Corrosion and fretting damage at the head-neck interface of artificial hip joints is more severe with larger head sizes. This is a concern, as the release of metal particles and ions can cause adverse tissue reactions, similar to those observed high wear metal-on-metal articulations. In the last few years corrosion was increasingly observed at head-neck interfaces of artificial hip joints, especially in joints with larger heads. There has always been evidence of some corrosion at modular junctions of artificial joints, but except for few designs, it was not seen as a real problem. It is important to better understand the factors contributing to corrosion at modular interfaces, so that necessary improvements can be made to minimise or completely avoid corrosion, in order to avoid possible adverse tissue reactions.Summary
Introduction