Hip implant retrieval analysis is the most important source of insight into the performance of new materials and designs of hip arthroplasties. Even the most rigorous in vitro testing will not accurately simulate the behavior of implant materials and new designs of prosthetic arthroplasties. Retrieval analysis has revealed such factors as the effects of gamma-in-air sterilisation of polyethylene, fatigue failure mechanisms of polymethylmethacrylate bone cement, fretting corrosion of Morse taper junctions, third body wear effects of both hard-on-hard and hard-on-soft bearing couples, and the effects of impingement of components on the full spectrum of bearing surfaces, none of which was predicted by pre-implantation in vitro testing of these materials and combinations. The temporal sequence of the retrieval process is approximately six years from first implantation through retrieval analysis, laboratory investigation, and publication of results, and thus, in addition to rigorous clinical evaluation, represents the true development and insight cycle for new designs and materials

This multicentre study analysed 12 alumina ceramic-on-ceramic components retrieved from squeaking total hip replacements after a mean of 23 months in situ (11 to 61). The rates and patterns of wear seen in these squeaking hips were compared with those seen in matched controls using retrieval data from 33 ‘silent’ hip replacements with similar ceramic bearings. All 12 bearings showed evidence characteristic of edge-loading wear. The median rate of volumetric wear was 3.4 mm. 3. /year for the acetabular component, 2.9 mm. 3. /year on the femoral heads and 6.3 mm. 3. /year for head and insert combined. This was up to 45 times greater than that of previously reported silent ceramic-on-ceramic retrievals. The rate of wear seen in ceramic components revised for squeaking hips appears to be much greater than in that seen in retrievals from ‘silent’ hips.

Arthroplasty registries are important for the surveillance of joint replacements and the evaluation of outcome. Independent validation of registry data ensures high quality. The ability for orthopaedic implant retrieval centres to validate registry data is not known. We analysed data from the National Joint Registry for England, Wales and Northern Ireland (NJR) for primary metal-on-metal hip arthroplasties performed between 2003 and 2013. Records were linked to the London Implant Retrieval Centre (RC) for validation. A total of 67 045 procedures on the NJR and 782 revised pairs of components from the RC were included. We were able to link 476 procedures (60.9%) recorded with the RC to the NJR successfully. However, 306 procedures (39.1%) could not be linked. The outcome recorded by the NJR (as either revised, unrevised or death) for a primary procedure was incorrect in 79 linked cases (16.6%). The rate of registry-retrieval linkage and correct assignment of outcome code improved over time. The rates of error for component reference numbers on the NJR were as follows: femoral head category number 14/229 (5.0%); femoral head batch number 13/232 (5.3%); acetabular component category number 2/293 (0.7%) and acetabular component batch number 24/347 (6.5%). . Registry-retrieval linkage provided a novel means for the validation of data, particularly for component fields. This study suggests that NJR reports may underestimate rates of revision for many types of metal-on-metal hip replacement. This is topical given the increasing scope for NJR data. We recommend a system for continuous independent evaluation of the quality and validity of NJR data. Cite this article: Bone Joint J 2015;97-B:10–18

The early failure and revision of bimodular primary total hip arthroplasty prostheses requires the identification of the risk factors for material loss and wear at the taper junctions through taper wear analysis. Deviations in taper geometries between revised and pristine modular neck tapers were determined using high resolution tactile measurements. A new algorithm was developed and validated to allow the quantitative analysis of material loss, complementing the standard visual inspection currently used. The algorithm was applied to a sample of 27 retrievals (in situ from 2.9 to 38.1 months) of the withdrawn Rejuvenate modular prosthesis. The mean wear volumes on the flat distal neck piece taper was 3.35 mm. 3. (0.55 to 7.57), mainly occurring in a characteristic pattern in areas with high mechanical loading. Wear volume tended to increase with time to revision (r² = 0.423, p = 0.001). Implant and patient specific data (offset, stem size, patient’s mass, age and body mass index) did not correlate with the amount of material loss observed (p >  0.078). Bilaterally revised implants showed higher amounts of combined total material loss and similar wear patterns on both sides. The consistent wear pattern found in this study has not been reported previously, suggesting that the device design and materials are associated with the failure of this prosthesis. Cite this article: Bone Joint J 2015;97-B:1350–7

Aims

Surgeons have commonly used modular femoral heads and stems from different manufacturers, although this is not recommended by orthopaedic companies due to the different manufacturing processes.

We compared the rate of corrosion and rate of wear at the trunnion/head taper junction in two groups of retrieved hips; those with mixed manufacturers (MM) and those from the same manufacturer (SM).

This study compared component wear rates and pre-revision blood metal ions levels in two groups of failed metal-on-metal hip arthroplasties: hip resurfacing and modular total hip replacement (THR).

There was no significant difference in the median rate of linear wear between the groups for both acetabular (p = 0.4633) and femoral (p = 0.0872) components. There was also no significant difference in the median linear wear rates when failed hip resurfacing and modular THR hips of the same type (ASR and Birmingham hip resurfacing (BHR)) were compared.

Unlike other studies of well-functioning hips, there was no significant difference in pre-revision blood metal ion levels between hip resurfacing and modular THR.

Edge loading was common in both groups, but more common in the resurfacing group (67%) than in the modular group (57%). However, this was not significant (p = 0.3479). We attribute this difference to retention of the neck in resurfacing of the hip, leading to impingement-type edge loading. This was supported by visual evidence of impingement on the femur.

These findings show that failed metal-on-metal hip resurfacing and modular THRs have similar component wear rates and are both associated with raised pre-revision blood levels of metal ions.

Two Durasul highly crosslinked polyethylene liners were exchanged during revision surgery four and five years after implantation, respectively. The retrieved liners were evaluated macroscopically and surface analysis was performed using optical and electron microscopy. A sample of each liner was used to determine the oxidation of the material by Fourier transform infrared spectroscopy. Samples of the capsule were examined histologically.

The annual wear rate was found to be 0.010 and 0.015 mm/year, respectively. Surface analysis showed very little loss of material caused by wear. Histological evaluation revealed a continuous neosynovial lining with single multinucleated foreign-body giant cells. Our findings showed no unexpected patterns of wear on the articulating surfaces up to five years after implantation and no obvious failure of material.

We present the histological findings of an extensor mechanism allograft which was used in a total knee arthroplasty two years after implantation. Analysis of the graft was undertaken at four distinct anatomical levels and it was found to be incorporated into host tissue at each level. A wedge of fibrinoid necrosis, probably related to impingement of the graft on the tibial polyethylene insert, was seen. Impingement may play a role in the injury and necrosis of an allograft and may be one mode of failure in an extensor mechanism allograft.

We have examined 26 retrieved, failed titanium-alloy femoral stems. The clinical details, radiological appearances and the histology of the surrounding soft tissues in each patient were also investigated.

The stems were predominantly of the flanged design and had a characteristic pattern of wear. A review of the radiographs showed a series of changes, progressive with time. The first was lateral debonding with subsidence of the stem. This was followed by calcar resorption and fragmentation or fracture of the cement. Finally, osteolysis was seen, starting with a radiolucency at the cement-bone interface and progressing to endosteal cavitation.

Three histological appearances were noted: granulomatous, necrobiotic and necrotic. We suggest that an unknown factor, possibly related to the design of the stem, caused it to move early. After this, micromovement at the cement-stem interface led to the generation of particulate debris and fracture of the cement. A soft-tissue reaction to the debris resulted in osteolysis and failure of fixation of the prostheses.

The causes of mechanical failure of five noncemented porous-coated components were studied. There were two cobalt-chromium alloy and three titanium alloy implants which fractured after 12 to 48 months. The implants included one acetabular component, and one femoral condylar, one patellar and two tibial components. Examination of the fractured surfaces revealed fatigue to be the mechanism of failure in all cases. The porous coating and the processes required for its fabrication had resulted in weakening and reduction of substrate thickness. Additional factors were stress concentration due to limited, localised bone ingrowth, and some features of the design of the implants.

We recovered 23 meniscal bearings from 18 failed bicompartmental Oxford knee prostheses. They had been implanted for one to nine years. The minimum thickness of the retrieved bearings was measured and compared with the thickness of 25 unused bearings. The mean penetration rate, calculated by two methods, was either 0.043 or 0.026 mm per annum. This compares with 0.19 mm per annum reported for the Charnley hip. The use of a fully congruous meniscal bearing prosthesis can reduce wear in knee arthroplasty to a very low rate.

Aims. Oxidized zirconium (OxZi) and highly cross-linked polyethylene (HXLPE) were developed to minimize wear and risk of osteolysis in total hip arthroplasty (THA). However, retrieval studies have shown that scratched femoral heads may lead to runaway wear, and few reports of long-term results have been published. The purpose of this investigation is to report minimum ten-year wear rates and clinical outcomes of THA with OxZi femoral heads on HXLPE, and to compare them with a retrospective control group of cobalt chrome (CoCr) or ceramic heads on HXLPE. Methods. From 2003 to 2006, 108 THAs were performed on 96 patients using an OxZi head with a HXLPE liner with minimum ten-year follow-up. Harris Hip Scores (HHS) were collected preoperatively and at the most recent follow-up (mean 13.3 years). Linear and volumetric liner wear was measured on radiographs of 85 hips with a minimum ten-year follow-up (mean 14.5 years). This was compared to a retrospective control group of 45 THAs using ceramic or CoCr heads from October 1999 to February 2005, with a minimum of ten years’ follow-up. Results. Average HHS improved from 50.8 to 91.9 and 51.0 to 89.8 in the OxZi group and control group, respectively (p = 0.644), with no osteolysis in either group. Linear and volumetric wear rates in the OxZi group averaged 0.03 mm/year and 3.46 mm. 3. /year, respectively. There was no statistically significant difference in HHS scores, nor in linear or volumetric wear rate between the groups, and no revision for any indication. Conclusion. The radiological and clinical outcomes, and survivorship of THA with OxZi femoral heads and HXLPE liners, were excellent, and comparable to CoCr or ceramic heads at minimum ten-year follow-up. Wear rates are below what would be expected for development of osteolysis. OxZi-HXLPE is a durable bearing couple with excellent long-term outcomes. Cite this article: Bone Joint J 2024;106-B(3 Supple A):38–43

Aims. Wear of the polyethylene (PE) tibial insert of total knee arthroplasty (TKA) increases the risk of revision surgery with a significant cost burden on the healthcare system. This study quantifies wear performance of tibial inserts in a large and diverse series of retrieved TKAs to evaluate the effect of factors related to the patient, knee design, and bearing material on tibial insert wear performance. Methods. An institutional review board-approved retrieval archive was surveyed for modular PE tibial inserts over a range of in vivo duration (mean 58 months (0 to 290)). Five knee designs, totalling 1,585 devices, were studied. Insert wear was estimated from measured thickness change using a previously published method. Linear regression statistical analyses were used to test association of 12 patient and implant design variables with calculated wear rate. Results. Five patient-specific variables and seven implant-specific variables were evaluated for significant association with lower insert wear rate. Six were significant when controlling for other factors: greater patient age, female sex, shorter duration in vivo, polished tray, highly cross-linked PE (HXLPE), and constrained knee design. Conclusion. This study confirmed that knee wear rate increased with duration in vivo. Older patients and females had significantly lower wear rates. Polished modular tibial tray surfaces, HXLPE, and constrained TKA designs were device design factors associated with significantly reduced wear rate. Cite this article: Bone Joint J 2021;103-B(11):1695–1701

Aims. The aim of this study was to investigate whether wear and backside deformation of polyethylene (PE) tibial inserts may influence the cement cover of tibial trays of explanted total knee arthroplasties (TKAs). Methods. At our retrieval centre, we measured changes in the wear and deformation of PE inserts using coordinate measuring machines and light microscopy. The amount of cement cover on the backside of tibial trays was quantified as a percentage of the total surface. The study involved data from the explanted fixed-bearing components of four widely used contemporary designs of TKA (Attune, NexGen, Press Fit Condylar (PFC), and Triathlon), revised for any indication, and we compared them with components that used previous generations of PE. Regression modelling was used to identify variables related to the amount of cement cover on the retrieved trays. Results. A total of 114 explanted fixed-bearing TKAs were examined. This included 76 used with contemporary PE inserts which were compared with 15 used with older generation PEs. The Attune and NexGen (central locking) trays were found to have significantly less cement cover than Triathlon and PFC trays (peripheral locking group) (p = 0.001). The median planicity values of the PE inserts used with central locking trays were significantly greater than of those with peripheral locking inserts (205 vs 85 microns; p < 0.001). Attune and NexGen inserts had a characteristic pattern of backside deformation, with the outer edges of the PE deviating inferiorly, leaving the PE margins as the primary areas of articulation. Conclusion. Explanted TKAs with central locking mechanisms were significantly more likely to debond from the cement mantle. The PE inserts of these designs showed characteristic patterns of deformation, which appeared to relate to the manufacturing process and may be exacerbated in vivo. This pattern of deformation was associated with PE wear occurring at the outer edges of the articulation, potentially increasing the frictional torque generated at this interface. Cite this article: Bone Joint J 2021;103-B(12):1791–1801

Aims. The STRYDE nail is an evolution of the PRECICE Intramedullary Limb Lengthening System, with unique features regarding its composition. It is designed for load bearing throughout treatment in order to improve patient experience and outcomes and allow for simultaneous bilateral lower limb lengthening. The literature published to date is limited regarding outcomes and potential problems. We report on our early experience and raise awareness for the potential of adverse effects from this device. Methods. This is a retrospective review of prospective data collected on all patients treated in our institution using this implant. We report the demographics, nail accuracy, reliability, consolidation index, and cases where concerning clinical and radiological findings were encountered. There were 14 STRYDE nails implanted in nine patients (three male and six female) between June 2019 and September 2020. Mean age at surgery was 33 years (14 to 65). Five patients underwent bilateral lengthening (two femoral and three tibial) and four patients unilateral femoral lengthening for multiple aetiologies. Results. At the time of reporting, eight patients (13 implants) had completed lengthening. Osteolysis and periosteal reaction at the junction of the telescopic nail was evident in nine implants. Five patients experienced localized pain and swelling. Macroscopic appearances following retrieval were consistent with corrosion at the telescopic junction. Tissue histology was consistent with effects of focal metallic wear debris. Conclusion. From our early experience with this implant we have found the process of lengthening to be accurate and reliable with good regenerate formation and consolidation. Proposed advantages of early load bearing and the ability for bilateral lengthening are promising. We have, however, encountered concerning clinical and radiological findings in several patients. We have elected to discontinue its use to allow further investigation into the retrieved implants and patient outcomes from users internationally. Cite this article: Bone Joint J 2021;103-B(6):1168–1172

Aims. The aim of this study was to develop a novel computational model for estimating head/stem taper mechanics during different simulated assembly conditions. Methods. Finite element models of generic cobalt-chromium (CoCr) heads on a titanium stem taper were developed and driven using dynamic assembly loads collected from clinicians. To verify contact mechanics at the taper interface, comparisons of deformed microgroove characteristics (height and width of microgrooves) were made between model estimates with those measured from five retrieved implants. Additionally, these models were used to assess the role of assembly technique—one-hit versus three-hits—on the taper interlock mechanical behaviour. Results. The model compared well to deformed microgrooves from the retrieved implants, predicting changes in microgroove height (mean 1.1 μm (0.2 to 1.3)) and width (mean 7.5 μm (1.0 to 18.5)) within the range of measured changes in height (mean 1.4 μm (0.4 to 2.3); p = 0.109) and width (mean 12.0 μm (1.5 to 25.4); p = 0.470). Consistent with benchtop studies, our model found that increasing assembly load magnitude led to increased taper engagement, contact pressure, and permanent deformation of the stem taper microgrooves. Interestingly, our model found assemblies using three hits at low loads (4 kN) led to decreased taper engagement, contact pressures and microgroove deformations throughout the stem taper compared with tapers assembled with one hit at the same magnitude. Conclusion. These findings suggest additional assembly hits at low loads lead to inferior taper interlock strength compared with one firm hit, which may be influenced by loading rate or material strain hardening. These unique models can estimate microgroove deformations representative of real contact mechanics seen on retrievals, which will enable us to better understand how both surgeon assembly techniques and implant design affect taper interlock strength. Cite this article: Bone Joint J 2020;102-B(7 Supple B):33–40

Aims. The aim of this study was to conduct the largest low contact stress (LCS) retrieval study to elucidate the failure mechanisms of the Porocoat and Duofix femoral component. The latter design was voluntarily recalled by the manufacturer. Materials and Methods. Uncemented LCS explants were divided into three groups: Duofix, Porocoat, and mixed. Demographics, polyethylene wear, tissue ingrowth, and metallurgical analyses were performed. Results. In 104 implants, a decrease in the odds of loosening and an increase in metallosis and tissue staining in the Duofix group relative to Porocoat group was detected (p = 0.028). There was an increased presence of embedded metallic debris in the Duofix group (p < 0.001). Decreased tissue ingrowth was associated with the Duofix surface (p < 0.001). The attached beads had reduced microhardness, indicative of adverse thermal processing, which resulted in bead shedding, particulate debris, and metallosis. Conclusion. Hydroxyapatite coating of the LCS femoral component produced unexpected results and led to its recall. The root cause was likely a combination of retained alumina grit and a reduction in bead microhardness (mechanical strength) resulting in increased particle debris, metallosis, and early revision. The Duofix LCS femoral component was not equivalent to the Porocoat version despite its approval through the Food and Drug Administration (FDA) 510(k) equivalance approval process. Regulation of the introduction of modified existing devices needs to be improved and the Duofix LCS should have been considered to be a new device for which equivalence had not been demonstrated at the point of introduction. Cite this article: Bone Joint J 2019;101-B:1248–1255

Aims. We evaluated a large database with mechanical failure of a single uncemented modular femoral component, used in revision hip arthroplasty, as the end point and compared them to a control group treated with the same implant. Patient- and implant-specific risk factors for implant failure were analyzed. . Methods. All cases of a fractured uncemented modular revision femoral component from one manufacturer until April 2017 were identified and the total number of implants sold until April 2017 was used to calculate the fracture rate. The manufacturer provided data on patient demographics, time to failure, and implant details for all notified fractured devices. Patient- and implant-specific risk factors were evaluated using a logistic regression model with multiple imputations and compared to data from a previously published reference group, where no fractures had been observed. The results of a retrieval analysis of the fractured implants, performed by the manufacturer, were available for evaluation. Results. There were 113 recorded cases with fracture at the modular junction, resulting in a calculated fracture rate of 0.30% (113/37,600). The fracture rate of the implant without signs of improper use was 0.11% (41/37,600). In 79% (89/113) of cases with a failed implant, either a lateralized (high offset) neck segment, an extralong head, or the combination of both were used. Logistic regression analysis revealed male sex, high body mass index (BMI), straight component design, and small neck segments were significant risk factors for failure. Investigation of the implants (76/113) showed at least one sign of improper use in 72 cases. Conclusion. Implant failure at the modular junction is associated with patient- and implant-specific risk factors as well as technical errors during implantation. Whenever possible, the use of short and lateralized neck segments should be avoided with this revision system. Implantation instructions and contraindications need to be adhered to and respected. Cite this article: Bone Joint J 2020;102-B(5):573–579

Aims. The aim of this study was to evaluate fretting and corrosion in retrieved oxidized zirconium (OxZr; OXINIUM, Smith & Nephew, Memphis, Tennessee) femoral heads and compare the results with those from a matched cohort of cobalt-chromium (CoCr) femoral heads. Patients and Methods. A total of 28 OxZr femoral heads were retrieved during revision total hip arthroplasty (THA) and matched to 28 retrieved CoCr heads according to patient demographics. The mean age at index was 56 years (46 to 83) in the OxZr group and 70 years (46 to 92) in the CoCr group. Fretting and corrosion scores of the female taper of the heads were measured according to the modified Goldberg scoring method. Results. The OxZr-retrieved femoral heads showed significantly lower mean corrosion scores than the CoCr heads (1.3 (1 to 2.75) vs 2.1 (1 to 4); p < 0.01). Mean fretting scores were also significantly lower in the OxZr cohort when compared with the CoCr cohort (1.3 (1 to 2) vs 1.5 (1 to 2.25); p = 0.02). OxZr heads had more damage in the proximal region compared with the distal region of the head. Location had no impact on damage of CoCr heads. A trend towards increased corrosion in large heads was seen only in the CoCr heads, although this was not statistically significant. Conclusion. Retrieval analysis of OxZr femoral heads showed a decreased amount of fretting and corrosion compared with CoCr femoral heads. OxZr seems to be effective at reducing taper damage. Cite this article: Bone Joint J 2019;101-B:386–389

Aims. The aim of this study was to evaluate the surface damage, the density of crosslinking, and oxidation in retrieved antioxidant-stabilized highly crosslinked polyethylene (A-XLPE) tibial inserts from total knee arthroplasty (TKA), and to compare the results with a matched cohort of standard remelted highly crosslinked polyethylene (XLPE) inserts. Materials and Methods. A total of 19 A-XLPE tibial inserts were retrieved during revision TKA and matched to 18 retrieved XLPE inserts according to the demographics of the patients, with a mean length of implantation of 15 months (1 to 42). The percentage areas of PE damage on the articular surfaces and the modes of damage were measured. The density of crosslinking of the PE and oxidation were measured at loaded and unloaded regions on these surfaces. Results. A-XLPE inserts had higher rates of burnishing and lower rates of pitting and scratching compared with XLPE. There were no differences in the density of crosslinking at loaded and unloaded regions. A-XLPE showed higher oxidation indices in the unloaded surface region compared with XLPE. There were no differences in the levels of oxidation in the loaded regions. Conclusion. Retrieval analysis of A-XLPE did not reflect a clinically relevant difference in surface damage, density of crosslinking, or oxidation compared with XLPE tibial inserts at short-term evaluation. Cite this article: Bone Joint J 2018;100-B:1330–5

Aims. The management of completely displaced fractures of the distal radius in children remains controversial. This study evaluates the outcomes of surgical and non-surgical management of ‘off-ended’ fractures in children with at least two years of potential growth remaining. Methods. A total of 34 boys and 22 girls aged 0 to ten years with a closed, completely displaced metaphyseal distal radial fracture presented between 1 November 2015 and 1 January 2020. After 2018, children aged ten or under were offered treatment in a straight plaster or manipulation under anaesthesia with Kirschner (K-)wire stabilization. Case notes and radiographs were reviewed to evaluate outcomes. In all, 16 underwent treatment in a straight cast and 40 had manipulation under anaesthesia, including 37 stabilized with K-wires. Results. Of the children treated in a straight cast, all were discharged with good range of mo (ROM). Five children were discharged at six to 12 weeks with no functional limitations at six-month follow-up. A total of 11 children were discharged between 12 and 50 weeks with a normal ROM and radiological evidence of remodelling. One child had a subsequent diaphyseal fracture proximal to the original injury four years after the initial fracture. Re-displacement with angulation greater than 10° occurred for 17 children who had manipulation under anaesthesia. Four had a visible cosmetic deformity at discharge and nine had restriction of movement, with four requiring physiotherapy. One child developed over- granulation at the pin site and one wire became buried, resulting in a difficult retrieval in clinic. No children had pin site infections. Conclusion. Nonoperative management of completely displaced distal radial fractures in appropriately selected cases results in excellent outcomes without exposing the child to the risks of surgery. This study suggests that nonoperative management of these injuries is a viable and potentially underused strategy. Cite this article: Bone Joint J 2021;103-B(5):902–907

We present a case of early retrieval of an Oxinium femoral head and corresponding polyethylene liner where there was significant surface damage to the head and polyethylene. The implants were retrieved at the time of revision surgery to correct leg-length discrepancy just 48 hours after the primary hip replacement. Appropriate analysis of the retrieved femoral head demonstrated loss of the Oxinium layer with exposure of the underlying substrate and transfer of titanium from the acetabular shell at the time of a reduction of the index total hip replacement. In addition, the level of damage to the polyethylene was extensive despite only 48 hours in situ. The purpose of this report is to highlight the care that is required at the time of reduction, especially with these hard femoral counter-faces such as Oxinium. To our knowledge, the damage occurring at the time of reduction has not been previously reported following the retrieval of an otherwise well-functioning hip replacement

Aims. There are limited published data detailing the volumetric material loss from tapers of conventional metal-on-polyethylene (MoP) total hip arthroplasties (THAs). Our aim was to address this by comparing the taper wear rates measured in an explanted cohort of the widely used Exeter THA with those measured in a group of metal-on-metal (MoM) THAs. Patients and Methods. We examined an existing retrieval database to identify all Exeter V40 and Universal MoP THAs. Volumetric wear analysis of the taper surfaces was conducted using previously validated methodology. These values were compared with those obtained from a series of MoM THAs using non-parametric statistical methodology. A number of patient and device variables were accounted for using multiple regression modelling. Results. A total of 95 Exeter MoP and 249 MoM THAs were examined. The median volumetric loss from the MoM cohort was over four times larger than that from the MoP cohort (1.01 mm. 3. vs 0.23 mm. 3. , p < 0.001), despite a significantly shorter median period in vivo for the MoM group (48 months vs 90 months, p < 0.001). Multiple regression modelling indicated that the dominant variables leading to greater female taper material loss were bearing diameter (p < 0.001), larger female taper angles (p < 0.001), and male titanium stem tapers (p < 0.001). Conclusion. Consistent with the long-term clinical success of the device, the volumetric material loss from Exeter femoral head tapers was, in general, small compared with that from larger-diameter MoM head tapers. Cite this article: Bone Joint J 2018;100-B:1310–9

Aims. We sought to establish whether an oxidised zirconium (OxZr) femoral component causes less loss of polyethylene volume than a cobalt alloy (CoCr) femoral component in total knee arthroplasty. Materials and Methods. A total of 20 retrieved tibial inserts that had articulated with OxZr components were matched with 20 inserts from CoCr articulations for patient age, body mass index, length of implantation, and revision diagnosis. Changes in dimensions of the articular surfaces were compared with those of pristine inserts using laser scanning. The differences in volume between the retrieved and pristine surfaces of the two groups were calculated and compared. Results. The loss of polyethylene volume was 122 mm. 3. (standard deviation (. sd. ) 87) in the OxZr group and 170 mm. 3. (. sd. 96) in the CoCr group (p = 0.033). The volume loss in the OxZr group was also lower in the medial (72 mm. 3 . (. sd. 67) versus 92 mm. 3 . (. sd. 60); p = 0.096) and lateral (49 mm. 3 . (. sd. 36) versus 79 mm. 3 . (. sd. 61); p = 0.096) compartments separately, but these differences were not significant. Conclusion. Our results corroborate earlier findings from in vitro testing and visual retrieval analysis which suggest that polyethylene volume loss is lower with OxZr femoral components. Since both OxZr and CoCr are hard surfaces that would be expected to create comparable amounts of polyethylene creep, the differences in volume loss may reflect differences in the in vivo wear of these inserts. Cite this article: Bone Joint J 2017;99-B:793–8

Aims. We present a case series of five patients who had revision surgery following magnetic controlled growing rods (MGCR) for early onset scoliosis. Metallosis was found during revision in four out of five patients and we postulated a mechanism for rod failure based on retrieval analysis. Patients and Methods. Retrieval analysis was performed on the seven explanted rods. The mean duration of MCGR from implantation to revision was 35 months (17 to 46). The mean age at revision was 12 years (7 to 15; four boys, one girl). Results. A total of six out of seven rods had tissue metallosis and pseudo-capsule surrounding the actuator. A total of four out of seven rods were pistoning. There were two rods which were broken. All rods had abrasive circumferential markings. A significant amount of metal debris was found when the actuators were carefully cut open. Analytical electron microscopy demonstrated metal fragments of predominantly titanium with a mean particle size of 3.36 microns (1.31 to 6.61). Conclusion. This study highlights concerns with tissue metallosis in MCGR. We recommend careful follow-up of patients who have received this implant. Cite this article: Bone Joint J 2016;98-B:1662–7

Aims

The purpose of this study was to assess mid-term survivorship following primary total knee arthroplasty (TKA) with Optetrak Logic components and identify the most common revision indications at a single institution.

Aims. The National Joint Registry for England, Wales and Northern Ireland (NJR) has extended its scope to report on hospital, surgeon and implant performance. Data linkage of the NJR to the London Implant Retrieval Centre (LIRC) has previously evaluated data quality for hip primary procedures, but did not assess revision records. . Methods. We analysed metal-on-metal hip revision procedures performed between 2003 and 2013. A total of 69 929 revision procedures from the NJR and 929 revised pairs of components from the LIRC were included. Results. We were able to link 716 (77.1%) revision procedures on the NJR to the LIRC. This meant that 213 (22.9%) revision procedures at the LIRC could not be identified on the NJR. We found that 349 (37.6%) explants at the LIRC completed the full linkage process to both NJR primary and revision databases. Data completion was excellent (> 99.9%) for revision procedures reported to the NJR. Discussion. This study has shown that only approximately one third of retrieved components at the LIRC, contributed to survival curves on the NJR. We recommend prospective registry-retrieval linkage as a tool to feedback missing and erroneous data to the NJR and improve data quality. Take home message: Prospective Registry – retrieval linkage is a simple tool to evaluate and improve data quality on the NJR. Cite this article: Bone Joint J 2016;98-B:33–9

Aims

In metal-on-polyethylene (MoP) total hip arthroplasty (THA), large metal femoral heads have been used to increase stability and reduce the risk of dislocation. The increased size of the femoral head can, however, lead to increased taper corrosion, with the release of metal ions and adverse reactions. The aim of this study was to investigate the relationship between the size of the femoral head and the levels of metal ions in the blood in these patients.

Aims

The aim of this study was to perform a systematic review of the evidence for the use of intraoperative cell salvage in patients undergoing revision hip arthroplasty, and specifically to analyze the available data in order to quantify any associated reduction in the use of allogenic blood transfusion, and the volume which is used.

Aims

This multicentre retrospective observational study’s aims were to investigate whether there are differences in the occurrence of radiolucent lines (RLLs) following total knee arthroplasty (TKA) between the conventional Attune baseplate and its successor, the novel Attune S+, independent from other potentially influencing factors; and whether tibial baseplate design and presence of RLLs are associated with differing risk of revision.

Aims

Conflicting clinical results are reported for the ATTUNE Total Knee Arthroplasty (TKA). This randomized controlled trial (RCT) evaluated five-year follow-up results comparing cemented ATTUNE and PFC-Sigma cruciate retaining TKAs, analyzing component migration as measured by radiostereometric analysis (RSA), clinical outcomes, patient-reported outcome measures (PROMs), and radiological outcomes.

Aims

Loosening of components after total knee arthroplasty (TKA) can be associated with the development of radiolucent lines (RLLs). The aim of this study was to assess the rate of formation of RLLs in the cemented original design of the ATTUNE TKA and their relationship to loosening.

Displaced fractures of the distal radius in children are usually reduced under sedation or general anaesthesia to restore anatomical alignment before the limb is immobilized. However, there is growing evidence of the ability of the distal radius to remodel rapidly, raising doubts over the benefit to these children of restoring alignment. There is now clinical equipoise concerning whether or not young children with displaced distal radial fractures benefit from reduction, as they have the greatest ability to remodel. The Children’s Radius Acute Fracture Fixation Trial (CRAFFT), funded by the National Institute for Health and Care Research, aims to definitively answer this question and determine how best to manage severely displaced distal radial fractures in children aged up to ten years.

Cite this article: Bone Joint J 2024;106-B(1):16–18.

Telehealth has the potential to change the way we approach patient care. From virtual consenting to reducing carbon emissions, costs, and waiting times, it is a powerful tool in our clinical armamentarium. There is mounting evidence that remote diagnostic evaluation and decision-making have reached an acceptable level of accuracy and can safely be adopted in orthopaedic surgery. Furthermore, patients’ and surgeons’ satisfaction with virtual appointments are comparable to in-person consultations. Challenges to the widespread use of telehealth should, however, be acknowledged and include the cost of installation, training, maintenance, and accessibility. It is also vital that clinicians are conscious of the medicolegal and ethical considerations surrounding the medium and adhere strictly to the relevant data protection legislation and storage framework. It remains to be seen how organizations harness the full spectrum of the technology to facilitate effective patient care.

Cite this article: Bone Joint J 2023;105-B(8):843–849.

Aims

Vascular compromise due to arterial injury is a rare but serious complication of a proximal humeral fracture. The aims of this study were to report its incidence in a large urban population, and to identify clinical and radiological factors which are associated with this complication. We also evaluated the results of the use of our protocol for the management of these injuries.

We analysed 54 alumina ceramic-on-ceramic bearings from total hip replacements retrieved at one centre after a mean duration of 3.5 years (0.2 to 10.6) in situ. These implants were obtained from 54 patients (16 men and 38 women) with a mean age of 67 years (33 to 88) who underwent revision for a variety of reasons. Posterior edge loading was found in the majority of these retrievals (32 out of 54). Anterosuperior edge loading occurred less often but produced a higher rate of wear. Stripe wear on the femoral heads had a median volumetric wear rate of 0.2 mm. 3. /year (0 to 7.2). The wear volume on the femoral heads corresponded to the width of edge wear on the matching liner. Anteversion of the acetabular component was found to be a more important determinant than inclination for wear in ceramic bearings. Posterior edge loading may be considered to be a normal occurrence in ceramic-on-ceramic bearings, with minimal clinical consequences. Edge loading should be defined as either anterosuperior or posterior, as each edge loading mechanism may result in different clinical implications

Retrieval studies of total hip replacements with highly cross-linked ultra-high-molecular-weight polyethylene liners have shown much less surface damage than with conventional ultra-high-molecular-weight polyethylene liners. A recent revision hip replacement for recurrent dislocation undertaken after only five months revealed a highly cross-linked polyethylene liner with a large area of visible delamination. In order to determine the cause of this unusual surface damage, we analysed the bearing surfaces of the cobalt-chromium femoral head and the acetabular liner with scanning electron microscopy, energy dispersive x-ray spectroscopy and optical profilometry. We concluded that the cobalt-chromium modular femoral head had scraped against the titanium acetabular shell during the course of the dislocations and had not only roughened the surface of the femoral head but also transferred deposits of titanium onto it. The largest deposits were 1.6 μm to 4.3 μm proud of the surrounding surface and could lead to increased stresses in the acetabular liner and therefore cause accelerated wear and damage. This case illustrates that dislocations can leave titanium deposits on cobalt-chromium femoral heads and that highly cross-linked ultra-high-molecular-weight polyethylene remains susceptible to surface damage

We present a series of 35 patients (19 men and 16 women) with a mean age of 64 years (36.7 to 75.9), who underwent total hip replacement using the ESKA dual-modular short stem with metal on-polyethylene bearing surfaces. This implant has a modular neck section in addition to the modular head. Of these patients, three presented with increasing post-operative pain due to pseudotumour formation that resulted from corrosion at the modular neck-stem junction. These patients underwent further surgery and aseptic lymphocytic vaculitis associated lesions were demonstrated on histological analysis. Retrieval analysis of two modular necks showed corrosion at the neck-stem taper. Blood cobalt and chromium levels were measured at a mean of nine months (3 to 28) following surgery. These were compared with the levels in seven control patients (three men and four women) with a mean age of 53.4 years (32.1 to 64.1), who had an identical prosthesis and articulation but with a prosthesis that had no modularity at neck-stem junction. The mean blood levels of cobalt in the study group were raised at 50.75 nmol/l (5 to 145) compared with 5.6 nmol/l (2 to 13) in control patients. Corrosion at neck-stem tapers has been identified as an important source of metal ion release and pseudotumour formation requiring revision surgery. Finite element modelling of the dual modular stem demonstrated high stresses at the modular stem-neck junction. Dual modular cobalt-chrome hip prostheses should be used with caution due to these concerns

Post-mortem retrieval of canine, cemented femoral components was analysed to assess the performance of these implants in the dog as a model for human total hip replacement (THR). Mechanical testing and radiological analysis were performed to determine the stability of the implant and the quality of the cement. Thirty-eight implants from 29 dogs were retrieved after time intervals ranging from 0.67 to 11.67 years. The incidence of aseptic loosening was 63.2%, much higher than in human patients (6% in post-mortem studies). Failure of the femoral implants began with debonding at the cement-metal interface, similar to that in implants in man. The incidence of aseptic loosening was much lower in bilateral than in unilateral implants. Significant differences were observed for three different designs of implant. While the dog remains the animal model of choice for THR, results from this study provide insight into interspecies differences in the performance of implants. For example, the performance of THR in dogs should be compared with that in young rather than in elderly human patients

Aims

Head-taper corrosion is a cause of failure in total hip arthroplasty (THA). Recent reports have described an increasing number of V40 taper failures with adverse local tissue reaction (ALTR). However, the real incidence of V40 taper damage and its cause remain unknown. The aim of this study was to evaluate the long-term incidence of ALTR in a consecutive series of THAs using a V40 taper and identify potentially related factors.

Aims

This study reports the ten-year wear rates, incidence of osteolysis, clinical outcomes, and complications of a multicentre randomized controlled trial comparing oxidized zirconium (OxZr) versus cobalt-chrome (CoCr) femoral heads with ultra-high molecular weight polyethylene (UHMWPE) and highly cross-linked polyethylene (XLPE) liners in total hip arthroplasty (THA).

The Oxford Unicompartmental Knee replacement (UKR) was introduced as a design to reduce polyethylene wear. There has been one previous retrieval study involving this implant, which reported very low rates of wear in some specimens but abnormal patterns of wear in others. There has been no further investigation of these abnormal patterns. The bearings were retrieved from 47 patients who had received a medial Oxford UKR for anteromedial osteoarthritis of the knee. None had been studied previously. The mean time to revision was 8.4 years (. sd. 4.1), with 20 having been implanted for over ten years. The macroscopic pattern of polyethylene wear and the linear penetration were recorded for each bearing. The mean rate of linear penetration was 0.07 mm/year. The patterns of wear fell into three categories, each with a different rate of linear penetration; 1) no abnormal macroscopic wear and a normal articular surface, n = 16 (linear penetration rate = 0.01 mm/year); 2) abnormal macroscopic wear and normal articular surfaces with extra-articular impingement, n = 16 (linear penetration rate = 0.05 mm/year); 3) abnormal macroscopic wear and abnormal articular surfaces with intra-articular impingement +/− signs of non-congruous articulation, n = 15 (linear penetration rate = 0.12 mm/year). The differences in linear penetration rate were statistically significant (p < 0.001). These results show that very low rates of polyethylene wear are possible if the device functions normally. However, if the bearing displays suboptimal function (extra-articular, intra-articular impingement or incongruous articulation) the rates of wear increase significantly

Allografts of bone from the femoral head are often used in orthopaedic procedures. Although the donated heads are thoroughly tested microscopically before release by the bone bank, some surgeons take additional cultures in the operating theatre before implantation. There is no consensus about the need to take these cultures. We retrospectively assessed the clinical significance of the implantation of positive-cultured bone allografts. The contamination rate at retrieval of the allografts was 6.4% in our bone bank. Intra-operative cultures were taken from 426 femoral head allografts before implantation; 48 (11.3%) had a positive culture. The most frequently encountered micro-organism was coagulase-negative staphylococcus. Deep infection occurred in two of the 48 patients (4.2%). In only one was it likely that the same micro-organism caused the contamination and the subsequent infection. In our study, the rate of infection in patients receiving positive-cultured allografts at implantation was not higher than the overall rate of infection in allograft surgery suggesting that the positive cultures at implantation probably represent contamination and that the taking of additional cultures is not useful

Aims

This study compared the cobalt and chromium serum ion concentration of patients treated with two different metal-on-metal (MoM) hinged total knee arthroplasty (TKA) systems, as well as a titanium nitride (TiN)-coated variant.

Aims

The aim of this study was to evaluate the incidence of liner malseating in two commonly used dual-mobility (DM) designs. Secondary aims included determining the risk of dislocation, survival, and clinical outcomes.

Aims

Limb-lengthening nails have largely replaced external fixation in limb-lengthening and reconstructive surgery. However, the adverse events and high prevalence of radiological changes recently noted with the STRYDE lengthening nail have raised concerns about the use of internal lengthening nails. The aim of this study was to compare the prevalence of radiological bone abnormalities between STRYDE, PRECICE, and FITBONE nails prior to nail removal.

Early failure associated with adverse reactions to metal debris is an emerging problem after hip resurfacing but the exact mechanism is unclear. We analysed our entire series of 660 metal-on-metal resurfacings (Articular Surface Replacement (ASR) and Birmingham Hip Resurfacing (BHR)) and large-bearing ASR total hip replacements, to establish associations with metal debris-related failures. Clinical and radiological outcomes, metal ion levels, explant studies and lymphocyte transformation tests were performed. A total of 17 patients (3.4%) were identified (all ASR bearings) with adverse reactions to metal debris, for which revision was required. This group had significantly smaller components, significantly higher acetabular component anteversion, and significantly higher whole concentrations of blood and joint chromium and cobalt ions than asymptomatic patients did (all p < 0.001). Post-revision lymphocyte transformation tests on this group showed no reactivity to chromium or cobalt ions. Explants from these revisions had greater surface wear than retrievals for uncomplicated fractures. The absence of adverse reactions to metal debris in patients with well-positioned implants usually implies high component wear. Surgeons must consider implant design, expected component size and acetabular component positioning in order to reduce early failures when performing large-bearing metal-on-metal hip resurfacing and replacement

Aims

Dual mobility implants in total hip arthroplasty are designed to increase the functional head size, thus decreasing the potential for dislocation. Modular dual mobility (MDM) implants incorporate a metal liner (e.g. cobalt-chromium alloy) in a metal shell (e.g. titanium alloy), raising concern for mechanically assisted crevice corrosion at the modular liner-shell connection. We sought to examine fretting and corrosion on MDM liners, to analyze the corrosion products, and to examine histologically the periprosthetic tissues.