Aims. Radiostereometric analysis (RSA) is the most accurate radiological method to measure in vivo wear of highly cross-linked polyethylene (XLPE) acetabular components. We have previously reported very low wear rates for a sequentially irradiated and annealed X3 XLPE liner (Stryker Orthopaedics, USA) when used in conjunction with a 32 mm femoral heads at ten-year follow-up. Only two studies have reported the long-term wear rate of X3 liners used in conjunction with larger heads using plain radiographs which have poor sensitivity. The aim of this study was to measure the ten-year wear of thin X3 XLPE liners against larger 36 or 40 mm articulations with RSA. Methods. We prospectively reviewed 19 patients who underwent primary cementless THA with the XLPE acetabular liner (X3) and a 36 or 40 mm femoral head with a resultant liner thickness of at least 5.8 mm. RSA radiographs at one week, six months, and one, two, five, and ten years postoperatively and femoral head penetration within the acetabular component were measured with UmRSA software. Of the initial 19 patients, 12 were available at the ten-year time point. Results. The median proximal, 2D, and 3D wear rates calculated between one and ten years were all less than 0.005 mm/year, with no patient recording a proximal wear rate of more than 0.021 mm/year. Importantly, there was no increase in the wear rate between five and ten years. Conclusion. The very low wear rate of X3 XLPE liners with larger articulations remains encouraging for the future clinical performance of this material. Cite this article: Bone Jt Open 2023;4(11):839–845

Aims. The primary outcome was investigating differences in wear, as measured by femoral head penetration, between cross-linked vitamin E-diffused polyethylene (vE-PE) and cross-linked polyethylene (XLPE) acetabular component liners and between 32 and 36 mm head sizes at the ten-year follow-up. Secondary outcomes included acetabular component migration and patient-reported outcome measures (PROMs) such as the EuroQol five-dimension questionnaire, 36-Item Short-Form Health Survey, Harris Hip Score, and University of California, Los Angeles Activity Scale (UCLA). Methods. A single-blinded, multi-arm, 2 × 2 factorial randomized controlled trial was undertaken. Patients were recruited between May 2009 and April 2011. Radiostereometric analyses (RSAs) were performed from baseline to ten years. Of the 220 eligible patients, 116 underwent randomization, and 82 remained at the ten-year follow-up. Eligible patients were randomized into one of four interventions: vE-PE acetabular liner with either 32 or 36 mm femoral head, and XLPE acetabular liner with either 32 or 36 mm femoral head. Parameters were otherwise identical except for acetabular liner material and femoral head size. Results. A total of 116 patients participated, of whom 77 were male. The median ages of the vE-PE 32 mm and 36 mm groups were 65 (interquartile range (IQR) 57 to 67) and 63 years (IQR 56 to 66), respectively, and of the XLPE 32 mm and 36 mm groups were 64 (IQR 58 to 66) and 61 years (IQR 54 to 66), respectively. Mean total head penetration was significantly lower into vE-PE acetabular liner groups than into XLPE acetabular liner groups (-0.219 mm (95% confidence interval -0.348 to -0.090); p = 0.001). There were no differences in wear according to head size, acetabular component migration, or PROMs, except for UCLA. There were no cases of aseptic loosening or failures requiring revision at long-term follow-up. Conclusion. Significantly lower wear was observed in vE-PE acetabular liners than in XLPE acetabular liners. No difference in wear was observed between different head size or PROMs except for the UCLA at ten years. Cite this article: Bone Joint J 2023;105-B(10):1052–1059

The creep and wear behaviour of highly cross-linked polyethylene and standard polyethylene liners were examined in a prospective, double-blind randomised, controlled trial using radiostereometric analysis. We randomised 54 patients to receive hip replacements with either highly cross-linked polyethylene or standard liners and determined the three-dimensional penetration of the liners over three years. After three years the mean total penetration was 0.35 mm (SD 0.14) for the highly cross-linked polyethylene group and 0.45 mm (SD 0.19) for the standard group. The difference was statistically significant (p = 0.0184). From the pattern of penetration it was possible to discriminate creep from wear. Most (95%) of the creep occurred within six months of implantation and nearly all within the first year. There was no difference in the mean degree of creep between the two types of polyethylene (highly cross-linked polyethylene 0.26 mm, SD 0.17; standard 0.27 mm, SD 0.2; p = 0.83). There was, however, a significant difference (p = 0.012) in the mean wear rate (highly cross-linked polyethylene 0.03 mm/yr, SD 0.06; standard 0.07 mm/yr, SD 0.05). Creep and wear occurred in significantly different directions (p = 0.01); creep was predominantly proximal whereas wear was anterior, proximal and medial. We conclude that penetration in the first six months is creep-dominated, but after one year virtually all penetration is due to wear. Highly cross-linked polyethylene has a 60% lower rate of wear than standard polyethylene and therefore will probably perform better in the long term

Oxidized zirconium (Oxinium) and highly cross-linked polyethylene (HXLPE) were developed with the purpose of minimizing wear, and subsequent osteolysis, in Total Hip Arthroplasty (THA). However, few articles have been published on long-term results of Oxinium on highly cross-linked polyethylene. The purpose of this investigation is to report minimum 10-year HXLPE wear rates and the clinical outcome of patients in this group and compare this population to a control group of cobalt chrome and ceramic. One hundred forty THAs were performed for 123 patients using an Oxinium head with an HXLPE liner. Ninety-seven had 10 years of clinical follow-up (avg. 14.5). Harris Hip Scores (HHS) were collected preoperatively and at the most recent follow-up. Radiographs of 85 hips were available for a minimum 10-year follow-up (avg. 14.5) and used to calculate wear using PolyWare software. Control groups of cobalt chrome and ceramic articulation on HXLPE with a minimum 10-year follow-up were studied. Clinical follow-up of the Oxinium group showed a statistical improvement compared to preoperative and was similar to the control group of patients. Radiographic evaluation found the linear and volumetric wear rates for the Oxinium group of 0.03 mm/year (range 0.00–0.08) and 3.46 mm. 3. /year (range 1.0 to 15.0) respectively. There was no statistically significant difference in linear or volumetric wear rate between the groups (P-value 0.92 and 0.55 respectively). None of these patients underwent revision of their hip for any reason. Oxinium on highly cross-linked polyethylene has performed exceptionally with wear rates comparable to those of cobalt chrome or ceramic on HXLPE

Introduction. Highly cross-linked polyethylene has been introduced to decrease osteolysis secondary to polyethylene wear debris generation, but there are few long-term data on revision total hip arthroplasty using highly cross-linked polyethylene liners. The purpose of this study was to report the long-term radiographic and clinical outcomes of a highly cross-linked polyethylene liner in revision total hip arthroplasty. Materials & Methods. We analyzed 63 revision total hip arthoplasties that were performed in 63 patients using a highly cross-linked polyethylene liner between April 2000 and February 2005. Of these, nine died and four were lost to follow-up before the end of the 10-year evaluation. Thus, the final study cohort consisted of 50 patients (50 hips). There were 26 males and 24 females with a mean age at time of revision total hip arthoplasty of 53 years (range, 27–75 years). Mean duration of follow-up was 11 years (range, 10–14 years). Results. Mean Harris hip score improved from 44 points preoperatively to 85 points at final follow-up. No radiographic evidence of osteolysis was found in any hip. One hip required re-revision surgery for acetabular cup loosening at 6.5 years postoperatively. One required re-revision with a constrained liner because of recurrent dislocation. Three sustained deep infections requiring additional surgical procedures. Kaplan-Meier survivorship with an end point of re-revision for any reason was 91.0% and for aseptic cup loosening was 97.9% at 11 years (Figs. 1 and 2). Conclusions. At a minimum of 10 years, the highly cross-linked polyethylene liners showed excellent clinical performance and implant survivorship, and were not associated with osteolysis in our group of patients with revision total hip arthoplasties

Introduction. Technological advances in the processing of polyethylene have led to improved survivorship of total hip arthroplasty. The purpose of this study was to determine if a second generation highly cross-linked polyethylene could improve upon wear rates compared to conventional and first generation cross-linked polyethylene in patients undergoing primary total hip arthroplasty. Methods. Linear and volumetric wear rates of a second generation highly cross-linked polyethylene were evaluated following primary total hip arthroplasty. There were 44 patients with an average age of 68.6 years and mean follow-up of 5.3 years. Patients were evaluated at six weeks, one, two and five years. Wear rates were determined from digitized AP Pelvis radiograph by an independent observer using Martell's software. Acetabular inclination and femoral head size were also evaluated to determine variability in wear rates. Results. The mean linear wear rate for the entire group was 0.015mm/year (±0.055). There was a 64% decrease in linear wear rate when compared to a first generation highly cross-linked polyethylene from the same institution. There was a 90% decrease in wear rate compared to conventional polyethylene. There were no differences in the linear wear rate between the 32mm vs. larger head sizes (36mm and 40mm). However, there was a 30% increase in volumetric wear rate with larger head sizes. The mean wear rate in patients with cup inclination less than 45 degrees was 0.006mm/year compared with 0.024mm/year for those with an inclination greater than 45 degrees. The amount of linear wear was increased by 4 times in patients with a cup inclination of greater than 45 degrees. There was no evidence of any osteolysis in this group of patients. Conclusion. Our data with a mean follow-up of 5.3 years, using a second generation highly cross-linked polyethylene, demonstrates a dramatic decrease in incidents of linear wear compared to conventional polyethylene and first generation highly cross-linked polyethylene (Figure 1). Of concern is the higher volumetric wear rate noted with larger head sizes and increased linear wear rates with cup inclination angles of greater than 45 degrees. Despite improvements in wear rates using a second generation highly cross-linked polyethylene, cup orientation and choice of head size play significant roles in implant survivorship

Aims. Oxidized zirconium (OxZi) and highly cross-linked polyethylene (HXLPE) were developed to minimize wear and risk of osteolysis in total hip arthroplasty (THA). However, retrieval studies have shown that scratched femoral heads may lead to runaway wear, and few reports of long-term results have been published. The purpose of this investigation is to report minimum ten-year wear rates and clinical outcomes of THA with OxZi femoral heads on HXLPE, and to compare them with a retrospective control group of cobalt chrome (CoCr) or ceramic heads on HXLPE. Methods. From 2003 to 2006, 108 THAs were performed on 96 patients using an OxZi head with a HXLPE liner with minimum ten-year follow-up. Harris Hip Scores (HHS) were collected preoperatively and at the most recent follow-up (mean 13.3 years). Linear and volumetric liner wear was measured on radiographs of 85 hips with a minimum ten-year follow-up (mean 14.5 years). This was compared to a retrospective control group of 45 THAs using ceramic or CoCr heads from October 1999 to February 2005, with a minimum of ten years’ follow-up. Results. Average HHS improved from 50.8 to 91.9 and 51.0 to 89.8 in the OxZi group and control group, respectively (p = 0.644), with no osteolysis in either group. Linear and volumetric wear rates in the OxZi group averaged 0.03 mm/year and 3.46 mm. 3. /year, respectively. There was no statistically significant difference in HHS scores, nor in linear or volumetric wear rate between the groups, and no revision for any indication. Conclusion. The radiological and clinical outcomes, and survivorship of THA with OxZi femoral heads and HXLPE liners, were excellent, and comparable to CoCr or ceramic heads at minimum ten-year follow-up. Wear rates are below what would be expected for development of osteolysis. OxZi-HXLPE is a durable bearing couple with excellent long-term outcomes. Cite this article: Bone Joint J 2024;106-B(3 Supple A):38–43

Aims. Highly cross-linked polyethylene (HXLPE) has greatly improved the durability of total hip arthroplasty (THA) in young patients because of its improved wear characteristics. Few studies have followed this population into the second decade, and therefore the purpose of this investigation was to evaluate the clinical outcome for THA patients 50 years of age and younger at a minimum of 15 years postoperatively. The second purpose was to evaluate the radiological findings secondary to wear or mechanical failure of the implant. Methods. Between October 1999 and December 2005, 105 THAs were performed in 95 patients (53 female, 42 male) aged 50 years and younger (mean 42 years (20 to 50)). There were 87 patients (96 hips) that were followed for a minimum of 15 years (mean 17.3 years (15 to 21)) for analysis. Posterior approach was used with cementless fixation with a median head size of 28 mm. HXLPE was the acetabular bearing for all hips. Radiographs were evaluated for polyethylene wear, radiolucent lines, and osteolysis. Results. Clinical outcomes showed significant improvement of mean Harris Hip Scores from 52.8 (SD 13.5) preoperatively to 94.8 (SD 7.6) postoperatively. One hip was revised for recurrent instability, and there were no infections. No hips were revised for mechanical loosening or osteolysis. Mean polyethylene linear wear was 0.04 mm/year and volumetric wear was 6.22 mm. 3. /year, with no significant differences between head size or material. Osteolysis was not present in any of the hips. Conclusion. The use of HXLPE in THA for patients aged 50 years and younger has performed exceptionally well without evidence of significant wear causing mechanical loosening or necessitating revision. The radiolucent lines of the acetabular component must be followed to determine the prognostic significance. This investigation represents the longest clinical follow-up of a large, consecutive cohort of patients aged 50 years or younger with THA using HXLPE. This long-term analysis found negligible polyethylene wear, no incidence of aseptic loosening, and excellent clinical outcomes at and beyond 15 years of follow-up. Cite this article: Bone Joint J 2021;103-B(7 Supple B):78–83

Aims. We aimed to evaluate the long-term outcome of highly cross-linked polyethylene (HXLPE) cemented acetabular components and assess whether any radiolucent lines (RLLs) which arose were progressive. Methods. We retrospectively reviewed 170 patients who underwent 187 total hip arthroplasties at two hospitals with a minimum follow-up of ten years. All interventions were performed using the same combination of HXLPE cemented acetabular components with femoral stems made of titanium alloy. Kaplan-Meier survival analysis was performed for the primary endpoint of acetabular component revision surgery for any reason and secondary endpoint of the appearance of RLLs. RLLs that had appeared once were observed over time. We statistically assessed potential relationships between RLLs and a number of factors, including the technique of femoral head autografting and the Japanese Orthopaedic Association score. Results. The mean follow-up period was 13.0 years (10.0 to 16.3). Femoral head autografting was performed on 135 hips (72.2%). One acetabular component was retrieved because of deep infection. No revision was performed for the aseptic acetabular loosening. The Kaplan-Meier survival curve for the primary and secondary endpoints were 98.2% (95% confidence interval (CI) 88.6% to 99.8%) and 79.3% (95% CI 72.8% to 84.6%), respectively. RLLs were detected in 38 hips (21.2%), at a mean of 1.7 years (1 month to 6 years) postoperatively. None of the RLLs were progressive, and the presence of RLLs did not show a significant association with the survival and clinical score. RLLs were more frequently observed in hips without femoral head autografts than in those with autografts. Conclusion. The use of HXLPE cemented acetabular components in total hip arthroplasty demonstrated excellent clinical outcomes after ten years, and no RLLs were progressive, and their presence did not affect the outcome. Femoral head autografting did not negatively impact the acetabular component survival or the appearance of RLLs. Cite this article: Bone Joint J 2021;103-B(10):1604–1610

We have performed an RCT of cross-linked versus non cross-linked polyethylene with 125 patients followed for five years. The study showed a dramatic reduction of wear with the cross-linked polyethylene consistent with the in-vitro studies. Because it has been recognised that hard bearings are sensitive to edge loading we were concerned that highly cross-linked polyethylene might exhibit wear properties similar to hard bearings. We have therefore analysed the wear rate as it relates to both anteversion and tilt, to compare non cross-linked polyethylene with cross-linked polyethylene. We found that there was no relationship between tilt and ante-version on any wear indices. These data suggest that, despite having different mechanical properties to non cross-linked polyethylene, cross-linked polyethylene does not exhibit increased wear with conditions that increase edge loading

Introduction: Wear simulator studies have predicted that highly cross-linked polyethylenes can reduce linear wear by 50–90% when compared to traditional polyethylene (gamma sterilized in air). Clinical experience with a highly cross-linked polyethylene which was irradiated to 10 megarads and cold anneled but not remelted (Crossfire) began in October 1998. Methods: 72 Crossfire implants (69 patients) were implanted and have a minimum 3 year follow-up (mean 3.85 years). 31 of these implants (29 patients) have a minimum 4 year follow-up (mean 4.64 years). Linear wear utilizing a validated computerized technique was measured and compared to 38 hips (37 patients) implanted with a non-cross-linked polyethylene (gamma irradiated – N2 vac) with a mean follow-up of 4.96 years. Results: The mean wear in millimeters per year for the highly cross-linked Crossfire polyethylene with minimum 3 year follow-up was 0.054 (sd=0.032). At minimum 4 year follow-up wear was 0.057 mm/yr (sd=0.036). The wear for the N2 vac non-cross-linked polyethylene was 0.138 mm/yr (sd=0.066). Using a standard t-test the difference in wear was highly significant at p=< 0.001. Discussion & Conclusion: Cross-linking is the only material characteristic shown to improve wear performance of polyethylene. Our clinical experience demonstrates a 50% reduction in wear over N2 vac irradiated polyethylene during the first three years with no significant change out to a mean of 4.64 years. Cross-linked polyethylenes hold great hopes for significant reduction in wear and osteolysis and prolonged life of hip arthroplasty in patients of all ages

Aims. We aimed to investigate if the use of the largest possible cobalt-chromium head articulating with polyethylene acetabular inserts would increase the in vivo wear rate in total hip arthroplasty. Methods. In a single-blinded randomized controlled trial, 96 patients (43 females), at a median age of 63 years (interquartile range (IQR) 57 to 69), were allocated to receive either the largest possible modular femoral head (36 mm to 44 mm) in the thinnest possible insert or a standard 32 mm head. All patients received a vitamin E-doped cross-linked polyethylene insert and a cobalt-chromium head. The primary outcome was proximal head penetration measured with radiostereometric analysis (RSA) at two years. Secondary outcomes were volumetric wear, periacetabular radiolucencies, and patient-reported outcomes. Results. At two years, 44 patients in each group were available for RSA assessment. The median total two-year proximal head penetration was -0.02 mm (IQR -0.09 to 0.07; p = 0.548) for the largest possible head and -0.01 mm (IQR -0.07 to 0.10; p = 0.525) for 32 mm heads. Their difference was not statistically significant (p = 0.323). Neither group demonstrated a bedding-in period. The median steady-state volumetric wear rates were 6.1 mm. 3. /year (IQR -59 to 57) and 3.5 mm. 3. /year (-21 to 34) respectively, and did not differ between the groups (p = 0.848). There were no statistically significant differences in periacetabular radiolucencies or patient-reported outcomes. Conclusion. The use of the largest possible metal head did not increase vitamin E-doped cross-linked polyethylene wear compared with 32 mm heads at two years. Linear wear was negligible and volumetric wear rates were very low in both head size groups. There was a tendency towards higher values of volumetric wear in large heads that warrants longer-term evaluation before any definite conclusions about the association between head size and wear can be drawn. Cite this article: Bone Joint J 2021;103-B(7):1206–1214

Aims. Vitamin E-infused highly cross-linked polyethylene (E1) has recently been introduced in total knee arthroplasty (TKA). An in vitro wear simulator study showed that E1 reduced polyethylene wear. However there is no published information regarding in vivo wear. Previous reports suggest that newly introduced materials which reduce in vitro polyethylene wear do not necessarily reduce in vivo polyethylene wear. To assist in the evaluation of the newly introduced material before widespread use, we established an in vivo polyethylene wear particle analysis for TKA. The aim of this study was to compare in vivo polyethylene wear particle generation between E1 and conventional polyethylene (ArCom) in TKA. Methods. A total of 34 knees undergoing TKA (17 each with ArCom or E1) were investigated. Except for the polyethylene insert material, the prostheses used for both groups were identical. Synovial fluid was obtained at a mean of 3.4 years (SD 1.3) postoperatively. The in vivo polyethylene wear particles were isolated from the synovial fluid using a previously validated method and examined by scanning electron microscopy. Results. The total number of polyethylene wear particles obtained from the knees with E1 (mean 6.9, SD 4.0 × 10. 7. counts/knee) was greater than that obtained from those with ArCom (mean 2.2, SD 2.6 × 10. 7. counts/knee) (p = 0.001). The particle size (equivalent circle of diameter) from the knees with E1 was smaller (mean 0.5 μm, SD 0.1) than that of knees with ArCom (mean 1.5, SD 0.3 μm) (p = 0.001). The aspect ratio of particles from the knees with E1 (mean 1.3, SD 0.1) was smaller than that with ArCom (mean 1.4, SD 0.1) (p < 0.001 ). Conclusion. This is the first report of in vivo wear particle analysis of E1. E1 polyethylene did not reduce the number of in vivo polyethylene wear particles compared with ArCom in early clinical stage. Further careful follow-up of newly introduced E1 for TKA should be carried out. Cite this article: Bone Joint J 2020;102-B(11):1527–1534

The 2021 Australian Orthopaedic Association National Joint Replacement Registry report indicated that total shoulder replacement using both mid head (TMH) length humeral components and reverse arthroplasty (RTSA) had a lower revision rate than stemmed humeral components in anatomical total shoulder arthroplasty (aTSA) - for all prosthesis types and diagnoses. The aim of this study was to assess the impact of component variables in the various primary total arthroplasty alternatives for osteoarthritis in the shoulder. Data from a large national arthroplasty registry were analysed for the period April 2004 to December 2020. The study population included all primary aTSA, RTSA, and TMH shoulder arthroplasty procedures undertaken for osteoarthritis (OA) using either cross-linked polyethylene (XLPE) or non-cross-linked polyethylene (non XLPE). Due to the previously documented and reported higher revision rate compared to other anatomical total shoulder replacement options, those using a cementless metal backed glenoid components were excluded. The rate of revision was determined by Kaplan-Meir estimates, with comparisons by Cox proportional hazard models. Reasons for revision were also assessed. For a primary diagnosis of OA, aTSA with a cemented XLPE glenoid component had the lowest revision rate with a 12-year cumulative revision rate of 4.7%, compared to aTSA with cemented non-XLPE glenoid component of 8.7%, and RTSA of 6.8%. The revision rate for TMH was lower than aTSA with cemented non-XLPE, but was similar to the other implants at the same length of follow-up. The reason for revision for cemented aTSR was most commonly component loosening, not rotator cuff deficiency. Long stem humeral components matched with XLPE in aTSA achieve a lower revision rate compared to shorter stems, long stems with conventional polyethylene, and RTSA when used to treat shoulder OA. In all these cohorts, loosening, not rotator cuff failure was the most common diagnosis for revision

Background. Cross-linked polyethylene has much less wear than conventional polyethylene and can used in a more bone conserving thickness of 4 mm. We have used it for hip resurfacing since 2001. Questions/Purposes. This study evaluated the effectiveness of a highly cross-linked polyethylene acetabular component for hip resurfacing in patients under age 50. I posed 5 questions: (1) What are the functional results, (2) What are the complications, (3) What is the 10-year implant survivorship, (4) What is the femoral head penetration into the polyethylene, and (5) What is the bone conservation?. Participants and Methods. There were 160 resurfacing procedures (144 participants) using a 2 piece acetabular shell and a cobalt chromium femoral component (fig. 1). Participants averaged 43 years of age at the time of surgery (range, 23 – 49.5 years) and 70% were women. Inclusion criteria were patients with adequate acetabular bone and a high enough head-neck ratio so that the reconstruction would not violate the femoral neck cortices or medial acetabular wall. The largest cross-linked polyethylene available was 49 mm so only patients with smaller femoral geometries were included. The Harris, WOMAC, and UCLA hip scores were used to assess pain, activity, and function and participants were asked about their satisfaction with the procedure. Digital radiography and computed tomographic scans were used to evaluate femoral head penetration and osteolysis. Removed polyethylene liners were analyzed. Results. The median follow-up was 11.5 years (range, 10 – 14 years). One participant was lost to follow-up and 1 died. The mean Harris Hip Score was 95 and 95% of the participants rated the results of their procedure as excellent. The average UCLA activity score was 8. One patient underwent successful revision surgery for acetabular loosening. Four participants underwent successful revision to a total hip replacement because of femoral neck fracture (2), femoral loosening, or infection. The Kaplan-Meier survivorship was 96%. There were no revisions for polyethylene wear and there were no instances of osteolysis. The medial acetabular wall thickness averaged 7.3 mm (range, 1.5 mm – 14.9 mm). The mean inclination angle was 39°. The mean femoral head penetration was 0.05 mm/year (range, .028 – .09 mm/year). Conclusions. Hip resurfacing with a highly cross-linked polyethylene acetabular component is a reliable procedure at mid-term follow-up. The rate of polyethylene wear is below the osteolytic threshold of .1 mm/yr. The preservation of both acetabular and femoral bone is reasonable even in comparison to thin metal shells available for metal-on-metal resurfacing and total hip replacement. The functional results are comparable to those of metal-on-metal resurfacing without the concerns of a metal bearing couple. The procedures are demanding and patient selection is critical to the success of the procedure. Although long-term follow-up is needed to determine if implant survivorship with highly cross-linked polyethylene acetabular components will equal that of metal-on-metal prostheses, the low rate of femoral head penetration suggests that many years of use in young highly active participants are possible

Introduction and Aims: While highly cross-linked polyethylene has achieved widespread clinical use based on laboratory testing showing significant wear reduction, there is little clinical information demonstrating its benefits in vivo. This study reports the early clinical and wear performance of a prospective randomised controlled trial comparing highly cross-linked to standard polyethylene. Method: One hundred patients were enrolled in a prospective randomised controlled trial in which all patients received a hybrid THR (cemented Versys stem, Triology cementless acetabulum). The two groups were virtually identical in terms of age, weight, male/female ratio and received identical hip implants, except that one half (50 patients) randomly received a highly cross-linked polyethylene liner. Clinical outcomes were determined using Harris hip, WOMAC and SF-12 scores. Two-dimensional (2D) and three-dimensional (3D) wear rates were determined using a validated radiographic technique based on AP and lateral radiographs at six weeks and one, two and three years post-operatively. Results: At two years minimum follow-up (range two to four years), there were no differences in Harris hip, WOMAC or SF-12 scores. No patients were lost to follow-up, although five patients had died of unrelated causes. There were no infections, dislocations or revisions to date. Wear analysis at one-year post-op showed high penetration rates for both groups (mean 3D wear approximately 0.25 mm/year) consistent with the bedding-in phenomena. At most recent radiographic follow-up (two or three years), there was a statistically significant although modest difference in wear rates between the two groups with a 2D and 3D wear rate of 0.14±0.10 mm/yr and 0.15±0.02 mm/yr respectively for conventional polyethylene compared to 0.09±0.04 mm/yr and 0.11±0.02 mm/yr for cross-linked polyethylene. This represented a 32 and 29 percent reduction in 2D and 3D wear rates respectively with cross-linked polyethylene. Conclusion: At early follow-up, there were no clinical differences. There was a modest wear reduction (approximately 30%) with highly cross-linked polyethylene, considerably less than expected based on laboratory testing. Longer follow-up, after the bedding-in process is completed, is required to demonstrate the wear reduction afforded by highly cross-linked polyethylene

Aims. Limited implant survival due to aseptic cup loosening is most commonly responsible for revision total hip arthroplasty (THA). Advances in implant designs and materials have been crucial in addressing those challenges. Vitamin E-infused highly cross-linked polyethylene (VEPE) promises strong wear resistance, high oxidative stability, and superior mechanical strength. Although VEPE monoblock cups have shown good mid-term performance and excellent wear patterns, long-term results remain unclear. This study evaluated migration and wear patterns and clinical and radiological outcomes at a minimum of ten years’ follow-up. Methods. This prospective observational study investigated 101 cases of primary THA over a mean duration of 129 months (120 to 149). At last follow-up, 57 cases with complete clinical and radiological outcomes were evaluated. In all cases, the acetabular component comprised an uncemented titanium particle-coated VEPE monoblock cup. Patients were assessed clinically and radiologically using the Harris Hip Score, visual analogue scale (pain and satisfaction), and an anteroposterior radiograph. Cup migration and polyethylene wear were measured using Einzel-Bild-Röntgen-Analyze software. All complications and associated treatments were documented until final follow-up. Results. Clinical assessment showed persistent major improvement in all scores. On radiological assessment, only one case showed a lucent line (without symptoms). At last follow-up, wear and migration were below the critical thresholds. No cup-related revisions were needed, indicating an outstanding survival rate of 100%. Conclusion. Isoelastic VEPE cups offer high success rates and may prevent osteolysis, aseptic loosening, and the need for revision surgeries in the long term. However, longer follow-up is needed to validate our findings and confirm the advantages offered by this cup. Cite this article: Bone Jt Open 2024;5(10):825–831

Introduction and Aims: Modular acetabular designs are widely used in THA procedures and now accommodate highly cross-linked polyethylene liners. However, polymer processing influences material properties, including a decrease in resistance to crack propagation. This study comparatively evaluated locking mechanism integrity of three modular acetabular designs, which employ conventional and highly cross-linked polyethylene liners. Method: Locking mechanism integrity was established for both conventional and highly cross-linked polymers through push-out (n=3) and lever-out (n=3) testing of fully seated liners. When possible, liners were reinserted and forcibly disassembled. Results: The push out and lever out strengths measured for the highly cross-linked polyethylene acetabular liners in this study indicated that short-term disassociation of these components is no more likely than that for the conventional polyethylene liners of each design. Student t-tests confirmed the null hypothesis. In addition, when compared to the strengths of clinically successful modular designs none of the systems evaluated presents any great risk of short-term disassociation. Significant reductions in locking mechanism strength after liner reinsertion were also noted for both polymers. Conclusion: Short-term static disassociation failure of highly cross-linked polyethylene liners were found to be equivalent to conventional polyethylene liners. Given their touted improvement in wear reduction, they would appear to be a reasonable alternative in the young patient requiring THA. Secondarily, neither conventional nor highly cross-linked polymers should be re-inserted for any reason at the time of surgery

Highly cross-linked polyethylene (HXLPE) is now a common used bearing surface in total hip arthroplasty. Current studies report superior wear rates with the use of HXLPE in total hip arthroplasty. However, there are few studies to support its long term use. The aim of this study is to measure the long term wear of HXLPE and evaluate patient satisfaction at more than 10 years follow up. 44 total hip arthroplasties were performed through a direct lateral approach by a single surgeon. All patients received the same uncemented acetabular component, mean liner thickness was 6.91mm (SD= 0.68). 16 of the femur components were cemented. Outcomes analysed include wear rates, osteolysis, revision rates, SF12 and Oxford hip scores. Wear rate was calculated using computer software (Polyware®) using edge detection software. Mean age at surgery was 58.9 years (SD= 11.67). The mean follow up was 11.3 years (SD= 1.19). There was no evidence of osteolysis and none had undergone revision surgery. Mean two dimensional wear was 0.38mm (SD= 0.25) and mean wear rate per year was 0.03mm (SD= 0.02, range 0.009 to 0.078). Oxford hip score at last follow up indicated satisfactory joint function (mean= 42 SD= 6.2). Our results support the use of highly cross-linked polyethylene in primary total hip replacements. The absence of osteolysis and need for revision surgery over a mean of 11.3 years is very encouraging

Press-fit fixation of uncemented acetabular components is increasingly being used for total hip replacement (THR) surgery. This study was aimed to analyse the survival of an established, un-cemented flexible metal backed cup with non-highly cross-linked polyethylene in primary and simple revision THR. We assessed the outcome of 1703 consecutive cementless elastic acetabular cups (Atlas, FH France) with non-highly cross-linked polyethylene (GUR1030) in total hip replacement surgery. There were 1582 patients (513 males and 1079 females) with mean age of 74 years (36–97 years). Seventeen senior operating surgeons accounted for 88.5% of cases from a single arthroplasty unit. Survival analysis was calculated using the Kaplan Meier Estimator. At 184 months post surgery the survivorship was 92.4% (95% CI 88.3–94.7) with cup revision for any cause as an endpoint. Three patients died within first month of surgery and 268 patients (17.13%) died due to unrelated causes. Overall, 59 patients had revisions (3.5%), Thirty eight patients (2.3%) were due to acetabular causes such as: aseptic loosening in 6 patients (0.35%); hip instability in 13 patients (0.76%); and deep infection in 11 patients (0.64%). We believe the cementless elastic acetabular cup on in total hip replacement is tolerant of technique and patient variation and continues to give excellent long-term results and its continued widespread use can be recommended