The aims of this study were to evaluate wear on the surface of cobalt-chromium (CoCr) femoral components used in total knee arthroplasty (TKA) and compare the wear of these components with that of ceramic femoral components. Optical profilometry was used to evaluate surface roughness and to examine the features created by the wear process in a knee wear simulator. We developed a method of measuring surface changes on five CoCr femoral components and quantifying the loss of material from the articular surface during the wear process. We also examined the articular surface of three ceramic femoral components from a previous test for evidence of surface damage, and compared it with that of CoCr components.Aims
Methods
Total knee arthroplasty (TKA) femoral components are known to wear and roughen with clinical use, and reaction to metal is a well-documented complication of TKA. Ceramic materials are resistant to wear and corrosion, but the surface wear of ceramic femoral components in TKA has not been reported. This study measured the changes in roughness and mass lost from cobalt-chromium (CoCr) femoral components tested in a knee simulator, and compared them to those observed in ceramic components. Six cast CoCr femoral components were tested in a knee simulator bearing against UHMWPE, with high-kinematics/high-load waveforms. Roughness and scratches were measured via optical profilometry. Scratch volume was equated to mass lost from abrasive wear, while nano-particulate wear and corrosion were estimated from the change in the distance of the surface to the depth of the scratches after increasing numbers of cycles. Three magnesia-stabilized zirconia femoral components that had been wear tested to 15 million cycles were compared with the CoCr components.Introduction
Methods