Aims. Vitamin E-infused highly cross-linked polyethylene (E1) has recently been introduced in total knee arthroplasty (TKA). An in vitro wear simulator study showed that E1 reduced polyethylene wear. However there is no published information regarding in vivo wear. Previous reports suggest that newly introduced materials which reduce in vitro polyethylene wear do not necessarily reduce in vivo polyethylene wear. To assist in the evaluation of the newly introduced material before widespread use, we established an in vivo polyethylene wear particle analysis for TKA. The aim of this study was to compare in vivo polyethylene wear particle generation between E1 and conventional polyethylene (ArCom) in TKA. Methods. A total of 34 knees undergoing TKA (17 each with ArCom or E1) were investigated. Except for the polyethylene insert material, the prostheses used for both groups were identical. Synovial fluid was obtained at a mean of 3.4 years (SD 1.3) postoperatively. The in vivo polyethylene wear particles were isolated from the synovial fluid using a previously validated method and examined by scanning electron microscopy. Results. The total number of polyethylene wear particles obtained from the knees with E1 (mean 6.9, SD 4.0 × 10. 7. counts/knee) was greater than that obtained from those with ArCom (mean 2.2, SD 2.6 × 10. 7. counts/knee) (p = 0.001). The particle size (equivalent circle of diameter) from the knees with E1 was smaller (mean 0.5 μm, SD 0.1) than that of knees with ArCom (mean 1.5, SD 0.3 μm) (p = 0.001). The aspect ratio of particles from the knees with E1 (mean 1.3, SD 0.1) was smaller than that with ArCom (mean 1.4, SD 0.1) (p < 0.001 ). Conclusion. This is the first report of in vivo wear particle analysis of E1. E1 polyethylene did not reduce the number of in vivo polyethylene wear particles compared with ArCom in early clinical stage. Further careful follow-up of newly introduced E1 for TKA should be carried out. Cite this article: Bone Joint J 2020;102-B(11):1527–1534

We describe a cohort of patients with a high rate of mid-term failure following Kinemax Plus total knee replacement inserted between 1998 and 2001. This implant has been recorded as having a survival rate of 96% at ten years. However, in our series the survival rate was 75% at nine years. This was also significantly lower than that of subsequent consecutive series of PFC Sigma knee replacements performed by the same surgeon. No differences were found in the clinical and radiological parameters between the two groups. At revision the most striking finding was polyethylene wear. An independent analysis of the polyethylene components was therefore undertaken. Scanning electron microscopy revealed type 2 fusion defects in the ultra-high molecular weight polyethylene (UHMWPE), which indicated incomplete boundary fusion. Other abnormalities consistent with weak UHMWPE particle interface strength were present in both the explanted inserts and in unused inserts from the same period. We consider that these type 2 fusion defects are the cause of the early failure of the Kinemax implants. This may represent a manufacturing defect resulting in a form of programmed polyethylene failure

Introduction. Infection remains as one of the major challenges of total joint surgery. One-stage irrigation, debridement and reimplantation, or two-stage revision surgery with a temporary implantation of antibiotic eluting bone cement spacer followed by reimplantation are two methods often used to treat infected patients with mixed outcomes. Like bone cement, ultra-high molecular weight polyethylene (UHMWPE) can also be used as a carrier for antibiotics. Recently, we demonstrated that vancomycin and rifampin can be delivered from UHMWPE implants at therapeutic levels to eradicate Staphylococcus aureus biofilm in a lupine animal model. There are regulatory challenges in translating these types of combination devices to clinical use. Last year, at this meeting, we presented the preliminary pre-clinical testing for a temporary UHMWPE spacer containing gentamicin sulfate as a first step towards clinical use. Since then, we carried out a survey among the Knee Society membership about their preference for spacer use in two-stage revision surgery and found that 43% prefer to use a CoCr femoral component on an all-poly cemented tibial insert, 22% prefer bone cement spacers molded in the OR, 20% prefer static bone cement spacers, and 14% prefer pre-formed bone cement spacers. We modified our implant design based on the majority's preference for a total knee system, rather than bone cement spacers, in the temporary two-stage approach. In this study, we explored the effect of gentamicin sulfate (GS) elution from UHMWPE/GS tibial inserts on bacterial colonization on CoCr surfaces. Methods. We characterized the gentamicin sulfate (GS) particles with scanning electron microscopy (SEM). We molded UHMWPE/GS powder blends and characterized the morphology using SEM and Energy Dispersive X-Ray Spectroscopy (EDS). We submerged samples of molded UHMWPE/GS in buffered phosphate solution (PBS) at 37°C and quantified the extent of GS elution into PBS with a method described by Gubernator et al. using o-phthaladehyde (OPA) [1]. Under basic conditions, OPA reacts with primary amino groups to form fluorescent complexes. Since gentamicin is the only source of such amino acids in our elution samples, the number of fluorescent complexes formed is directly proportional to the amount of gentamicin in the sample. Using this method, we could quantify gentamicin elution by measuring sample fluorescence post OPA-reaction. We used a plate reader to excite the fluorescent complexes formed in the OPA reaction and measured the resulting emission at wavelengths of 340 nm and 455 nm, respectively. We also quantified the effect of the standard cleaning protocol (heated sonication in alkaline water and alcohol) used to clean UHMWPE implants on subsequent GS elution from UHMWPE/GS samples using the OPA method. We used agar diffusion tests to characterize antibacterial properties of UHMWPE/GS samples after cleaning. For these tests, we collected eluents collected from UHMWPE/GS and gentamicin-impregnated bone cement (BC/GS) following 1, 2, 3, and 4 weeks of elution, and tested against S. aureus (ATCC 12600). We used the “daughter cells” method developed by Bechert et al. to assess anticolonizing properties of UHMWPE/GS [2,3]. We also characterized the colonization of bacteria on CoCr surfaces in the presence of GS eluting from UHMWPE/GS test samples. For this we modified a Pin-on-Disc (PoD) wear tester: An UHMWPE/GS pin and UHMWPE pin (control) articulated against an implant-finish CoCr disc with Tryptic Soy Broth containing S. Aureus as the lubricant. After 18 hrs, we rinsed the articular surfaces of the pin and disc and stamped them onto Agar gel to transfer any adherent bacteria. We incubated the Agar plate overnight such that adherent bacteria proliferated and became visible. Results. SEM characterized the GS particles as hollow spheres (Fig 1a). These formed small groups of agglomerated domains at the virgin resin boundaries of UHMWPE after molding (Fig 1b). Sulfur signature from the EDS analysis identified the agglomerated domains as GS particles (Fig 2). Elution of GS started with an initial burst and was followed by steady elution up to 12 weeks (Fig 3). Cleaning reduced the initial burst GS elution; and the elution remained unchanged after 2 days (Fig 4). The agar diffusion test showed simmilar inhibition zones for the eluents collected from UHMWPE/GS and BC/GS, suggesting that these samples yield similar antibacterial activity against S. aureus (Fig 5). UHMWPE/GS demonstrated pronounced anticolonizing properties, effectively mitigating the proliferation of S. aureus “daughter” cells. Anticolonizing activity of Palacos R+G was not significantly different when compared with UHMWPE/GS. The PoD test showed little-to-no colonization of CoCr surfaces in the presence of UHMWPE/GS pins, indicative of excellent antibacterial properties of UHMWPE/GS against S. aureus. Conclusion. SEM and EDS has allowed us to visualize domains of gentamicin sulfate particles in UHMWPE. Our OPA method has greater precision than traditional agar-well diffusion methods of measuring gentamicin concentration and showed that gentamicin sulfate-loaded UHMWPE elutes at the same rate as Palacos R+G. Pin-on-disc experiments and the daughter cell method both confirmed that these two materials have similar anticolonization abilities. We also found that using the standard cleaning protocol for UHMWPE orthopedic implants decreased the burst of gentamicin eluting from UHMWPE, but after 2 days, it had no effect compared to uncleaned UHMWPE/GS. Finally, we found that UHMWPE/GS can reduce the colonization of bacteria on CoCr. UHMWPE/GS continues to be a promising material for treating PJI. For figures, tables, or references, please contact authors directly

Advances in polyethylene (PE) in total hip arthroplasty have led to interest and increased use of highly crosslinked PE (HXLPE) in total knee arthroplasty (TKA). Biomechanical data suggest improved wear characteristics for HXLPE inserts over conventional PE in TKA. Short-term results from registry data and few clinical trials are promising. Our aim is to present a review of the history of HXLPEs, the use of HXLPE inserts in TKA, concerns regarding potential mechanical complications, and a thorough review of the available biomechanical and clinical data.

Cite this article: Bone Joint J 2017;99-B:996–1002.

Metallosis is a rare cause of failure after total knee replacement and has only previously been reported when there has been abnormal metal-on-metal contact. We describe 14 patients (15 knees) whose total knee replacement required revision for a new type of early failure caused by extensive metallosis. A modification of a cementless rotating platform implant, which had previously had excellent long-term survival, had been used in each case. The change was in the form of a new porous-beaded surface on the femoral component to induce cementless fixation, which had been used successfully in the fixation of acetabular and tibial components. This modification appeared to have resulted in metallosis due to abrasive two-body wear. The component has subsequently been recalled and is no longer in use. The presentation, investigation, and findings at revision are described and a possible aetiology and its implications are discussed.