Aims

The aim of this study was to evaluate blood metal ion levels, leucocyte profiles, and serum cytokines in patients with a total hip arthroplasty (THA) involving modular dual-mobility components.

Aims

The purpose of this study was to compare two different types of metal-on-metal (MoM) bearing for total hip arthroplasty (THA): one with a large femoral head (38 mm to 52 mm) and the other with a conventional femoral head (28 mm or 32 mm). We compared clinical outcome, blood metal ion levels, and the incidence of pseudotumour in the two groups.

Metal ions generated from joint replacements are a cause for concern. There is no consensus on the best surrogate measure of metal ion exposure. This study investigates whether serum and whole blood concentrations can be used interchangeably to report results of cobalt and chromium ion concentrations.

Concentrations of serum and whole blood were analysed in 262 concurrent specimens using high resolution inductively-coupled plasma mass-spectrometry. The agreement was assessed with normalised scatterplots, mean difference and the Bland and Altman limits of agreement.

The wide variability seen in the normalised scatterplots, in the Bland and Altman plots and the statistically significant mean differences between serum and whole blood concentrations suggest that they cannot be used interchangeably. A bias was demonstrated for both ions in the Bland-Altman plots. Regression analysis provided a possible conversion factor of 0.71 for cobalt and 0.48 for chromium. However, even when the correction factors were applied, the limits of agreement were greater than ±67% for cobalt and greater than ±85% for chromium, suggesting that serum and whole blood cannot be used interconvertibly. This suggests that serum metal concentrations are not useful as a surrogate measure of systemic metal ion exposure.

As adverse events related to metal on metal hip arthroplasty have been better understood, there has been increased interest in toxicity related to the high circulating levels of cobalt ions. However, distinguishing true toxicity from benign elevations in cobalt levels can be challenging. The purpose of this review is to examine the use of cobalt alloys in total hip arthroplasty, to review the methods of measuring circulating cobalt levels, to define a level of cobalt which is considered pathological and to review the pathophysiology, risk factors and treatment of cobalt toxicity. To the best of our knowledge, there are 18 published cases where cobalt metal ion toxicity has been attributed to the use of cobalt-chromium alloys in hip arthroplasty. Of these cases, the great majority reported systemic toxic reactions at serum cobalt levels more than 100 μg/L. This review highlights some of the clinical features of cobalt toxicity, with the goal that early awareness may decrease the risk factors for the development of cobalt toxicity and/or reduce its severity.

Take home message: Severe adverse events can arise from the release of cobalt from metal-on-metal arthroplasties, and as such, orthopaedic surgeons should not only be aware of the presenting problems, but also have the knowledge to treat appropriately.

Cite this article: Bone Joint J 2016;98-B:14–20.

Metal-on-metal bearings are being increasingly used in young patients. The potential adverse effects of systemic metal ion elevation are the subject of ongoing investigation. The purpose of this study was to investigate whether cobalt and chromium ions cross the placenta of pregnant women with a metal-on-metal hip resurfacing and reach the developing fetus. Whole blood levels were estimated using high-resolution inductively-coupled plasma mass spectrometry.

Our findings showed that cobalt and chromium are able to cross the placenta in the study patients with metal-on-metal hip resurfacings and in control subjects without any metal implants. In the study group the mean concentrations of cobalt and chromium in the maternal blood were 1.39 μg/l (0.55 to 2.55) and 1.28 μg/l (0.52 to 2.39), respectively. The mean umbilical cord blood concentrations of cobalt and chromium were comparatively lower, at 0.839 μg/l (0.42 to 1.75) and 0.378 μg/l (0.14 to 1.03), respectively, and this difference was significant with respect to chromium (p < 0.05).

In the control group, the mean concentrations of cobalt and chromium in the maternal blood were 0.341 μg/l (0.18 to 0.54) and 0.199 μg/l (0.12 to 0.33), and in the umbilical cord blood they were 0.336 μg/l (0.17 to 0.5) and 0.194 μg/l (0.11 to 0.56), respectively. The differences between the maternal and umbilical cord blood levels in the controls were marginal, and not statistically significant (p > 0.05). The mean cord blood level of cobalt in the study patients was significantly greater than that in the control group (p < 0.01). Although the mean umbilical cord blood chromium level was nearly twice as high in the study patients (0.378 μg/l) as in the controls (0.1934 μg/l), this difference was not statistically significant. (p > 0.05)

The transplacental transfer rate was in excess of 95% in the controls for both metals, but only 29% for chromium and 60% for cobalt in study patients, suggesting that the placenta exerts a modulatory effect on the rate of metal ion transfer.

The long term biological effects of wear products following total hip arthroplasty (THA) are unclear. However, the indications for THA are expanding, with increasingly younger patients undergoing the procedure.

This prospective, randomised study compared two groups of patients undergoing THA after being randomised to receive one of two different bearing surfaces: metal-on-polyethylene (MoP) n = 22 and metal-on-metal (MoM) n = 23. We investigated the relationship between three variables: bearing surface (MoP vs MoM), whole blood levels of chromium (Cr) and cobalt (Co) and chromosomal aberrations in peripheral lymphocyte pre-operatively and at one, two and five years post-surgery.

Our results demonstrated significantly higher mean cobalt and chromium (Co and Cr) blood levels in the MoM group at all follow-up points following surgery (p < 0.01), but there were no significant differences in the chromosomal aberration indices between MoM and MoP at two or five years (two years: p = 0.56, p = 0.08, p = 0.91, p = 0.51 and five years: p = 0.086, p = 0.73, p = 0.06, p = 0.34) for translocations, breaks, loss and gain of chromosomes respectively. Regression analysis showed a strong linear relationship between Cr levels and the total chromosomal aberration indices in the MoM group (R² = 0.90016), but this was not as strong for Co (R² = 0.68991). In the MoP group, the analysis revealed a poor relationship between Cr levels and the total chromosomal aberration indices (R² = 0.23908) but a slightly stronger relationship for Co (R² = 0.64292). Across both groups, Spearman’s correlation detected no overall association between Co and Cr levels and each of the studied chromosomal aberrations. There remains no clear indication which THA bearing couple is the most biocompatible, especially in young active patients. While THA continues to be very successful at alleviating pain and restoring function, the long-term biological implications of the procedure still require further scrutiny.

Cite this article: Bone Joint J 2015;97-B:1183–91.

Increased concentrations of metal ions after metal-on-metal resurfacing arthroplasty of the hip remain a concern. Although there has been no proven link to long-term health problems or early prosthetic failure, variables associated with high metal ion concentrations should be identified and, if possible, corrected. Our study provides data on metal ion levels from a series of 76 consecutive patients (76 hips) after resurfacing arthroplasty with the Articular Surface Replacement. Chromium and cobalt ion concentrations in the whole blood of patients with smaller (≤ 51 mm) femoral components were significantly higher than in those with the larger (≥ 53 mm) components (p < 0.01). Ion concentrations in the former group were significantly related to the inclination (p = 0.01) and anteversion (p = 0.01) of the acetabular component. The same relationships were not significant in the patients with larger femoral components (p = 0.61 and p = 0.49, respectively). Accurate positioning of the acetabular component intra-operatively is essential in order to reduce the concentration of metal ions in the blood after hip resurfacing arthroplasty with the Articular Surface Replacement implant.

We report a case of a male patient presenting with bilateral painful but apparently well-positioned and -fixed large-diameter metal-on-metal hip replacements four years post-operatively. Multiple imaging modes revealed a thick-walled, cystic expansile mass in communication with the hip joint (a pseudotumour). Implant retrieval analysis and tissue culture eliminated high bearing wear or infection as causes for the soft-tissue reaction, but noted marked corrosion of the modular neck taper adaptor and corrosion products in the tissues. Therefore, we believe corrosion products from the taper caused by mismatch of the implant components led to pseudotumour formation requiring revision.

We report serum metal ion level data in patients with unilateral and bilateral hip resurfacing over a ten-year period. In these patients there is an increase in both cobalt and chromium levels above the accepted reference ranges during the first 18 months after operation. Metal ion levels remain elevated, but decline slowly for up to five years. However, the levels then appear to start rising again in some patients up to the ten-year mark. There was no significant difference in cobalt or chromium levels between men and women. These findings appear to differ from much of the current literature.

The clinical significance of a raised metal ion level remains under investigation.

This study reports on ceramic-on-metal (CoM) bearings in total hip replacement. Whole blood metal ion levels were measured. The median increase in chromium and cobalt at 12 months was 0.08 μg/1 and 0.22 μg/1, respectively, in CoM bearings. Comparable values for metal-on-metal (MoM) were 0.48 μg/1 and 0.32 μg/1. The chromium levels were significantly lower in CoM than in MoM bearings (p = 0.02). The cobalt levels were lower, but the difference was not significant. Examination of two explanted ceramic heads revealed areas of thin metal transfer. CoM bearings (one explanted head and acetabular component, one explanted head and new acetabular component, and three new heads and acetabular components) were tested in a hip joint simulator. The explanted head and acetabular component had higher bedding-in. However, after one million cycles all the wear rates were the same and an order of magnitude less than that reported for MoM bearings. There were four outliers in each clinical group, primarily related to component malposition.

The recent resurgence in the use of metal-on-metal bearings has led to fresh concerns over metal wear and elevated systemic levels of metal ions.

In order to establish if bearing diameter influences the release of metal ions, we compared the whole blood levels of cobalt and chromium (at one year) and the urinary cobalt and chromium output (at one to three and four to six years) following either a 50 mm or 54 mm Birmingham hip resurfacing or a 28 mm Metasul total hip replacement. The whole blood concentrations and daily output of cobalt and chromium in these time periods for both bearings were in the same range and without significant difference.