Background and aim. Recent proposals have been introduced to modify stem design and/or femoral fixation in total hip replacement (THR). New designs need to consider previous design features and their results. The aim of this study has been to evaluate the clinical and radiological results of six different designs of tapered uncemented stems implanted in our Institution. Methods. 1918 uncemented hips were prospectively assessed from 1999 to 2011 (minimum follow-up of five years for the unrevised hips). All hips had a 28 or 32 mm femoral head and metal-on-polyethylene or alumina-on-alumina bearing surface. Six uncemented femoral designs that shared a femoral tapered stem incorporating a coating surface were included in the study. The different design features included the type of coating, metaphyseal filling, and sectional shape. Results. Intra-operative proximal femoral crack was 6.7% in one of the designs (p=0.01), univariate analysis showing a lower risk of crack in the other designs. The position of the stem was neutral in 80% of the cases for all designs. Femoral canal filing was related to the stem design (p<0.001 at the three levels) and to the femoral level assessed (subset alpha=0.005). Twelve stems were revised for aseptic loosening (6 from two different designs). The survival rate for femoral aseptic loosening at 15 years was 96.6% (95% CI 93.8 to 99.4) for one of these two designs ad 97.4% (95% CI95.5 to 99.6) for the other. Regression analysis showed that stem design was the only factor related to aseptic loosening when adjusted for femoral canal filling (at the three levels) stem position (neutral or not) and femoral type (cylindrical or not). Conclusion. Tapered uncemented stems consistently provide excellent bone fixation. New designs need to avoid changing successful features and concentrate on the less successful aspects

Intraoperative fractures although rare are one of the complications known to occur while performing a total hip arthroplasty (THA). However, due to lower incidence rates there is currently a gap in this area of literature that systematically reviews this important issue of complications associated with THA. Method: We looked into Electronic databases including PubMed, Cochrane Central Register of Controlled Trials (CENTRAL), the archives of meetings of orthopaedic associations and the bibliographies of included articles and asked experts to identify prospective studies, published in any language that evaluated intra-operative fractures occurring during total hip arthroplasty from the year 1950-2020. The screening, data extraction and quality assessment were carried out by two researchers and if there was any discrepancy, a third reviewer was involved. Fourteen studies were identified. The reported range of occurrence of fracture while performing hip replacement surgery was found to be 0.4-7.6%. Major risk factors identified were surgical approaches, Elderly age, less Metaphyseal-Diaphyseal Index score, change in resistance while insertion of the femur implants, inexperienced surgeons, uncemented femoral components, use of monoblock elliptical components, implantation of the acetabular components, patients with ankylosing spondylitis, female gender, uncemented stems in patients with abnormal proximal femoral anatomy and with cortices, different stem designs, heterogeneous fracture patterns and toothed design. Intraoperative fractures during THA were managed with cerclage wire, femoral revision, intramedullary nail and cerclage wires, use of internal fixation plates and screws for management of intra operative femur and acetabular fractures. The main reason for intraoperative fracture was found to be usage of cementless implants but planning and timely recognition of risk factors and evaluating them is important in management of intraoperative fractures. Adequate surgical site exposure is critical especially during dislocation of hip, reaming of acetabulum, impaction of implant and preparing the femoral canal for stem insertion. Eccentric and increased reaming of acetabulum to accommodate a larger cup is to be avoided, especially in females and elderly patients as the acetabulum is thinner. However, this area requires more research in order to obtain more evidence on effectiveness, safety and management of intraoperative fractures during THA

Our aim was to determine the precision of the measurements of bone mineral density (BMD) by dual-energy x-ray absorptiometry in the proximal femur before and after implantation of an uncemented implant, with particular regard to the significance of retro- and prospective studies. We examined 60 patients to determine the difference in preoperative BMD between osteoarthritic and healthy hips. The results showed a preoperative BMD of the affected hip which was lower by a mean of 4% and by a maximum of 9% compared with the opposite side. In addition, measurements were made in the operated hip before and at ten days after operation to determine the effect of the implantation of an uncemented custom-made femoral stem. The mean increase in the BMD was 8% and the maximum was 24%. Previous retrospective studies have reported a marked loss of BMD on the operated side. The precision of double measurements using a special foot jig showed a modified coefficient of variation of 0.6% for the non-operated side in 15 patients and of 0.6% for the operated femur in 20 patients. The effect of rotation on the precision of the measurements after implantation of an uncemented femoral stem was determined in ten explanted femora and for the operated side in ten patients at 10° rotation and in 20 patients at 30° rotation. Rotation within 30° influenced the precision in studies in vivo and in vitro by a mean of 3% and in single cases in up to 60%. Precise prediction of the degree of loss of BMD is thus only possible in prospective cross-sectional measurements, since the effect of the difference in preoperative BMD, as well as the apparent increase in BMD after implantation of an uncemented stem, is not known from retrospective studies. The DEXA method is a reliable procedure for determining periprosthetic BMD when positioning and rotation are strictly controlled

We have compared the changes in the pattern of the principal strains in the proximal femur after insertion of eight uncemented anatomical stems and eight customised stems in human cadaver femora. During testing we aimed to reproduce the physiological loads on the proximal femur and to simulate single-leg stance and stair-climbing. The strains in the intact femora were measured and there were no significant differences in principal tensile and compressive strains in the left and right femora of each pair. The two types of femoral stem were then inserted randomly into the left or right femora and the cortical strains were again measured. Both induced significant stress shielding in the proximal part of the metaphysis, but the deviation from the physiological strains was most pronounced after insertion of the anatomical stems. The principal compressive strain at the calcar was reduced by 90% for the anatomical stems and 67% for the customised stems. Medially, at the level of the lesser trochanter, the corresponding figures were 59% and 21%. The anatomical stems induced more stress concentration on the anterior aspect of the femur than did the customised stems. They also increased the hoop strains in the proximomedial femur. Our study shows a consistently more physiological pattern of strain in the proximal femur after insertion of customised stems compared with standard, anatomical stems

Summary. Particulate wear debris with different chemical composition induced similar periprosthetic tissue reactions in patients with loosened uncemented and cemented titanium hip implants, which suggests that osteolysis can develop independent of particle composition. Introduction. Periprosthetic osteolysis is a serious long-term complication in total hip replacements (THR). Wear debris-induced inflammation is thought to be the main cause for periprosthetic bone loss and implant loosening. The aim of the present study was to compare the tissue reactions and wear debris characteristics in periprosthetic tissues from patients with failed uncemented (UC) and cemented (C) titanium alloy hip prostheses. We hypothesised that implant wear products around two different hip designs induced periprosthetic inflammation leading to osteolysis. Patients & Methods. Thirty THR-patients undergoing revision surgery were included: Fifteen patients had loose cemented titanium stems (Titan. ®. , DePuy) and 15 had well-fixed uncemented titanium stems (Profile, DePuy), but loose or worn uncemented metal-backed cups with conventional UHMWPE liners (Gemini, Tropic and Tri-Lock Plus, DePuy; Harris/Galante and Trilogy, Zimmer). A semi-quantitative histological evaluation was performed in 59 sections of periprosthetic tissues using light microscopy. Wear particles were counted by polarised light and high resolution dark-field microscopy. Additionally, particle composition was determined by SEM-EDXA following particle isolation using an enzymatic digestion method. Blood metal ions were determined with high resolution-ICP-MS. Results. The implants in the uncemented group were revised after a median of 15.7 years (range: 7.25–19.3) due to osteolysis and high wear of the polyethylene liner and metal backing resulting in gross metallosis, and/or cup loosening. The average lifetime of implants in the cemented group was only 6.5 years (range: 1.5–11.75) due to early stem loosening with large osteolysis pockets in the femur close to the cement mantle. Tissue examination revealed similar results for both groups: numerous mononuclear histiocytes and chronic inflammatory cells, a few neutrophils and multinucleated giant cells, and to some extent necrosis. The amount of metal particles per histiocyte positively correlated with the tissue reactions in the cemented, but not in the uncemented group. A higher particle load (medians: C: 14727 vs. UC: 1382 particles/mm. 2. , p<0.0001) was found in tissues adjacent to cemented stems, which contained mainly submicron ZrO. 2. particles. Particles containing pure Ti or Ti alloy elements (size range: 0.21 to 6.46 µm) were most abundant in tissues from the uncemented group. Here, also PE was more frequent, but accounted only for a small portion of total particles (2.8 PE/mm. 2. ). The blood concentrations of titanium (range: 3.8–138.5 microgram/L) and zirconium (cemented cases, range: 0.6–3.5 microgram/L) were highly elevated in cases with high abrasive wear and metallosis. Discussion/Conclusion. Phagocytosis of different wear particles by histiocytes induced a similar chronic inflammatory reaction in the periprosthetic tissues in both groups. ZrO. 2. particles, originating from bone cement degradation, dominated in the cemented group, while in the uncemented group the high abundance of pure Ti and Ti alloy particles of various sizes indicates wear of the metal-backed cups. The low density of polyethylene particles in the tissues suggests that they are not solely responsible for the tissue reactions and accompanying osteolysis. Our findings suggest that the chemical composition of wear particles plays a minor role in the mechanism of osteolysis. Particle size, load and ionic exposure might be more important

Introduction. Primary mechanical stability is important with uncemented THR because early migration is reduced, leading to more rapid osseointegration between the implant and bone. Such primary mechanical stability is provided by the design features of the device. The aim of this study was to compare the migration patterns of two uncemented hip stems, the Furlong Active and the Furlong HAC stem; the study was designed as a randomised control trial. The implants were the Furlong HAC, which is an established implant with good long term results, and the Furlong Active, which is a modified version of the Furlong HAC designed to minimise stress concentrations between the implant and bone, and thus to improve fixation. Materials and methods. The migration of 43 uncemented femoral components for total hip replacement was measured in a randomised control trial using Roentgen Stereophotogrammetric Analysis (RSA) over two years. Twenty-three Furlong HAC and twenty Furlong Active stems were implanted into 43 patients. RSA examinations were carried out post-operatively, and at six months, 12 months and 24 months post-operatively. The patients stood in-front of a purpose made calibration frame which contained accurately positioned radio-opaque markers. From the obtained images, the 3-D positions of the prosthesis and the host bone were reconstructed. Geometrical algorithms were used to identify the components of the implant. These algorithms allowed the femoral component to be studied without the need to attach markers to the prosthesis. The migration was calculated relative to the femoral coordinate system representing the anterior-posterior (A-P), medial-lateral (M-L) and proximal-distal (P-D) directions respectively. Distal migration was termed subsidence. Results. Both stems subsided significantly during the first six months following surgery but almost all stems did not progressively subside thereafter. The Furlong Active stem experienced approximately three times the amount of subsidence of the Furlong HAC stem; this difference was significant (p = 0.02). There was one subsidence outlier (four standard deviations from the mean) for the Furlong Active stem between one and two years post-operatively. Both the stems migrated laterally and rotated into valgus. Lateral migration was greater for the Furlong Active stem; at 12 and 24 months there was a significant migration of the Furlong Active head laterally of 0.51 mm (p = 0.012) and 0.58 mm (p = 0.013) respectively. There was no significant difference in clinical scores between the implants at any RSA examination post-operatively. Discussion. The initial fixation of the Furlong Active stem was not as good as the established stem making it less likely to integrate effectively with the bone. In this study, the theoretical design of a hip replacement to minimise the stress concentration between the implant and bone and thus improve fixation actually resulted in worse implant fixation. Stems designed theoretically to improve fixation may not achieve this. Therefore we recommend that new devices should be tested using Roentgen Stereophotogrammetric Analysis. Acknowledgments This work was funded by the Furlong Charitable Research Foundation

Hydroxyapatite-coated standard anatomical and customised femoral stems are designed to transmit load to the metaphyseal part of the proximal femur in order to avoid stress shielding and to reduce resorption of bone. In a randomised in vitro study, we compared the changes in the pattern of cortical strain after the insertion of hydroxyapatite-coated standard anatomical and customised stems in 12 pairs of human cadaver femora. A hip simulator reproduced the physiological loads on the proximal femur in single-leg stance and stair-climbing. The cortical strains were measured before and after the insertion of the stems.

Significantly higher strain shielding was seen in Gruen zones 7, 6, 5, 3 and 2 after the insertion of the anatomical stem compared with the customised stem. For the anatomical stem, the hoop strains on the femur also indicated that the load was transferred to the cortical bone at the lower metaphyseal or upper diaphyseal part of the proximal femur.

The customised stem induced a strain pattern more similar to that of the intact femur than the standard, anatomical stem.

Bone surface strains were measured in cadaver femora during loading prior to and after resurfacing of the hip and total hip replacement using an uncemented, tapered femoral component. In vitro loading simulated the single-leg stance phase during walking. Strains were measured on the medial and the lateral sides of the proximal aspect and the mid-diaphysis of the femur. Bone surface strains following femoral resurfacing were similar to those in the native femur, except for proximal shear strains, which were significantly less than those in the native femur. Proximomedial strains following total hip replacement were significantly less than those in the native and the resurfaced femur.

These results are consistent with previous clinical evidence of bone loss after total hip replacement, and provide support for claims of bone preservation after resurfacing arthroplasty of the hip.

We implanted titanium and carbon fibre-reinforced plastic (CFRP) femoral prostheses of the same dimensions into five prosthetic femora. An abductor jig was attached and a 1 kN load applied. This was repeated with five control femora. Digital image correlation was used to give a detailed two-dimensional strain map of the medial cortex of the proximal femur. Both implants caused stress shielding around the calcar. Distally, the titanium implant showed stress shielding, whereas the CFRP prosthesis did not produce a strain pattern which was statistically different from the controls. There was a reduction in strain beyond the tip of both the implants.

This investigation indicates that use of the CFRP stem should avoid stress shielding in total hip replacement.