in an increase in clinically significant taper fretting and corrosion. Those factors include an increased usage of large diameter (36 mm) heads, reduced femoral neck and taper dimensions, greater variability in taper assembly with smaller incision surgery, and higher taper stresses due to increased patient weight and/or physical activity. Additional studies are needed to determine the role of taper assembly compared with design, manufacturing and other implant variables.

Cite this article: Bone Joint J 2013;95-B, Supple A:3–6.

We studied prospectively the long-term results of the Charnley Elite-Plus femoral stem in 184 consecutive young patients (194 hips). There were 130 men and 54 women with a mean age of 49.1 years (21 to 60). The predominant diagnosis was osteonecrosis of the femoral head (63.6%, 117 patients). Clinical and radiological evaluation was undertaken at each follow-up. The mean follow-up was 11.2 years (10 to 12).

The mean pre-operative Harris hip score was 43.4 (12 to 49) which improved to 91 (59 to 100) at the final follow-up. The survival of the femoral stem at 12 years was 99% with revision as the end-point. The mean annual linear wear of the polyethylene liner was 0.17 mm (0.13 to 0.22). The prevalence of acetabular osteolysis was 10.8% (21 hips) and osteolysis of the calcar femorale 12.9% (25 hips).

A third-generation cementing technique, accurate alignment of the stem and the use of a 22 mm zirconia head were important factors in the prevention of aseptic loosening of the Elite Plus femoral stem in these high-risk young patients.

The aim of this prospective randomised study was to compare the clinical and radiological results of a cemented all-polyethylene Ultima acetabular component with those of a cementless porous-coated acetabular component (PFC) following total hip replacement (THR). A total of 287 patients received either a polyethylene acetabular component (group A) or a cobalt–chromium porous-coated component (group B) with an identical cemented femoral component and 28 mm cobalt-chromium head, thus making it the largest study of its type. Patients were evaluated radiologically and clinically using the Harris hip score (HHS). Group A comprised 183 patients (73 male, 110 female) with a mean age of 71.3 years (55 to 89). Group B comprised 104 patients (48 male, 56 female) with a mean age of 69.8 years (56 to 89). A total of 16 patients (13 in Group A, three in Group B) did not have post-operative data for analysis. The mean follow-up in group A was 7.52 years (0.4 to 15.0) and in Group B 7.87 years (0.5 to 14.0).

At final follow-up the mean HHS was similar between groups A and B (74.5 (25 to 100) and 78.0 (37 to 100), respectively; p = 0.068). The total number of revisions for any cause was 28, 17 of which were in group A and 11 in group B. The ten-year survivorship was 86.8% (95% confidence interval (CI) 78.4 to 92.1) and 89.2% (95% CI 78.3 to 94.8) for groups A and B, respectively (log-rank p-value = 0.938). A total of 20 cemented and two cementless acetabular components had evidence of acetabular radiolucencies or acetabular component migration at last follow-up (p = 0.001).

These results indicate that patients with a cemented all-polyethylene and cementless porous-coated polyethylene lined acetabular component have similar long-term clinical outcomes.

Metallosis after shoulder replacement has not previously been described in the literature. We report a patient who developed extensive metallosis after implantation of an uncemented Nottingham shoulder replacement. He underwent a revision procedure.

Examination of the retrieved prosthesis showed that the titanium porous coating was separating from the humeral stem and becoming embedded in the ultra-high-molecular-weight polyethylene glenoid component, resulting in abrasive wear of the humeral component. There was metallosis despite exchange of the modular humeral head. Both components had to be exchanged to resolve the problem.

In Africa the amount of joint replacement surgery is increasing, but the indications for operation and the age of the patients are considerably different from those in the developed world. New centres with variable standards of care and training of the surgeons are performing these procedures and it is important that a proper audit of this work is undertaken.

In Malawi, we have pioneered a Registry which includes all joint replacements that have been carried out in the country. The data gathered include the age, gender, indication for operation, the prosthesis used, the surgical approach, the use of bone graft, the type of cement, pressurising systems and the thromboprophylaxis used. All patients have their clinical scores recorded pre-operatively and then after three and six months and at one year. Before operation all patients are counselled and on consent their HIV status is established allowing analysis of the effect of HIV on successful joint replacement.

To date, 73 total hip replacements (THRs) have been carried out in 58 patients by four surgeons in four different hospitals. The most common indications for THR were avascular necrosis (35 hips) and osteoarthritis (22 hips). The information concerning 20 total knee replacements has also been added to the Registry.

We report the case of a 12-year-old boy with polyostotic fibrous dysplasia of the upper femur in whom a massive customised polyethylene prosthesis functioned successfully for more than fifty years.

In 2004 we described the ten-year prospective results of 38 total hip replacements using the Furlong hydroxyapatite-ceramic-coated femoral component in 35 patients < 50 years old. We have now reviewed the surviving 35 arthroplasties in 33 patients at a mean of 16 years (10.3 to 19.9). The mean age of the surviving patients at the time of operation was 41.3 years (26.0 to 49.0). Of these, eight have undergone revision of their acetabular component for aseptic loosening. None of the femoral components has had revision for aseptic loosening giving a survival rate of 100% at 16 years (95% confidence interval 89% to 100%).

The Furlong hydroxyapatite-ceramic-coated femoral component gives excellent long-term survival in young and active patients.

The original forged Müller straight stem (CoNiCr) has shown excellent ten- to 15-year results. We undertook a long-term survival analysis with special emphasis on radiological changes within a 20-year period of follow-up.

In all, 165 primary total hip replacements, undertaken between July 1984 and June 1987 were followed prospectively. Clinical follow-up included a standardised clinical examination, and radiological assessment was based on a standardised anteroposterior radiograph of the pelvis, which was studied for the presence of osteolysis, debonding and cortical atrophy.

Survival of the stem with revision for any reason was 81% (95% confidence interval (CI), 76 to 86) at 20 years and for aseptic loosening 87% (95% CI, 82 to 90). At the 20-year follow-up, 15 of the surviving 36 stems showed no radiological changes. Debonding (p = 0.005), osteolysis (p = 0.003) and linear polyethylene wear (p = 0.016) were associated with aseptic loosening, whereas cortical atrophy was not associated with failure (p = 0.008).

The 20-year results of the Müller straight stem are comparable to those of other successful cemented systems with similar follow-up. Radiological changes are frequently observed, but with a low incidence of progression, and rarely result in revision. Cortical atrophy appears to be an effect of ageing and not a sign of loosening of the femoral component.

Bone surface strains were measured in cadaver femora during loading prior to and after resurfacing of the hip and total hip replacement using an uncemented, tapered femoral component. In vitro loading simulated the single-leg stance phase during walking. Strains were measured on the medial and the lateral sides of the proximal aspect and the mid-diaphysis of the femur. Bone surface strains following femoral resurfacing were similar to those in the native femur, except for proximal shear strains, which were significantly less than those in the native femur. Proximomedial strains following total hip replacement were significantly less than those in the native and the resurfaced femur.

These results are consistent with previous clinical evidence of bone loss after total hip replacement, and provide support for claims of bone preservation after resurfacing arthroplasty of the hip.

Between June 1991 and January 1995, 42 hydroxyapatite-coated CAD-CAM femoral components were inserted in 25 patients with inflammatory polyarthropathy, 21 of whom had juvenile idiopathic arthritis. Their mean age was 21 years (11 to 35). All the patients were reviewed clinically and radiologically at one, three and five years. At the final review at a mean of 11.2 years (8 to 13) 37 hips in 23 patients were available for assessment.

A total of four femoral components (9.5%) had failed, of which two were radiologically loose and two were revised. The four failed components were in patients aged 16 years or less at the time of surgery. Hydroxyapatite-coated customised femoral components give excellent medium- to long-term results in skeletally-mature young adults with inflammatory polyarthropathy. Patients aged less than 16 years at the time of surgery have a risk of 28.5% of failure of the femoral component at approximately ten years.

We describe the results at five years of a prospective study of a new tri-tapered polished, cannulated, cemented femoral stem implanted in 51 patients (54 hips) with osteoarthritis. The mean age and body mass index of the patients was 74 years and 27.9, respectively. Using the anterolateral approach, half of the stems were implanted by a consultant orthopaedic surgeon and half by six different registrars. There were three withdrawals from the study because of psychiatric illness, a deep infection and a recurrent dislocation. Five deaths occurred prior to five-year follow-up and one patient withdrew from clinical review.

In the remaining 51 hips the mean pre-operative Oxford hip score was 47 points which decreased to 19 points at five years (45 hips). Of the stems 49 (98%) were implanted within 1° of neutral in the femoral canal. The mean migration of the stem at five years was 1.9 mm and the survivorship for aseptic loosening was 100%. There was no significant difference in outcome between the consultant and registrar groups. At five years, the results were comparable with those of other polished, tapered, cemented stems. Long-term surveillance continues.

We carried out a clinical and radiological review of 103 cementless primary hip arthroplasties with a tapered rectangular grit-blasted titanium press-fit femoral component and a threaded conical titanium acetabular component at a mean follow-up of 14.4 years (10.2 to 17.1).

The mean Harris hip score at the last follow-up was 89.2 (32 to 100). No early loosening and no fracture of the implant were found. One patient needed revision surgery because of a late deep infection. In 11 hips (10.7%), the reason for revision was progressive wear of the polyethylene liner. Exchange of the acetabular component because of aseptic loosening without detectable liner wear was carried out in three hips (2.9%).

After 15 years the survivorship with aseptic loosening as the definition for failure was 95.6% for the acetabular component and 100% for the femoral component.

We report the clinical and radiological outcome of 86 revisions of cemented hip arthroplasties using JRI-Furlong hydroxyapatite-ceramic-coated acetabular and femoral components. The acetabular component was revised in 62 hips and the femoral component in all hips. The mean follow-up was 12.6 years and no patient was lost to follow-up.

The mean age of the patients was 71.2 years. The mean Harris hip and Oxford scores were 82 (59 to 96) and 23.4 (14 to 40), respectively. The mean Charnley modification of the Merle d’Aubigné and Postel score was 5 (3 to 6) for pain, 4.9 (3 to 6) for movement and 4.4 (3 to 6) for mobility. Migration of the acetabular component was seen in two hips and the mean acetabular inclination was 42.6°. The mean linear polyethylene wear was 0.05 mm/year. The mean subsidence of the femoral component was 1.9 mm and stress shielding was seen in 23 (28%) with bony ingrowth in 76 (94%). Heterotopic ossification was seen in 12 hips (15%). There were three re-revisions, two for deep sepsis and one for recurrent dislocation and there were no re-revisions for aseptic loosening. The mean EuroQol EQ-5D description scores and health thermometer scores were 0.69 (0.51 to 0.89) and 79 (54 to 95), respectively. With an end-point of definite or probable loosening, the probability of survival at 12 years was 93.9% and 95.6% for the acetabular and femoral components, respectively. Overall survival at 12 years, with removal or further revision of either component for any reason as the end-point, was 92.3%.

Our study supports the continued use of this arthroplasty and documents the durability of hydroxyapatite-ceramic-coated components.