Introduction

Histology is still considered the gold standard method for the evaluation of soft tissues in the musculoskeletal field, thanks to the possibility of studying structures using different staining and high magnification microscopy. To overcome the intrinsic limits of this method, contrast enhanced microtomographic (CE- microCT) protocols are constantly evolving to allow 3D study of soft tissues. However, no standardized approaches are available, and many concerns exist about the alterations induced to the samples.

The use of implant biomaterials for prosthetic reconstructive surgery and osteosynthesis is consolidated in the orthopaedic field, improving the quality of life of patients and allowing for healthy and better ageing. However, there is the lack of advanced innovative methods to investigate the potentialities of smart biomaterials, particularly for the study of local effects of implant and osteointegration. Despite the complex process of osseointegration is difficult to recreate in vitro, the growing challenges in developing alternative models require to set-up and validate new approaches. Aim of the present study is to evaluate an advanced in vitro tissue culture model of osteointegration of titanium implants in human trabecular bone. Cubic samples (1.5×1.5 cm) of trabecular bone were harvested as waste material from hip arthroplasty surgery (CE AVEC 829/2019/Sper/IOR); cylindrical defects (2 mm Ø, 6 mm length) were created, and tissue specimens assigned to the following groups: 1) empty defects- CTR-; 2) defects implanted with a cytotoxic copper pin (Merck cod. 326429)- CTR+; 3) defects implanted with standard titanium pins of 6 µm-rough (ZARE S.r.l) -Ti6. Tissue specimens were cultured in mini rotating bioreactors in standard conditions, weekly assessing viability. At the 8-week-timepoint, immunoenzymatic, microtomographic, histological and histomorphometric analyses were performed. The model was able to simulate the effects of implantation of the materials, showing a drop in viability in CTR+, differently from Ti6 which appears to have a trophic effect on the bone. MicroCT and histological analysis supported the results, with lower BV/TV and Tb.Th values observed in CTR- compared to CTR+ and Ti6 and signs of matrix and bone deposition at the implant site. The collected data suggest the reliability of the tested model which can recreate the osseointegration process in vitro and can therefore be used for preliminary evaluations to reduce and refine in vivo preclinical models.

Acknowledgment: This work was supported by Emilia-Romagna Region for the project “Sviluppo di modelli biologici in vitro ed in silico per la valutazione e predizione dell'osteointegrazione di dispositivi medici da impianto nel tessuto osseo”

Osteoarthritis (OA), the most common chronic degenerative joint disease, is characterized by inflammation, degradation of the articular cartilage and subchondral bone lesions, causing pain and decreased functionality.

NF-κB pathway is involved in OA and, in most cases, its activation depends on the phosphorylation and degradation of IκBα, the NF-κB endogenous inhibitor that sequesters NF-κB in the cytosol. Under inflammatory stimuli, IκBα is degraded by the IKK signalosome and NF-κB moves into the nucleus, inducing the transcription of inflammatory mediator genes and catabolic enzymes. The IKK signalosome includes IKKβ and IKKα kinases, the latter shown to be pivotal in the OA extracellular matrix derangement. The current OA therapies are not curative and nowadays, the preclinical research is evaluating new structure-modifying pharmacological treatments, able to prevent or delay cartilage degradation.

N-acetyl phenylalanine derivative (NAPA), is a derivative of glucosamine, a constituent of the glycosaminoglycans of cartilage and a chondroprotective agent. Previous in vitro studies showed the ability of NAPA to increase cartilage components and to reduce inflammatory cytokines, inhibiting IKKα kinase activity and its nuclear migration.

The present study aims to further clarify the effect of NAPA in counteracting OA progression, in an in vivo mouse model after destabilization of the medial meniscus (DMM).

Mice were divided into 3 groups:

-

DMM group: DMM surgery without NAPA;

DMM surgery was performed in the right knee, according to Glasson SS [2], while the left knee did not undergo any surgery. Four weeks after surgery (mild-to-moderate OA), some animals received one intra-articular injection of NAPA (2.5 mM) and after 2 weeks, the animals were pharmacologically euthanized. The mice of the 1^st group were euthanized 4 weeks after DMM and those of the 3^rd group after 6 weeks from their arrival in the animal facility. At the end of experimental times, both knee joints of the animals were analyzed through histology, histomorphometry, immunohistochemistry and subchondral bone microhardness.

The injection of NAPA significantly improved cartilage structure, increased cartilage thickness (p<0.0005), reduced Chambers and Mankin scores (p<0.005), fibrillation index (p<0.005) and decreased MMP13 (p<0.05) and ADAMTS5, MMP10, and IKKα (p<0.0005) staining. The microhardness measurements did not shown statistically significant differences between groups.

This study demonstrated the chondroprotective activities exerted by NAPA in vivo. NAPA markedly improved the physical structure of articular cartilage and reduced the amount of catabolic enzymes, and therefore of extracellular matrix remodeling. The reduction in OA grading and catabolic enzymes paralleled the reduction of IKKα expression. This further hints at a pivotal role of IKKα in OA development by regulating MMP activity through the control of procollagenase (MMP10) expression. We believe that the preliminary preclinical data, here presented, contribute to improve the knowledge on the development of disease modifying drugs since we showed the ability of NAPA of reverting the surgically induced OA in the widely accepted DMM model.

A critical bone defect may be more frequently the consequence of a trauma, especially when a fracture occurs with wide exposure, but also of an infection, of a neoplasm or congenital deformities. This defect needs to be treated in order to restore the limb function. The treatments most commonly performed are represented by implantation of autologous or homologous bone, vascularized fibular grafting with autologous or use of external fixators; all these treatments are characterized by several limitations.

Nowadays bone tissue engineering is looking forward new solutions: magnetic scaffolds have recently attracted significant attention. These scaffolds can improve bone formation by acting as a “fixed station” able to accumulate/release targeted growth factors and other soluble mediators in the defect area under the influence of an external magnetic field. Further, magnetic scaffolds are envisaged to improve implant fixation when compared to not-magnetic implants.

We performed a series of experimental studies to evaluate bone regeneration in rabbit femoral condyle defect by implanting hydroxyapatite (HA), polycaprolactone (PCL) and collagen/HA hybrid scaffolds in combination with permanent magnets.

Our results showed that ostetoconductive properties of the scaffolds are well preserved despite the presence of a magnetic component. Interestingly, we noticed that, using bio-resorbable collagen/HA magnetic scaffolds, under the effect of the static magnetic field generated by the permanent magnet, the reorganization of the magnetized collagen fibers produces a highly-peculiar bone pattern, with highly-interconnected trabeculae orthogonally oriented with respect to the magnetic field lines. Only partial healing of the defect was seen within the not magnetic control groups.

Magnetic scaffolds developed open new perspectives on the possibility to exploiting magnetic forces to improve implant fixation, stimulate bone formation and control the bone morphology of regenerated bone by synergically combining static magnetic fields and magnetized biomaterials. Moreover magnetic forces can be exploited to guide targeted drug delivery of growth factors functionalized with nanoparticles.

Spinal fusion is one of the most common surgical procedures in spine surgery, whose primary objective is the stabilization of the spine for the treatment of many degenerative, traumatic and oncological diseases of the spine. Autologous bone is still considered the “gold standard” technique for spinal fusion. However, biomaterials which are potentially osteogenic, osteoinductive and osteoconductive can be used to increase the process of spinal fusion. We evaluated two new bone substitutes as an alternative to autologous bone for spinal fusion, using an animal model of large size (adult sheep).

A preclinical study was designed to compare the efficacy of SINTlife® Putty and DBSINT® biomaterials with conventional bone autograft in an ovine model of lumbar spine fusion. SINTlife® is a biomaterial made from hydroxyapatite enriched with magnesium ions, resulting to be very similar to natural bone. DBSint® is a paste composite bone, osteo-inductive, pliable and conformable, consisting of demineralized bone matrix (DBM) carried by hydroxyapatite biomimetics. Eighteen adult female sheep were selected for two-levels spine surgical procedures. The animals were divided in two groups: in Group A, one fusion level was treated with SINTlife® Putty and the other level received cortical-cancellous bone autograft; in Group B, one fusion level was treated with DBSINT® and the other level received cortical-cancellous bone autograft. At the end of the experimental time, all the animals were euthanized. The spine segments were analyzed macroscopically, radiographically, microtomographically, histologically and histomorphometrically.

The SINT-Life® Putty shows a perfect osteointegration in all the histological specimens. A high percentage of newly formed bone tissue is detected, with lots of trabeculae having structure and morphology similar to the pre-existing bone. In all the specimens collected from DBSINT®-treated animals the presence of hydroxyapatite alone is reported but not the demineralized bone matrix. The presence of newly formed bone tissue can be detected in all the specimens but newly formed bone shows very thin and irregular trabeculae next to the cartilage zone, while away from the border of ossification there are thicker trabeculae similar to the pre-existing bone.

The use of the experimental biomaterial SINT-Life® Putty in an ovine model of spine fusion leads to the development of newly formed bone tissue without qualitative and quantitative differences with the one formed with autologous bone. The experimental material DBSINT® seems to lead to less deposition of newly formed bone with wider intertrabecular spaces. Following these results, we planned and submitted to the Ethical Committee a clinical study to evaluate the safety and efficacy of SINT-Life® product in comparison to autologous bone, as an alternative treatment for spine fusion procedures.

Summary Statement

An Implant Disposable Antibacterial Coating (i-DAC®) is described, consisting of a fully resorbable, biocompatible hydrogel, able to release antibacterial and antibiofilm agents. Direct application of the hydrogel on implants prevented infection occurrence in an in vitro model of peri-prosthetic infection.

We investigated the effect of stimulation with a pulsed electromagnetic field on the osseointegration of hydroxyapatite in cortical bone in rabbits. Implants were inserted into femoral cortical bone and were stimulated for six hours per day for three weeks.

Electromagnetic stimulation improved osseointegration of hydroxyapatite compared with animals which did not receive this treatment in terms of direct contact with the bone, the maturity of the bone and mechanical fixation. The highest values of maximum push-out force (F_max) and ultimate shear strength (σ_u) were observed in the treated group and differed significantly from those of the control group at three weeks (F_max; p < 0.0001; σ_u, p < 0.0005).

Aim: This study wants to investigate whether the administration of stromal stem cells (SSC) in a platelet-rich plasma (PRP) scaffold could promote angiogenesis which resulted in a better allograft integration.

Methods: surgery: A monolateral resection of 3cm segment of the metatarsus, was perfomed in 10 adult cross-breed sheep (3–4 years old), weighting 60–70 kg.

Isolation and ex-vivo expansion of SSC: nucleated cells were isolated with density gradient and expanded ex-vivo with alpha-MEM containing 20% FCS.

Radiographic and histomorphometric analysis: Radiographs were made after surgery and after 1, 2 and 4 months. Histomorphometric studies were carried out to study the defect and the new bone formation at the implant site

Results: Union had occurred in all the 5 animals of the SSC group after 4 months as observed radiographically and morphologically, while in the control group the osteotomy line was still visible. Histomorphometric analysis demonstrated a higher % of new-bone formation in both the host (%section quadrant) and the grafted bone in SSC animals.

Conclusions: Results presented suggest that SSC in PRP-based scaffold have improved allograft integration. In conclusion the application of this surgical approach may result in an increased and accelerated bone graft integration, reducing the time required for bone healing and increasing the chances of a successful bone implant.

Aims:. To test the effect of different surface roughness and fluorohydroxyapatite (FHA) coating on osteoblast-like cell (MG63) viability, proliferation, differentiation and synthetic activity, then to compare the various surfaces tested and try to identify an osteoblast parameter that can better explain the different behaviour of the tested surfaces observed in previous in vivo studies.

Methods: The tested materials were made of Ti6Al4V coated with Ti and with Ti plus FHA with different roughness; they can be divided into four groups: low roughness (LR; Ra: 5.9 B5m), low roughness plus FHA coating (LR+FHA; Ra: 5.6 B5m), high roughness (HR; Ra: 22.5 B5m), high roughness plus FHA coating (HR+FHA; Ra: 21.2 B5m). MG63 were cultivated on 6 samples of each group and on polystyrene as control; after 72 hours the proliferation assay (WST-1) was done, alkaline phosphatase activity (ALP) was determined and the synthesis of osteocalcin (OC), type 1 collagen (CICP), transforming growth factor α 1 (TGF-A71), interleukin-6 (IL-6) and tumor necrosis factor-α (TNF-a) were measured. Samples of each material were randomly processed for analysis with a scanning electron microscope (SEM).

Results: Cells proliferated on biomaterials more slowly than in the control group (p < 0.0001), the proliferation rate was higher on FHA-coated LR than uncoated HR (p = 0.037). CICP production was positively affected by the LR surface (p = 0.001) as compared to controls, while it was significantly lower (p = 0.0001) in the HR surfaces. Compared to controls, LR and HR surfaces led to enhanced production of TGF-A71, further improved by FHA (FHA-coated LR: p = 0.007; FHA-coated HR p < 0.0001 respectively). ALP, OC, IL-6 levels were not significantly different from the controls

Conclusions: Results suggest that CICP production could be useful in predicting the in vivo osteointegration rate of biocompatible biomaterials observed in previous studies.

When investigating orthopaedic biomaterials and tissue engineered devices, biological investigations by means of in vitro and in vivo tests are mandatory to obtain a overall picture of biocompatibility and therapeutic efficacy. However, various aspects requiring careful consideration should be kept in mind and can explain the complex situations encountered by researchers when the skeletal tissue is involved. This presentation aimed to summarize some useful information in improving in vivo methodology to test present and future therapies for orthopaedic surgery. Some in vivo biological tests to study innovative reconstructive surgical techniques are summarized on the basis of the experience of the Experimental Surgery Department –IOR.

After in vitro and in vivo biocompatibility tests, for the study of bone defect healing and of biomaterial osteo-inductive properties the subcutaneous and intramuscular implants are usually performed in laboratory animals while osteoconduction and bone healing evaluation require the development of “nonunions” (sites that never achieve functional bone continuity) and “critical size defects” (the smallest defect that will heal with less than 10% bony growth) models. Biomaterial osteointegration properties are investigated by means of metaphyseal, diaphyseal and intramedullary implantation. The use of pathological animals is also recommended to take into account the clinical situation where biomaterials are often implanted in aged and osteoporotic patients. As far as articular cartilage pathology is concerned, chondral and osteochondral “critical size defects” may be performed and the development of osteoarthritic animals could be also useful.

At different experimental times post-explantation evaluations by means of radiology, histology, histomorphometry and biomechanics provide a complete characterization of biomaterials and biotechnologies showing their potential therapeutic efficacy for skeletal reconstruction.

In vivo studies provide important pre-clinical information on new biomaterials and biotechnologies for the skeletal reconstruction Among the factors that are increasingly improving the reliability of in vivo testing are the continuous improvement in knowledge on bone biology and comparative science between humans and animals, the awareness that animal suffering should be reduced as much as possible, and, finally, the amount and the accuracy of in vivo post-explantation findings.

We implanted nails made of titanium (Ti6Al4V) and of two types of glass ceramic material (RKKP and AP40) into healthy and osteopenic rats. After two months, a histomorphometric analysis was performed and the affinity index calculated. In addition, osteoblasts from normal and osteopenic bone were cultured and the biomaterials were evaluated in vitro.

In normal bone the rate of osseointegration was similar for all materials tested (p > 0.5) while in osteopenic bone AP40 did not osseointegrate (p > 0.0005).

In vitro, no differences were observed for all biomaterials when cultured in normal bone-derived cells whereas in osteopenic-bone-derived cells there was a significant difference in some of the tested parameters when using AP40.

Our findings suggest that osteopenic models may be used in vivo in the preclinical evaluation of orthopaedic biomaterials. We suggest that primary cell cultures from pathological models could be used as an experimental model in vitro.