Orthopaedic Proceedings
Vol. 105-B, Issue SUPP_3 | Pages 85 - 85
23 Feb 2023
Flynn S Lemoine M Boland F O'Brien F O'Byrne J
Full Access

Restoration a joint's articular surface following degenerative or traumatic pathology to the osteochondral unit pose a significant challenge. Recent advances have shown the utility of collagen-based scaffolds in the regeneration of osteochondral tissue. To provide these collagen scaffolds with the appropriate superstructure novel techniques in 3D printing have been investigated. This study investigates the use of polyɛ-caprolactone (PCL) collagen scaffolds in a porcine cadaveric model to establish the stability of the biomaterial once implanted.

This study was performed in a porcine cadaveric knee model. 8mm defects were created in the medial femoral trochlea and repaired with a PCL collagen scaffold. Scaffolds were secured by one of three designs; Press Fit (PF), Press Fit with Rings (PFR), Press Fit with Fibrin Glue (PFFG). Mobilisation was simulated by mounting the pig legs on a continuous passive motion (CPM) machine for either 50 or 500 cycles. Biomechanical tensile testing was performed to examine the force required to displace the scaffold.

18 legs were used (6 PF, 6 PFR, 6 PFFG). Fixation remained intact in 17 of the cohort (94%). None of the PF or PFFG scaffolds displaced after CPM cycling. Mean peak forces required to displace the scaffold were highest in the PFFG group (3.173 Newtons, Standard deviation = 1.392N). The lowest peak forces were observed in the PFR group (0.871N, SD = 0.412N), while mean peak force observed in the PF group was 2.436N (SD = 0.768). There was a significant difference between PFFG and PFR (p = 0.005). There was no statistical significance in the relationship between the other groups.

PCL reinforcement of collagen scaffolds provide an innovative solution for improving stiffness of the construct, allowing easier handling for the surgeon. Increasing the stiffness of the scaffold also allows press fit solutions for reliable fixation. Press fit PCL collagen scaffolds with and without fibrin glue provide dependable stability. Tensile testing provides an objective analysis of scaffold fixation. Further investigation of PCL collagen scaffolds in a live animal model to establish quality of osteochondral tissue regeneration are required.


Orthopaedic Proceedings
Vol. 100-B, Issue SUPP_15 | Pages 112 - 112
1 Nov 2018
Lemoine M O'Byrne J Kelly DJ O'Brien FJ
Full Access

Damage to articular cartilage is difficult to treat, as it has a low capacity to regenerate. Biomimetic natural polymer scaffolds can potentially be used to regenerate cartilage. Collagen hyaluronic acid (CHyA) scaffolds have been developed in our laboratory to promote cell infiltration and repair of articular cartilage. However, the low mechanical properties of such scaffolds potentially limit their use to the treatment of small cartilage defects. 3D-printed polymers can provide a reinforcing framework in these scaffolds, thus allowing their application in the treatment of larger defects. The aim of this study was to create mechanically functional biomaterial scaffolds by incorporating a CHyA matrix into 3D-printed polymer meshes resulting in an integrated porous material composite with improved mechanical properties for repair of large cartilage defects. 3D-printed meshes were developed to facilitate an architecture suitable for nutrient flow, cell infiltration, and even CHyA incorporation. And the meshes were freeze dried in custom made moulds to create a pore structure suitable for chondrogenesis. Uniaxial compressive testing of the scaffolds revealed improved mechanical properties following reinforcement with printed meshes, with the compressive modulus increasing from 0.8kPa (alone) to 0.5MPa (reinforced structure). The reinforced scaffolds maintained interconnected pores with the mean pore diameter increasing from 130 to 175µm. The reinforcement had no negative impact on MSC viability, with 90.1% viability in reinforced scaffolds at day 7. The compressive modulus of the reinforced CHyA scaffold is close to native articular cartilage, suggesting that this approach can be used for treatment of large cartilage defects.