Summary. Fifteen irradiated, vitamin E-diffused UHMWPE retrievals with up to three years in vivo service showed no appreciable oxidation, nor change in material properties from a never-implanted liner, and showed a 94% decrease in free radical content. Introduction. Radiation cross-linking, used to improve wear resistance of ultra-high molecular weight polyethylene (UHMWPE) bearings used in total joint arthroplasty, generates residual free radicals which are the precursors to oxidative embrittlement. First generation materials adopted thermal treatments to eliminate or reduce free radical content, but came with compromises in reduced mechanical properties or insufficient stabilization. A second generation alternative method infuses an antioxidant, vitamin E, into irradiated UHMWPE to stabilise free radicals while maintaining fatigue strength. In vitro studies predict excellent oxidation and wear resistance in vitamin E-stabilised bearings, but the long-term in vivo oxidation behavior, influenced by lipid absorption and cyclic loading, remains largely unknown. Our aim was to investigate in vivo changes in UHMWPE surgically-retrieved explants that were radiation cross-linked and stabilised by vitamin E. Patients & Methods. Fifteen surgically-retrieved irradiated, vitamin E-diffused and inert-gamma sterilised bearings (E1™, Biomet, Inc., Warsaw IN) with in vivo durations ranging from 3 days to 36.6 months were analyzed at unloaded rim/eminence and the articular surface along with one never-implanted component. Total lifetime of components was summed as shelf storage prior to implantation, in vivo duration and ex vivo duration in air. Fourier Transform Infrared Spectroscopy (FTIR) was used to measure carbonyl index (CI; per ASTM F2102-01ε1) both before and after 16 hour hexane extraction to. Extracted thin films were also reacted with nitric oxide to quantify hydroperoxides, an intermediate oxidation product associated with oxidation potential. Cross-link density was calculated from gravimetric swelling analysis per ASTM F2214. Crystallinity measurements were performed regionally using differential scanning calorimetry (DSC). Free radical content was measured by electron spin resonance (Memphis, TN). Results. Irradiated and vitamin E-diffused retrievals showed scratching at the articular surface, but retained machining marks up to three years in vivo, indicative of no measurable wear. Retrievals showed no significant oxidation at the time of surgical removal with maximum post-hexane carbonyl indices in the barely detectable range (MCI=0.029–0.154), located at the surface of retrievals. Ex vivo oxidation was not observed after 18 months of aging in air at room temperature. There was no increase in hydroperoxides (never-implanted HI=0.62±0.04; retrieval HI= 0.62±0.04), nor change in cross-link density (never-implanted: 0.275±0.015 mol/dm. 3. ; retrieval: 0.295±0.016 mol/dm. 3. ) or crystallinity (never-implanted: 58.3±1.4%; retrievals: 60.0±3.5%). Lipid penetration increased with time, showing a higher rate of diffusion in loaded regions. Free radical content was observed to decay with increasing in vivo duration (R. 2. =0.44; p<0.05), and by one order of magnitude (94%) by 36.6 months. A stronger negative correlation (R. 2. =0.65) was observed between the total lifetime of the liner and free radical content. Discussion/Conclusion. The free-radical scavenging activity of the vitamin E appears to successfully prevent both in vivo and ex vivo oxidation for short durations. Without an increase in hydroperoxides, the oxidation cascade initiated by radiation-induced and lipid-derived free radicals appears to have been halted. Retrievals also gave no indication of wear in this timeframe, similar to improved wear resistance seen in first generation materials. Continued monitoring will be necessary at longer implant durations

NHS Greater Glasgow & Clyde has six hospitals that provide an inpatient trauma service, but only two have facilities to receive patients by helicopter. The Southern General Hospital contains regional Neurosurgical and Spinal Injuries services and attracts the majority of major trauma delivered by helicopter. This study explores the impact that Emergency Medical Retrieval (EMRS) and Air Ambulance services have on the Trauma & Orthopaedic department at our Hospital. We examined the period 1. st. January 2010 to 31. st. December 2010 identifying Trauma & Orthopaedic admissions brought to our hospital by the Emergency Medical Retrieval and Air Ambulance services. These patients were identified from records kept by our Trauma Nurse Practitioner and an additional search of the hospital admissions database. Details of the admissions were extracted from this database, clinical records and various electronic patient records. Patients admitted to other departments were excluded from the study. 48 admissions (30 male, 18 female) were identified. Age ranged from 16-87 years. 16 patients had multiple injuries. 8 required High-Dependency or Intensive Care admission and there was 1 death in our cohort. 21 patients required surgery. In total, these patients required approximately 52.5 hours of operative time. These patients accounted for 373 inpatient days with an average hospital stay of 7.7 days (1-36 days). In addition, 25 patients have required a total of 35 outpatient appointments to date. This study quantifies the significant impact on inpatient and outpatient Trauma & Orthopaedic services from helicopter derived admissions. Some patients admitted under Neurosurgery and Spinal Injuries also undergo surgery, but were not included in the study, representing an additional workload. We believe this study supports an argument for additional investment in this growing trauma service, especially given the recent expansion of EMRS to cover the whole of Scotland

Dual mobility (DM) total hip replacements (THRs) were introduced to reduce dislocation risk, which is the most common cause of early revision. Although DM THRs have shown good overall survivorship and low dislocation rates, the mechanisms which describe how these bearings function in-vivo are not fully understood. Therefore, the study aim was to comprehensively assess retrieved DM polyethylene liners for signs of damage using visual inspection and semi-quantitative geometric assessment methods.

Retrieved DM liners (n=18) were visually inspected for the presence of surface damage, whereby the internal and external surfaces were independently assigned a score of one (present) or zero (not present) for seven damage modes. The severity of damage was not assessed. The material composition of embedded debris was characterised using energy-dispersive x-ray analysis (EDX). Additionally, each liner was geometrically assessed for signs of wear/deformation [1].

Scratching and pitting were the most common damage modes on either surface. Additionally, burnishing was observed on 50% of the internal surfaces and embedded debris was identified on 67% of the external surfaces. EDX analysis of the debris identified several materials including titanium, cobalt-chrome, iron, and tantalum. Geometric analysis demonstrated highly variable damage patterns across the liners.

The incidence of burnishing was three times greater for the internal surfaces, suggesting that this acts as the primary articulation site. The external surfaces sustained more observable damage as evidenced by a higher incidence of embedded debris, abrasion, delamination, and deformation. In conjunction with the highly variable damage patterns observed, these results suggest that DM kinematics are complex and may be influenced by several factors (e.g., soft tissue fibrosis, patient activities) and thus further investigation is warranted.

Background. Skeletal stem cells can be combined with human allograft, and impacted to produce a mechanically stable living bone composite. This strategy has been used for the treatment of femoral head avascular necrosis, and has been translated to four patients, of which three remain asymptomatic at up to three year follow-up. In one patient collapse occurred in both hips due to widely distributed and advanced AVN disease, necessitating bilateral hip arthroplasty. However this has provided the opportunity to retrieve the femoral heads and analyse human tissue engineered bone. Aims. Analysis of retrieved human tissue-engineered bone in conjunction with clinical follow-up of this translational case series. Methods. A parallel in vitro culture of the implanted cell-graft constructs was set up at the time of surgery, with serial cell viability stains performed up to six weeks. Patient follow-up was by serial clinical and radiological examination. Tissue engineered bone from the two retrieved femoral heads was analysed histologically by Alcian blue & Sirius red stain and bi-refringence, by micro computed tomography (microCT) for both bone density and morphology, and by compression testing for mechanical strength. Normal trabecular and cortical bone from the femoral heads was used as controls. Results. Parallel in vitro analysis demonstrated sustained cell growth and viability on the allograft. Histologically, the retrieved tissue engineered specimens demonstrated a mature trabecular micro-architecture and organization identical to normal trabecular bone. MicroCT revealed trabecular morphology within the tissue-engineered bone, with bone density of 1400 Grey scale units (compared to 1200 for natural trabecular bone and 1800 for cortical bone). Axial compression testing showed no difference in strength between engineered and trabecular bone. Conclusions. Widespread residual necrosis in the femoral heads of one patient resulted in collapse requiring hip arthroplasty, but analysis of the tissue engineered bone sections has demonstrated the translational potential of a living bone composite to restore both the biological and mechanical characteristics of bone defects. Clinical follow-up shows this to be an effective new treatment for focal early stage avascular necrosis of the femoral head, and this unique retrieval analysis data confirms the potential of cell-based strategies for clinical treatment of bone defects

Summary Statement. This study assesses oxidation, mechanical behavior and revision reasons of 2. nd. generation HXLPE used in total hip and knee arthroplasty. While oxidation was low for both X3 and E1 HXLPEs, oxidative regional variations were detected in the sequentially annealed cohort. Introduction. First generation highly crosslinked polyethylenes (HXPLEs) have proven successful in lowering both penetration and osteolysis rates. However, 1. st. generation annealing and remelting thermal stabilization have been associated with in vivo oxidation or reduced mechanical properties. Thus, 2. nd. generation HXLPEs were developed to improve oxidative stability while still maintaining material properties. Little is known about the in vivo clinical failure modes of these 2. nd. generation HLXPEs. The purpose of this study was to assess the revision reasons, wear, oxidative stability, and mechanical behavior of retrieved sequentially annealed Vitamin E diffused HXLPE in THA and TKA. Methods. 251 2. nd. Generation HXLPE hip and knee components were consecutively retrieved during revision surgeries and continuously analyzed in a prospective, IRB approved, multicenter study. 123 acetabular liners (Implanted 1.2y; Range 0–5.0y) and 117 tibial inserts (Implanted 1.6y; Range 0–5.8y) were highly crosslinked and annealed in 3 sequential steps (X3). Five acetabular liners (Implanted 0.6y; Range 0–2.0y) and six tibial inserts (Implanted 1.3y; Range 0.5–1.8y) were diffused with Vitamin E (E1). Patient information was collected from medical records. Linear penetration of liners was measured using a calibrated digital micrometer (accuracy: 0.001 mm). Surface damage of tibial components was assessed using the Hood method. Thin sections were taken from the acetabular liners (along the superior/inferior axis) and the tibial components (along the medial condyle and central spine) for oxidation analysis and analyzed according to ASTM 2102. Mechanical behavior was assessed via the small punch test (ASTM 2183). Results. The liners and tibial components fabricated from both HXLPEs were revised predominantly for loosening, instability, and infection. The average penetration rate for the Sequentially Annealed group was low (PR=0.045mm/yr). Pitting, scratching and burnishing were the predominant damage mechanisms of the tibial inserts within both material groups, with no evidence of delamination. Oxidation indices were low (Mean OI≤0.3) and similar between liners and inserts of the Sequentially Annealed components at the bearing and backside surface (p≥0.15). Oxidation was positively correlated with implantation time at the bearing surface of the Sequentially Annealed groups (Rho>0.29, p<0.005). The Ultimate Load of the Sequentially Annealed acetabular liners was statistically higher than the tibial components (p<0.001), however the mean difference was minimal (∼6N). Discussion. This study evaluated the properties of 2. nd. generation HXLPEs used in THA and TKA. Sequentially Annealed liners had penetration rates comparable with 1. st. generation HXLPEs. While oxidation was low for both sequentially annealed and Vitamin E HXLPEs, we were able to detect regional variations in the oxidative in the sequentially annealed cohort. Longer-term retrievals are necessary to fully assess the oxidative stability of Vitamin E diffused HXLPE used in TKA and THA

This study reports the mid-term results of a large bearing hybrid metal on metal total hip replacement (MOMHTHR) in 199 hips (185 patients) with mean follow up of 62 months. Clinical, radiological outcome, metal ion levels and retrieval analysis were performed. Seventeen patients (8.6%) had undergone revision, and a further fourteen are awaiting surgery (defined in combination as failures). Twenty one (68%) failures were females. All revisions and ten (71%) of those awaiting revision were symptomatic. Twenty four failures (86%) showed progressive radiological changes. Fourteen revision cases showed evidence of adverse reactions to metal debris (ARMD). The failure cohort had significantly higher whole blood cobalt ion levels (p=0.001), but no significant difference in cup size (p=0.77), inclination (p=0.38) or cup version (p=0.12) in comparison to the non revised cohort. Female gender was associated with an increased risk of failure (chi squared p=0.04). Multifactorial analysis demonstrated isolated raised Co levels in the absence of either symptoms or XR changes was not predictive of failure (p=0.675). However both the presence of pain (p<0.001) and XR changes (p<0.001) in isolation were both significant predictors of failure. Wear analysis (n=5) demonstrated increased wear at the trunnion/head interface (mean out of roundness measurements of 34.5 microns +/−13.3 (+/−2SD, normal range 8-10 microns) with normal levels of wear at the articulating surfaces. There was evidence of corrosion at the proximal and distal stem surfaces. The cumulative survival rate, with revision for any reason was 92.4% (95%CI: 87.4-95.4) at 5 years. Including those awaiting surgery, the revision rate would be 15.1% with cumulative survival at 5 years of 89.6% (95% CI: 83.9-93.4). This MOMHTHR series has demonstrated unacceptable high failure rates with evidence of high wear at the head/trunnion interface and passive corrosion to the stem surface. This raises concern with the use of large heads on conventional 12/14 tapers. Female gender was an independent risk factor of failure. Metal ion levels remain a useful aspect of the investigation work up but in isolation are not predictive of failure

Knee arthroplasty with a rotating hinge knee (RHK) prosthesis has become an important clinical treatment option for knee revisions and primary patients with severe varus or valgus deformities and instable ligaments. The rotational axle constraints the anterior-posterior shear and varus-valgus moments, but currently used polyethylene bushings may fail in the mid-term due to insufficient creep and wear resistance of the material. Due to that carbon-fibre-reinforced (CFR) PEEK as an alternativ bushing material with enhanced creep, wear and fatigue behaviour has been introduced in a RHK design [Grupp 2011, Giurea 2014]. The objective of our study was to compare results from the pre-clinical biotribological characterisation to ex vivo findings on a series of retrieved implants.

In vitro wear simulation according to ISO 14243-1 was performed on rotating hinge knee devices (EnduRo® Aesculap, Germany) made out of cobalt-chromium and of a ZrN multi-layer ceramic coating for 5 million cycles. The mobile gliding surfaces were made out of polyethylene (GUR 1020, β-irradiated 30 ± 2 kGy). For the bushings of the rotational and flexion axles and the flanges a new bearing material based on CFR-PEEK with 30% PAN fiber content was used.

Analysis of 12 retrieved EnduRo^® RHK systems in cobalt-chromium and ZrN multi-layer in regard to

-

loosening torques in comparison with initial fastening torques

with a focus on the four CFR-PEEK components integrated in the EnduRo^® RHK design.

For the rotating hinge knee design with flexion bushing and flanges out of CFR-PEEK the volumetric wear rates were 2.3 ± 0.48 mm³/million cycles (cobalt-chromium) and 0.21 ± 0.02 mm³/million cycles (ZrN multi-layer), a 10.9-fold reduction (p = 0.0016). The UHMWPE and CFR-PEEK particles were comparable in size and morphology and predominantly in submicron size [5]. The biological response to representative sub-micron sized CFR-PEEK particles has been demonstrated in vivo based on the leucoyte-endothelian-cell interactions in the synovia of a murine intra-articular knee model by Utzschneider 2010. Schwiesau 2013 extracted the frequency of daily activities in hip and knee replacement patients from literature and estimated an average of 1.76 million gait cycles per year. Thus, the 5 million cycles of in vitro wear testing reflect a mean in vivo service life of 2.9 years, which fits to the time in vivo of 12–60 months of the retrieved RHK devices. The in vitro surface articulation pattern of the wear simulation tests are comparable to findings on retrieved CFR-PEEK components for both types of articulations – cobalt-chromium and ZrN multi-layer coating.

For the rotating hinge knee design the findings on retrieved implants demonstrate the high suitability of CFR-PEEK as a biomaterial for highly loaded bearings, such as RHK bushings and flanges in articulation to cobalt-chromium and to a ZrN multi-layer coating.

We have examined 26 retrieved, failed titanium-alloy femoral stems. The clinical details, radiological appearances and the histology of the surrounding soft tissues in each patient were also investigated.

The stems were predominantly of the flanged design and had a characteristic pattern of wear. A review of the radiographs showed a series of changes, progressive with time. The first was lateral debonding with subsidence of the stem. This was followed by calcar resorption and fragmentation or fracture of the cement. Finally, osteolysis was seen, starting with a radiolucency at the cement-bone interface and progressing to endosteal cavitation.

Three histological appearances were noted: granulomatous, necrobiotic and necrotic. We suggest that an unknown factor, possibly related to the design of the stem, caused it to move early. After this, micromovement at the cement-stem interface led to the generation of particulate debris and fracture of the cement. A soft-tissue reaction to the debris resulted in osteolysis and failure of fixation of the prostheses.

Objectives. To assess the structure and extracellular matrix molecule expression of osteogenic cell sheets created via culture in medium with both dexamethasone (Dex) and ascorbic acid phosphate (AscP) compared either Dex or AscP alone. Methods. Osteogenic cell sheets were prepared by culturing rat bone marrow stromal cells in a minimal essential medium (MEM), MEM with AscP, MEM with Dex, and MEM with Dex and AscP (Dex/AscP). The cell number and messenger (m)RNA expression were assessed in vitro, and the appearance of the cell sheets was observed after mechanical retrieval using a scraper. β-tricalcium phosphate (β-TCP) was then wrapped with the cell sheets from the four different groups and subcutaneously implanted into rats. Results. After mechanical retrieval, the osteogenic cell sheets from the MEM, MEM with AscP, and MEM with Dex groups appeared to be fragmented or incomplete structures. The cell sheets cultured with Dex/AscP remained intact after mechanical retrieval, without any identifiable tears. Culture with Dex/AscP increased the mRNA and protein expression of extracellular matrix proteins and cell number compared with those of the other three groups. More bridging bone formation was observed after transplantation of the β-TCP scaffold wrapped with cell sheets cultured with Dex/AscP, than in the other groups. Conclusions. These results suggest that culture with Dex/AscP improves the mechanical integrity of the osteogenic cell sheets, allowing retrieval of the confluent cells in a single cell sheet structure. This method may be beneficial when applied in cases of difficult tissue reconstruction, such as nonunion, bone defects, and osteonecrosis. Cite this article: M. Akahane, T. Shimizu, T. Kira, T. Onishi, Y. Uchihara, T. Imamura, Y. Tanaka. Culturing bone marrow cells with dexamethasone and ascorbic acid improves osteogenic cell sheet structure. Bone Joint Res 2016;5:569–576. DOI: 10.1302/2046-3758.511.BJR-2016-0013.R1

Objectives. The Attune total knee arthroplasty (TKA) has been used in over 600 000 patients worldwide. Registry data show good clinical outcome; however, concerns over the cement-tibial interface have been reported. We used retrieval analysis to give further insight into this controversial topic. Methods. We examined 12 titanium (Ti) PFC Sigma implants, eight cobalt-chromium (CoCr) PFC Sigma implants, eight cobalt-chromium PFC Sigma rotating platform (RP) implants, and 11 Attune implants. We used a peer-reviewed digital imaging method to quantify the amount of cement attached to the backside of each tibial tray. We then measured: 1) the size of tibial tray thickness, tray projections, peripheral lips, and undercuts; and 2) surface roughness (Ra) on the backside and keel of the trays. Statistical analyses were performed to investigate differences between the two designs. Results. There was no evidence of cement attachment on any of the 11 Attune trays examined. There were significant differences between Ti and CoCr PFC Sigma implants and Attune designs (p < 0.05); however, there was no significant difference between CoCr PFC Sigma RP and Attune designs (p > 0.05). There were significant differences in the design features between the investigated designs (p < 0.05). Conclusion. The majority of the earliest PFC Sigma designs showed evidence of cement, while all of the retrieved Attune trays and the majority of the RP PFC trays in this study had no cement attached. This may be attributable to the design differences of these implants, in particular in relation to the cement pockets. Our results may help explain a controversial aspect related to cement attachment in a recently introduced TKA design. Cite this article: A. Cerquiglini, J. Henckel, H. Hothi, P. Allen, J. Lewis, A. Eskelinen, J. Skinner, M. T. Hirschmann, A. J. Hart. Analysis of the Attune tibial tray backside: A comparative retrieval study. Bone Joint Res 2019;8:136–145. DOI: 10.1302/2046-3758.83.BJJ-2018-0102.R2

In 2020 almost 90% of femoral heads for total hip implants in Germany were made of ceramic. Nevertheless, the cellular interactions and abrasion mechanisms in vivo have not been fully understood until now. Metal transfer from the head-neck taper connection, occurring as smear or large-area deposit, negatively influences the surface quality of the articulating bearing. In order to prevent metal transfer, damage patterns of 40 Biolox delta ceramic retrievals with CoC and CoPE bearings were analysed. A classification of damage type and severity for each component (n=40) was done according to an established scoring system. To investigate the physical properties, the surface quality was measured using confocal microscopy, quantitative analysis of phase composition were performed by Raman spectroscopy and qualitative analysis of metal traces was done by scanning electron microscopy (SEM) with energy dispersive X-ray spectroscopy (EDX). The periprosthetic tissue was analysed for abrasion particles with SEM and EDX. Both bearing types show different damage patterns. Dotted/ drizzled metal smears were identified in 82 % of CoC (n=16) and 96 % of CoPE (n=24) bearings. Most traces on the ceramic heads were identified in the proximal area while they were observed predominantly in the distal area for the ceramic inlays. The identified marks are similar to those of metallic bearings. Metallic smears lead to an increase of up to 30 % in the monoclinic crystalline phase of the ceramic. The roughness increases by up to six times to Ra=48 nm. Ceramic and metallic wear particles from the articulating surfaces or head neck taper junctions were found in the periprosthetic tissue. Damage patterns on CoC hip implants seem to be similar to those of metallic implants. More detailed analysis of CoC implants are needed to understand the described damage patterns and provide advice for prevention

Summary. Four highly cross-linked UHWMPEs except vitamin E-stabilised explants. Introduction. The development of both first and second generation highly cross-linked material focused on stabilizing radiation-induced free radicals as the sole precursor to oxidative degradation; however, secondary in vivo oxidation mechanisms have been identified in both conventional and highly cross-linked UHMWPE, induced by absorbed lipids and cyclic mechanical load. Retrieval studies are reporting in vivo oxidation highly cross-linked retrievals with up to ten year in vivo durations. Preclinical aging tests did not predict these in vivo material changes. With only a decade of these materials in clinical use, retrieval studies are limited to mid-term follow-up. In vitro studies face a challenge in effectively replicating the precise in vivo conditions that lead to this loss of oxidation resistance. In this study, we bypass replicating these in vivo variables by examining surgically-retrieved components, thereby testing material that has been affectively “pre-conditioned” by their in vivo service. After a preliminary post-operative analysis, we subjected retrievals to accelerated aging tests in order to predict the extent to which their oxidative stability had been uniquely compromised in vivo. Patients & Methods. Twenty-four highly cross-linked retrievals of four manufacturing methods (n=6 each of Longevity™, Prolong™, X3™ and E1™) and in vivo durations (1–4 years) were analyzed post-operatively and after accelerated aging (70°C, 5atm O. 2. for 2 weeks; ASTM F2003). Never-implanted components (n=1) of each material type were also aged. Infrared microscopy was used to evaluate lipid absorption, oxidation (per ASTM F2102-01ε1) and hydroperoxide levels after 16 hrs of nitric oxide staining for oxidation potential, and gravimetric swelling analysis assessed cross-link density (ASTM F2214). Results. All retrievals contained absorbed lipids penetrating below both loaded (penetration depth=1.3 ± 0.5 mm) and unloaded (0.6 ± 0.2 mm) surfaces. Each material type subset contained retrievals with and without detectable oxidation after in vivo service (Max OI=0.01–0.94). After aging, all post-irradiation thermally-treated, highly cross-linked retrievals, regardless of initial lipid levels or oxidation, showed oxidative degradation, demonstrated by subsurface oxidative peaks (MOI=0.30–2.63), increased hydroperoxides (3–5X), and decreased cross-link density (−34–90%). In contrast, vitamin E-stabilised retrievals showed below MOI<0.2 with no significant loss of cross-link density. Never-implanted controls for each material type showed no oxidative changes after accelerated aging. Discussion/Conclusion. Accelerating aging after in vivo service has shown oxidative instability characterised by high oxidation and material property loss in the three highly cross-linked materials without an incorporated antioxidant. This oxidative degradation took place regardless of post-operative oxidation levels, indicating that even without detectable oxidation the material had undergone changes during in vivo service, as compared to the lack of oxidative response in never-implanted controls. These findings also suggest that the presence of an antioxidant may be able to slow down and/or stabilise in vivo mechanisms compromising long-term oxidative stability and increase the longevity of highly cross-linked UHMWPE materials

Metal-on-metal hip resurfacing prostheses are a relatively recent intervention for relieving the symptoms of common musculoskeletal diseases such as osteoarthritis. While some short term clinical studies have offered positive results, in a minority of cases there is a recognised issue of femoral fracture, which commonly occurs in the first few months following the operation. This problem has been explained by a surgeon's learning curve and notching of the femur but, to date, studies of explanted early fracture components have been limited. Tribological analysis was carried out on fourteen retrieved femoral components of which twelve were revised after femoral fracture and two for avascular necrosis (AVN). Eight samples were Durom (Zimmer, Indiana, USA) devices and six were Articular Surface Replacements (ASR, DePuy, Leeds, United Kingdom). One AVN retrieval was a Durom, the other an ASR. The mean time to fracture was 3.4 months. The AVNs were retrieved after 16 months (Durom) and 38 months (ASR). Volumetric wear rates were determined using a Mitutoyo Legex 322 co-ordinate measuring machine (scanning accuracy within 1 micron) and a bespoke computer program. The method was validated against gravimetric calculations for volumetric wear using a sample femoral head that was artificially worn in vitro. At 5mm3, 10mm3, and 15mm3 of material removal, the method was accurate to within 0.5mm3. Surface roughness data was collected using a Zygo NewView500 interferometer (resolution 1nm). Mean wear rates of 17.74mm3/year were measured from the fracture components. Wear rates for the AVN retrievals were 0.43mm3/year and 3.45mm3/year. Mean roughness values of the fracture retrievals (PV = 0.754nm, RMS = 0.027nm) were similar to the AVNs (PV = 0.621nm, RMS = 0.030nm), though the AVNs had been in vivo for significantly longer. Theoretical lubrication calculations were carried out which found that in both AVN retrievals and in seven of the twelve cases of femoral fracture the roughening was sufficient to change the lubrication regime from fluid film to mixed. Three of these surfaces were bordering on the boundary lubrication regime. The results show that even before the femoral fracture, wear rates and roughness values were high and the implants were performing poorly

Summary. Sequentially irradiated and annealed UHMWPE hip and knee retrievals showed subsurface in vivo oxidation in both the articular surface and unloaded surfaces, while three of four never-implanted shelf stored liners had oxidation in the bulk. Introduction. Highly cross-linked polyethylene was developed to improve the wear resistance of UHMWPE bearing surfaces in total hip arthroplasty. First generation irradiated and annealed polyethylene showed high oxidation in vivo, largely attributed to only the partial-quenching of free radicals, along with additional radicals generated during terminal gamma sterilization. A second generation, three-step sequential irradiation and annealing method was advanced with the promise of better oxidative stability and improved mechanical properties. We hypothesised that without the complete elimination of free radicals combined with gas plasma sterilization requiring oxygen-permeable packaging, that this second generation material would be prone to shelf-oxidation in addition to in vivo oxidation. Patients & Methods. Fifty surgically-retrieved sequentially irradiated and annealed, gas plasma-sterilised UHWMPE acetabular liners and tibial bearings (X3™, Stryker, Mahwah, NJ), with in vivo durations of 0.5–73 months, were analyzed at their articular surface and an unloaded surface, along with four never implanted acetabular liners. Infrared microscopy was used to evaluate lipid absorption, oxidation (per ASTM F2102-01ε1) and hydroperoxide levels after nitric oxide staining. Gravimetric swelling analysis assessed cross-link density (per ASTM F2214), and crystallinity measurements were performed using differential scanning calorimetry. Results. There was detectable oxidation (OI > 0.1) in 37 of the 50 components with as little as 2 weeks of in vivo service. Maximum oxidation values averaged OI = 0.30 ± 0.30 (range = 0.03–1.59). Oxidation profiles were predominantly characterised by subsurface oxidation peaks approximately 1–2 mm below the surface, in both the articular surface and rim, along with a pattern of embrittlement induced white banding in four and six year liners. Three short in vivo duration liners (0.1–15.5 month) showed oxidation and degradation of material properties throughout the bulk. Three of four never-implanted liners, with up to five years shelf storage, also showed bulk oxidation (Max OI ≤ 1.5), loss of cross-link density and increased crystallinity. Discussion/Conclusion. High levels of detectable oxidation, subsurface oxidation peaks, and white banding were all identified in sequentially irradiated and annealed UHMWPE retrievals with short in vivo durations. These results raise concerns about the long-term clinical performance of these materials. Oxidation measured in shelf-stored, never implanted liners also raises concerns that liners may already be oxidatively compromised before being implanted into patients. Due to gas plasma sterilization methods, these free-radical containing liners are packaged and stored in air, likely resulting in a pre-implantation oxidation effect similar to that historically reported in gamma-in-air sterilised UHMWPE. Longer-term retrievals are needed to better understand the progress of these in vivo changes and whether or not it will compromise the longevity of the implants

Summary Statement. A new 28mm-diameter ceramic-on-ceramic (COC) acetabular bearing couple (Biomet Orthopedics) showed extremely low wear, even under adverse microseparation conditions∗. The wear results are similar or more favorable than those reported for clinical retrievals and wear testing of similar ceramic bearings. Introduction. A new acetabular shell and ceramic insert design (Biomet) incorporates features to help prevent malalignment during implantation, while still providing secure fixation within the acetabular shell. The incorporation of Biolox. ®. Delta (zirconia toughened alumina, CeramTec) material should provide improved wear resistance over pure alumina ceramics. The goal of this study is to evaluate the wear durability of this system for standard and microseparation testing. Materials & Methods. The 28 mm diameter ceramic heads and inserts (CeramTec) were seated on taper spigots and within acetabular shells (Biomet), respectively. Six sets of parts were tested for 5M cycles of standard hip wear testing (ISO 14242) and an additional six sets of parts for 2M cycles of microseparation testing. The microseparation testing protocol included a steep cup angle (60° in-vivo), side load, and reduced axial load to induce head-liner separation. The lateral displacement was increased from 0.5mm, to 1mm, and then to 2mm in order to replicate wear features observed in extreme situations of clinical retrievals. [1]. The parts were weighed (gravimetric wear rates) and photographed throughout the test. SEM, transformation, and wear debris analyses were completed. Results. The steady-state wear rate throughout standard testing was 0.0094 +/− 0.0029 mm. 3. /10. 6. cycles (+/-95% CI). The initial 0.5mm microseparation distance (0–1M cycles) showed no signs of wear. Most heads showed wear stripes after increasing to 1.0mm (1–1.5M cycles), and then all test parts showed stripes after increasing to 2mm. The increased visibility in wear stripes correlated with an increased level of measured wear. For the 2mm separation-distance testing interval, the wear rate was 0.178 +/− 0.052mm. 3. /10. 6. cycles. Discussion/Conclusion. The lack of wear stripes during 0.5mm of microseparation is an indication of the strength of the implants. A distance of 1–2mm is an extreme level of microseparation and the 60° in-vivo cup inclination created an even worse-case situation for wear; however, the implants showed excellent mechanical strength and low wear rates. SEM and transformation analyses showed minimal wear and evidence of stress-induced ceramic toughening. Microseparation testing at another lab . [2]. has shown a similarly low wear rate (0.5 mm. 3. /10. 6. cycles) for Biolox. ®. Delta ceramic, with Biolox. ®. Forte (alumina ceramic, without zirconia) showing a considerably higher wear rate (6.3mm. 3. /10. 6. cycles). The standard testing wear rate (0.0094+/-0.0029 mm. 3. /10. 6. cycles) was much lower than the average wear rate (0.69+/-0.63 mm. 3. /10. 6. cycles) of several COC implant retrievals by Walter . [1]. The 28mm steady-state wear rate of this test is better than or equal to the wear rate (0.0101 mm. 3. /10. 6. cycles) observed in other 28mm COC systems.∗∗. ∗Ceramic-on-Ceramic articulation is not cleared for use in the United States. ∗∗Laboratory results are not necessarily indicative of clinical performance

Osteoarthritis (OA) is a degenerative disease with a strong inflammatory component. Intra-articular (IA) injections of mesenchymal stem cells (MSCs) modulate local inflammation, although the lack of engraftment suggests that they undergo apoptosis. The aim of this study is to investigate the fate of IA-delivered MSCs in an animal model of OA and to assess the role of apoptosis in vitro. Collagenase-induced OA (CIOA) was performed on C57BL/6 mice and 2×10∧5 GFP+ MSCs were IA-injected in the animals. 3 days later, knee joints were digested into a single-cell suspension and MSCs retrieved by cell sorting. Conditioned medium (CM) of retrieved cells was tested on murine macrophages and cytokine secretion was measured. Apoptosis of MSCs was induced in vitro with staurosporine (STS) and evaluated by Annexin V/Sytox Blue staining; activation of caspases was measured by FLICA assays. Murine lymphocytes were cocultured with apoptotic MSCs and their proliferation measured by quantification of Cell Trace Violet. 1.63% of injected cells were retrieved and proliferated in culture. Their CM significantly modulated activation of macrophages, with greater effects from OA-induced MSCs. STS induced apoptosis with activation of Caspase 3/7. Apoptotic MSCs significantly prevented the proliferation of murine lymphocytes. MSCs can be administered and retrieved from murine knees. Retrieval yield is low, consistent with previous studies. MSCs were licensed from the OA joint to produce an immunosuppressive milieu that modulated macrophages ex vivo. In vitro, apoptosis increased the immunomodulatory potential of MSCs. This suggests that apoptosis may contribute to the therapeutic effects of MSCs in OA

Intra-articular infusions of adipose tissue-derived stem cells (ASCs) are a promising tool for bone regenerative medicine, thanks to their multilineage differentiating ability. One major limitation of ASCs is represented by the necessity to be isolated and expanded through in vitro culture, thus a strong interest was generated by the adipose stromal vascular fraction (SVF), the non-cultured fraction of ASCs. Besides the easiness of retrieval, handling and good availability, SVF is a heterogeneous population able to differentiate in vitro into osteoblasts, chondrocytes and adipocytes, according to the different stimuli received. We investigated and compared the bone regenerative potential of SVF and ASCs, through their ability to grow on SmartBone. ®. , a composite xenohybrid bone scaffold. SVF plated on SmartBone. ®. showed better osteoinductive capabilities than ASCs. Collagen I, osteocalcin and TGF↕ markedly stained the new tissue on SmartBone. ®. ; microCT analysis indicated a progressive increase in mineralised tissue apposition by quantification of newly formed trabeculae (3391 ± 270,5 vs 1825 ± 133,4, p± 0,001); an increased secretion of soluble factors stimulating osteoblasts, as VEGF (153,5 to 1278,1 pg/ml) and endothelin 1 (0,43 to 1,47 pg/ml), was detected over time. In conclusion, the usage of SVF, whose handling doesn't require manipulation in an in vitro culture, could definitively represent a benefit for a larger use in clinical applications. Our data strongly support an innovative idea for a bone regenerative medicine based on resorbable scaffold seeded with SVF, which will improve the precision of stem cells implant and the quality of new bone formation

The poor outcome of large head metal on metal total hip replacements (LHMOMTHR) in the absence of abnormal articulating surface wear has focussed attention on the trunnion / taper interface. The RedLux ultra-precision 3D form profiler provides a novel indirect optical method to detect small changes in form and surface finish of the head taper as well as quantitative assessment of wear volume. This study aimed to assess and compare qualitatively tapers from small and large diameter MOMTHR's. Tapers from 3 retrieval groups were analysed. Group 1: 28mm CoCr heads from MOMTHRs (n=5); Group 2: Large diameter CoCr heads from LHMOMTHRs (n=5); Gp 3 (control): 28mm heads from metal on polyethylene (MOP) THRs; n=3). Clinical data on the retrievals was collated. RedLux profiling of tapers produced a taper angle and 3D surface maps. The taper angles were compared to those obtained using CMM measurements. There was no difference between groups in mean 12/14 taper angles or bearing surface volumetric and linear wear. Only LHMOMs showed transfer of pattern from stem trunnion to head taper, with clear demarcation of contact and damaged areas.3D surface mapping demonstrated wear patterns compatible with motion or deformations between taper and trunnion in the LHMOM group. These appearances were not seen in tapers from small diameter MOM and MOP THRs. Differences in appearance of the taper surface between poorly functioning LHMOMTHRs and well functioning MOP or MOM small diameter devices highlight an area of concern and potential contributor to the mode of early failure

Post-mortem retrieval of canine, cemented femoral components was analysed to assess the performance of these implants in the dog as a model for human total hip replacement (THR). Mechanical testing and radiological analysis were performed to determine the stability of the implant and the quality of the cement. Thirty-eight implants from 29 dogs were retrieved after time intervals ranging from 0.67 to 11.67 years. The incidence of aseptic loosening was 63.2%, much higher than in human patients (6% in post-mortem studies). Failure of the femoral implants began with debonding at the cement-metal interface, similar to that in implants in man. The incidence of aseptic loosening was much lower in bilateral than in unilateral implants. Significant differences were observed for three different designs of implant. While the dog remains the animal model of choice for THR, results from this study provide insight into interspecies differences in the performance of implants. For example, the performance of THR in dogs should be compared with that in young rather than in elderly human patients

Total ankle replacement (TAR) has a mean survivorship of 77% at 10 years which is poor compared to other types of joint arthroplasty. Osteolysis and aseptic loosening are commonly cited TAR failure modes, the mechanisms of which are unknown. Retrieval analyses of TAR devices may reveal mechanisms of failure similar or dissimilar to other joint replacements. This study investigated whether TAR explants exhibit similar damage modes to those recognised in other total joint replacements. 22 Ankle Evolution System TARs (Transystème, Nimes, France) were implanted and retrieved by the same surgeon. Mean implantation time was 7.8 yrs (5.3 to 12.1 range). Pain and/or loosening were the indications for revision. Macro photography, an Alicona Infinite microscope and the Hood/Wasielewski scale were used to classify damage modes on the polyethylene insert. Scanning electron microscopy with energy dispersive X-ray spectroscopy was used to determine the composition of third body debris and to image the fixation surface of the tibial components. Mean damage score was 185.4 (± 40.0 SD). Damage modes common to total knee replacements were identified on both the superior and inferior insert surfaces, these included: burnishing, scratching, pitting and abrasion. Titanium particles, hydroxyapatite fragments and bone debris were embedded in the insert surfaces. Fixation surface delamination was identified by the ongrowth of tissue between the cobalt chromium substrate and titanium alloy coating. Damage modes indicative of high levels of wear and deformation were evident. Pitting caused by third body debris was abundant and suggested fixation surface wear and failure