Aims. The aim of this study was to determine whether there is a difference in the rate of wear between acetabular components positioned within and outside the ‘safe zones’ of anteversion and inclination angle. Patients and Methods. We reviewed 100 hips in 94 patients who had undergone primary total hip arthroplasty (THA) at least ten years previously. Patients all had the same type of acetabular component with a bearing couple which consisted of a 28 mm cobalt-chromium head on a highly crosslinked polyethylene (HXLPE) liner. A supine radiostereometric analysis (RSA) examination was carried out which acquired anteroposterior (AP) and lateral paired images. Acetabular component anteversion and inclination angles were measured as well as total femoral head penetration, which was divided by the length of implantation to determine the rate of polyethylene wear. Results. The mean anteversion angle was 19.4° (-15.2° to 48°, . sd. 11.4°), the mean inclination angle 43.4° (27.3° to 60.5°, . sd. 6.6°), and the mean wear rate 0.055 mm/year (. sd. 0.060). Exactly half of the hips were positioned inside the ‘safe zone’. There was no difference (median difference, 0.012 mm/year; p = 0.091) in the rate of wear between acetabular components located within or outside the ‘safe zone’. When compared to acetabular components located inside the ‘safe zone’, the wear rate was no different for acetabular components that only achieved the target anteversion angle (median difference, 0.012 mm/year; p = 0.138), target inclination angle (median difference, 0.013 mm/year; p = 0.354), or neither target (median difference, 0.012 mm/year; p = 0.322). Conclusion. Placing the acetabular component within or outside the ‘safe zone’ did not alter the wear rate of HXLPE at long-term follow-up to a level that risked osteolysis. HXLPE appears to be a forgiving bearing material in terms of articular surface wear, but care must still be taken to position the acetabular component correctly so that the implant is stable. Cite this article: Bone Joint J 2018;100-B:891-7

Objectives

The accuracy and precision of two new methods of model-based radiostereometric analysis (RSA) were hypothesised to be superior to a plain radiograph method in the assessment of polyethylene (PE) wear.

Lewinnek's safe zone recommendation to minimise dislocations was a target of 5–25° for anteversion angle and 30–50° for inclination angle. Subsequently, it was demonstrated that mal-positioning of the acetabular cup can also lead to edge loading, liner fracture, and greater conventional polyethylene wear. The purpose of this study was to measure the effect of acetabular cup position on highly crosslinked polyethylene wear in total hip arthroplasty (THA) at long-term follow-up. We identified all patients that underwent primary THA with a minimum of 10 years follow-up using an institutional database in London, Ontario, Canada. Patients with a single implant design consisting of a 28 mm cobalt chromium head and highly crosslinked polyethylene liner (ram extruded, GUR 1050, 100 kGy gamma irradiated, remelted, ethylene oxide sterilised) were selected for inclusion. In total, 85 hips from 79 recruited patients were analysed. Patients underwent a supine radiostereometric analysis (RSA) exam in which the x-ray sources and detectors were positioned to obtain an anterior-posterior and cross-table lateral radiograph. Acetabular cup anteversion angle, inclination angle, and 3D penetration rate (including wear and creep) were measured from the stereo radiograph pairs. At a mean follow-up of 13 years (range, 10–17 years) the mean penetration rate was 0.059 mm/year (95% CI: 0.045 to 0.073 mm/year). Mean anteversion angle was 18.2° (range, −14 to 40°) and mean inclination angle was 43.6° (range, 27 to 61°). With respect to the Lewinnek safe zone, 67% hips met the target for anteversion angle, 77% met the target for inclination angle, and 51% met the target for both. There was no correlation between anteversion angle and penetration rate (r = −0.14, p = 0.72) or between inclination angle and penetration rate (r = 0.11, p = 0.35). There was also no difference (p = 0.07) in penetration rate between hips located within the Lewinnek safe zone for both anteversion angle and inclination angle (mean 0.057 mm/year, 95% CI: 0.036 to 0.079 mm/year) and those outside the safe zone (mean 0.062 mm/year, 95% CI: 0.042 to 0.083 mm/year). Acetabular cup position had no effect on the wear rate of highly crosslinked polyethylene at long-term follow-up. Although care should still be taken to correctly position the acetabular cup for stability, highly crosslinked polyethylene is a forgiving bearing material that can withstand a wide range of cup positions without negatively impacting longevity due to wear

The purpose of this study was to precisely measure the 10-year polyethylene wear rate of primary total hips using Radiostereometric analysis (RSA) comparing Oxidized Zirconium (OxZi) to cobalt chrome (CoCr) femoral heads articulating with highly cross-linked polyethylene (XLPE). RSA was performed on 46 patients who underwent total hip arthroplasty − 23 who received OxZi femoral heads and 23 who received CoCr heads in combination with XLPE at a minimum of 10 years follow-up. All patients had identical THR systems implanted except for the femoral head utilized. The Centre Index method was utilised to assess total wear rates (from index surgery until final evaluation) using a dedicated RSA Software program (UmRSA Digital Measure v.2.2.1). In addition, the Martell technique was used to subtract head penetration occurring in the first 1–2 years (i.e. bedding-in phase) to allow calculation of the ‘steady state’ wear rates. There were no significant differences in demographics (i.e age, BMI, gender) between the groups. The average time from surgery of the RSA examinations was 11.7 and 12.6 years for the CoCr and OxZi groups respectively. Using the Centre Index Method to calculate total head penetration, wear rates were slightly higher in the OxZi group (0.048 +/− 0.021mm/year) compared to the CoCr group (0.035 +/− 0.017mm/year) with no statistical difference between the groups (p= 0.02). After correction for the bedding-in period, there was no statistically significant difference in mean ‘steady-state’ wear rate between OxZi (0.031 +/− 0.021mm/year) and CoCr (0.024 +/− 0.019mm/year) at 10 year follow up (p= 0.24). A comparison of preoperative and postoperative SF12, HHS, and WOMAC scores showed no statistical difference between the groups. RSA demonstrated the 10 year in-vivo wear rates of both bearing combinations to be well below the threshold for osteolysis. There was no significant difference between either the total or ‘steady-state’ wear rates of the OxZi and CoCr groups at 10 years

We examined the behaviour of alumina ceramic heads in 156 cemented total hip arthroplasties, at a minimum follow-up of eight years. They were divided into three groups according to the size of the femoral head; 22, 26, and 28 mm. We measured polyethylene wear radiologically using a computer-aided technique. The linear wear rate of polyethylene sockets for the 28 mm heads was high (0.156 mm/year), whereas those for the 22 and 26 mm heads were relatively low (0.090 and 0.098 mm/year, respectively). Moreover, the surface roughness data of retrieved femoral heads clearly showed maintenance of an excellent surface finish of the current alumina. We conclude that the alumina ceramic femoral heads currently used are associated with a reduced rate of polyethylene wear

We assessed the clinical and radiological outcome of a single uncemented total hip replacement (THR) after twenty years, analysing polyethylene wear and osteolysis. 82 hips implanted between 1992 and 1995 were prospectively evaluated. Mean follow-up was 20.6 years (18–23). A hemispherical porous-coated cup matched to a proximally hydroxyapatite-coated anatomic stem. A 28mm PE liner, sterilised by gamma irradiation in air, was used in all hips. Radiological position, eventual loosening and osteolysis were recorded over time. Penetration of the head into the liner was measured by the Roentgen Monographic Analysis (ROMAN) Tool at 6 weeks, 6 months, one year and yearly thereafter. Six cups were revised due to wear and four cups because of late dislocation. All stems showed osseointegration and all cups appeared radiographically well-fixed. Six unrevised hips showed osteolysis on the acetabular side and two hips on the proximal femur. Creep at one year was 0.30±0.23 mm. Mean total femoral head penetration was 1.23mm at ten years, 1.52mm at 15 years and 1.92mm at 23 years. Overall mean wear was 0.12±0.1 mm/year and 0.09±0.06 mm/year after the creep period. Mean wear was 0.08±0.06 mm/year in hips without osteolysis and 0.14±0.03 mm/year in hips revised or hips with osteolysis (p<0.001). Although continued durable fixation can be observed with porous-coated cups and proximally hydroxyapatite-coated anatomic stems, true wear continues to increase at a constant level over time. PE wear remains as the main reason for osteolysis and revision surgery in uncemented THR after twenty years

We have studied the influence of weight-bearing on the measurement of wear of the polyethylene acetabular component in total hip arthroplasty using two techniques. The measured vertical wear was significantly greater when radiographs were taken weight-bearing rather than with the patient supine (p = 0.001, method 1; p = 0.007, method 2). Calculations of rates of linear wear of the acetabular component were significantly underestimated (p < 0.05) when radiographs were taken supine. There are two reasons for this. First, a change in pelvic orientation when bearing weight ensures that the thinnest polyethylene is brought into relief, and secondly, the head of the femoral component assumes the position of maximal displacement along its wear path. Interpretation of previous studies on both linear and volumetric polyethylene wear in total hip arthroplasty should be reassessed in the light of these findings

Aims. Vitamin E-diffused, highly crosslinked polyethylene (VEPE) and porous titanium-coated (PTC) shells were introduced in total hip arthroplasty (THA) to reduce the risk of aseptic loosening. The purpose of this study was: 1) to compare the wear properties of VEPE to moderately crosslinked polyethylene; 2) to assess the stability of PTC shells; and 3) to report their clinical outcomes at seven years. Patients and Methods. A total of 89 patients were enrolled into a prospective study. All patients received a PTC shell and were randomized to receive a VEPE liner (n = 44) or a moderately crosslinked polyethylene (ModXLPE) liner (n = 45). Radiostereometric analysis (RSA) was used to measure polyethylene wear and component migration. Differences in wear were assessed while adjusting for body mass index, activity level, acetabular inclination, anteversion, and head size. Plain radiographs were assessed for radiolucency and patient-reported outcome measures (PROMs) were administered at each follow-up. Results. In total, 73 patients (82%) completed the seven-year visit. Mean seven-year linear proximal penetration was -0.07 mm (. sd. 0.16) and 0.00 mm (. sd. 0.22) for the VEPE and ModXLPE cohorts, respectively (p = 0.116). PROMs (p = 0.310 to 0.807) and radiolucency incidence (p = 0.330) were not different between the polyethylene cohorts. The mean proximal shell migration rate was 0.04 mm per year (. sd. 0.09). At seven years, patients with radiolucency (34%) demonstrated greater migration (mean difference: 0.6 mm (. sd. 0.2); p < 0.001). PROMs were lower for patients with radiolucency and greater proximal migration (p = 0.009 to p = 0.045). No implants were revised for aseptic loosening. Conclusion. This is the first randomized controlled trial to report seven-year RSA results for VEPE. All wear rates were below the previously reported osteolysis threshold (0.1 mm per year). PTC shells demonstrated acceptable primary stability through seven years, as indicated by low migration and lack of aseptic loosening. However, patients with acetabular radiolucency were associated with higher shell migration and lower PROM scores. Cite this article: Bone Joint J 2019;101-B:760–767

We have followed up for a period of seven to nine years 100 consecutive arthroplasties of the hip in which an entirely HA-coated implant had been used. The clinical results were excellent and bony incorporation was extensive in all components. No stem became loose or subsided but five cups were revised because of loosening after 3.8 to 5.5 years, having functioned painlessly and shown radiological ingrowth. Revision procedures because of excessive polyethylene wear have been performed on 18 hips and are planned for six more. Two eroded metal backings with worn-through polyethylene were exchanged; six hips showed metallosis without polyethylene wear-through. There were two cases of granulomatous cysts in the groin and 66 hips had osteolysis located periarticularly, in the greater trochanter or in the acetabulum

Oxidized zirconium (Oxinium) and highly cross-linked polyethylene (HXLPE) were developed with the purpose of minimizing wear, and subsequent osteolysis, in Total Hip Arthroplasty (THA). However, few articles have been published on long-term results of Oxinium on highly cross-linked polyethylene. The purpose of this investigation is to report minimum 10-year HXLPE wear rates and the clinical outcome of patients in this group and compare this population to a control group of cobalt chrome and ceramic.

One hundred forty THAs were performed for 123 patients using an Oxinium head with an HXLPE liner. Ninety-seven had 10 years of clinical follow-up (avg. 14.5). Harris Hip Scores (HHS) were collected preoperatively and at the most recent follow-up. Radiographs of 85 hips were available for a minimum 10-year follow-up (avg. 14.5) and used to calculate wear using PolyWare software. Control groups of cobalt chrome and ceramic articulation on HXLPE with a minimum 10-year follow-up were studied.

Clinical follow-up of the Oxinium group showed a statistical improvement compared to preoperative and was similar to the control group of patients. Radiographic evaluation found the linear and volumetric wear rates for the Oxinium group of 0.03 mm/year (range 0.00–0.08) and 3.46 mm³/year (range 1.0 to 15.0) respectively. There was no statistically significant difference in linear or volumetric wear rate between the groups (P-value 0.92 and 0.55 respectively). None of these patients underwent revision of their hip for any reason.

Oxinium on highly cross-linked polyethylene has performed exceptionally with wear rates comparable to those of cobalt chrome or ceramic on HXLPE.

Aims. The aim of this study was to evaluate the performance of first-generation annealed highly cross-linked polyethylene (HXLPE) in cementless total hip arthroplasty (THA). Methods. We retrospectively evaluated 29 patients (35 hips) who underwent THA between December 2000 and February 2002. The survival rate was estimated using the Kaplan-Meier method. Hip joint function was evaluated using the Japanese Orthopaedic Association (JOA) score. Two-dimensional polyethylene wear was estimated using Martell’s Hip Analysis Suite. We calculated the wear rates between years 1 and 5, 5 and 10, 10 and 15, and 15 and final follow-up. Results. The mean follow-up period was 19.1 years (SD 0.6; 17.3 to 20.1). The 19-year overall survival rate with the end point of all-cause revision was 97.0% (95% confidence interval (CI) 91 to 100). The mean JOA score improved from 43.2 (SD 10.6; 30 to 76) before surgery to 90.2 (SD 6.4; 76 to 98) at the final follow-up (p < 0.001). There was no osteolysis or loosening of the acetabular or femoral components. The overall steady-state wear rate was 0.013 mm/year (SD 0.012). There was no hip with a steady-state wear rate of > 0.1 mm/year. There was no significant difference in wear rates for each period. We found no significant correlation between the wear rate and age, body weight, BMI, or cup inclination. Conclusion. First-generation annealed HXLPE shows excellent wear resistance and no acceleration of wear for approximately 20 years, with low all-cause revision rates. Cite this article: Bone Joint J 2022;104-B(2):200–205

Isolated liner exchange with highly crosslinked polyethylene (HXLPE) is an option to address polyethylene wear and osteolysis after total hip arthroplasty (THA). The liner can be fixed with either the original locking mechanism or cemented into the acetabular cup. Whether the method used for fixation of HXLPE liner has any bearing on the outcomes 10 to 15 years after surgery is still unclear. Data for all patients who had undergone isolated liner exchange surgery with HXLPE in our institution between August 2000 and January 2015 were retrieved. Patients were classified according to the locking mechanism used (original locking mechanism or cemented). Survivorship and revision rates were compared among different subgroups. A total of 86 isolated liner exchanges were performed and patients had a mean duration of follow-up of 13 years (range, 5 to 22). 50 patients had the new liner cemented and the other 36 patients used the original locking mechanism. 20 patients (23.3%) had complications, with dislocation being the most common (7). 10 of them (12.6%) required re-revision surgery. Overall estimated mean survivorship was 19.2 years. There was no significant difference in the re-revision rate between original locking mechanism (11.1%) and cementation (12.0%) for the fixation of HXLPE (p=0.899). Using the Kaplan-Meier survival analysis, the revision-free survival of HXLPE fixed with original locking mechanism and cementation were 94.1% and 93.2%, respectively, at 10 years, and were 84.7% and 81.3%, respectively, at 20 years (p=0.840). The re-revision rate and the revision-free survival of liner exchange surgery using HXLPE liner were not affected by the fixation technique used. Both cementing a HXLPE liner or using the original locking mechanism were associated with good survivorship at 13 years follow up

We selected randomly a consecutive series of 162 patients requiring hip replacement to receive either a cementless, hemispherical, modular, titanium acetabular cup or a cemented, all-polyethylene cup. These replacements were performed by two surgeons in four general hospitals. The same surgical technique was used and a 26 mm metal-head femoral component was used in every case.

After exclusions, 115 hips were studied for differences in rates of wear and osteolysis. The mean clinical follow-up was eight years and the mean radiological follow-up, 6.5 years. The cementless cups wore at a mean rate of 0.15 mm per year and the cemented cups at 0.07 mm per year. This difference was significant (p < 0.0001).

Our findings in this mid-term study suggest that cementless cups wear more than cemented cups.

It has been suggested that the wear of ultra-high molecular weight polyethylene (UHMWPE) in total hip replacement is substantially reduced when the femoral head is ceramic rather than metal. However, studies of alumina and zirconia ceramic femoral heads on the penetration of an UHMWPE liner in vivo have given conflicting results.

The purpose of this study was to examine the surface characteristics of 30 alumina and 24 zirconia ceramic femoral heads and to identify any phase transformation in the zirconia heads. We also studied the penetration rate of alumina and zirconia heads into contemporary UHMWPE liners. The alumina heads had been implanted for a mean of 11.3 years (8.1 to 16.2) and zirconia heads for a mean of 9.8 years (7.5 to 15).

The mean surface roughness values of the explanted alumina heads (Ra 40.12 nm and Rpm 578.34 nm) were similar to those for the explanted zirconia heads (Ra 36.21 nm and Rpm 607.34 nm). The mean value of the monoclinic phase of two control zirconia heads was 1% (0.8% to 1.5%) and 1.2% (0.9% to 1.3%), respectively. The mean value of the monoclinic phase of 24 explanted zirconia heads was 7.3% (1% to 26%).

In the alumina group, the mean linear penetration rate of the UMWPE liner was 0.10 mm/yr (0.09 to 0.12) in hips with low Ra and Rpm values (13.22 nm and 85.91 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.13 mm/yr (0.07 to 0.23) in hips with high Ra and Rpm values (198.72 nm and 1329 nm, respectively). This difference was significant (p = 0.041).

In the zirconia head group, the mean linear penetration rate of the UHMWPE liner was 0.09 mm/yr (0.07 to 0.14) in hips with low Ra and Rpm values (12.78 nm and 92.99 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.12 mm/yr (0.08 to 0.22) in hips with high Ra and Rpm values (199.21 nm and 1381 nm, respectively). This difference was significant (p = 0.039).

The explanted zirconia heads which had a minimal phase transformation had similar surface roughness and a similar penetration rate of UHMWPE liner as the explanted alumina head.

Aims. This paper describes the methodology, validation and reliability of a new computer-assisted method which uses models of the patient’s bones and the components to measure their migration and polyethylene wear from radiographs after total hip arthroplasty (THA). Materials and Methods. Models of the patient’s acetabular and femoral component obtained from the manufacturer and models of the patient’s pelvis and femur built from a single computed tomography (CT) scan, are used by a computer program to measure the migration of the components and the penetration of the femoral head from anteroposterior and lateral radiographs taken at follow-up visits. The program simulates the radiographic setup and matches the position and orientation of the models to outlines of the pelvis, the acetabular and femoral component, and femur on radiographs. Changes in position and orientation reflect the migration of the components and the penetration of the femoral head. Validation was performed using radiographs of phantoms simulating known migration and penetration, and the clinical feasibility of measuring migration was assessed in two patients. Results. Migration of the acetabular and femoral components can be measured with limits of agreement (LOA) of 0.37 mm and 0.33 mm, respectively. Penetration of the femoral head can be measured with LOA of 0.161 mm. Conclusion. The migration of components and polyethylene wear can be measured without needing specialised radiographs. Accurate measurement may allow earlier prediction of failure after THA. Cite this article: Bone Joint J 2017;99-B:1290–7

Aims

We previously reported the long-term results of the cementless Duraloc-Profile total hip arthroplasty (THA) system in a 12- to 15-year follow-up study. In this paper, we provide an update on the clinical and radiological results of a previously reported cohort of patients at 23 to 26 years´ follow-up.

We evaluated the outcome of 41 consecutive Charnley low-friction arthroplasties (LFAs) performed by a single surgeon in 28 patients aged ≤ 35 years at operation between 23 and 36 years previously. There were 20 women and eight men with a mean age of 32 years (23 to 35) at surgery. Two patients (three hips) were lost to follow-up at 12 and 17 years post-operatively, respectively, and one patient (one hip) died at 13 years post-operatively. These patients were excluded from the final evaluation. The survival rate of the acetabular components was 92.7% (95% confidence interval (CI) 88.7 to 96.7) at ten years, 67.1% (95% CI 59.75 to 74.45) at 20 years and 53.2% (95% CI 45.3 to 61.1) at 25 years. For the femoral component the survival was 95.1% (95% CI 91.8 to 98.5) at ten years, 77.1% (95% CI 73.9 to 80.3) at 20 years and 68.2% (95% CI 60.7 to 75.8) at 25 years. The results indicate that the Charnley LFA remains a reasonable choice in the treatment of young patients and can serve for comparison with newer techniques and implants.

Cite this article: Bone Joint J 2013;95-B:1052–6.

Aims. Vitamin E-infused highly crosslinked polyethylene (VEPE) has been introduced into total hip arthroplasty (THA) with the aim of further improving the wear characteristics of moderately and highly crosslinked polyethylenes (ModXLPE and HXLPE). There are few studies analyzing the outcomes of vitamin E-infused components in cemented arthroplasty, though early acetabular component migration has been reported. The aim of this study was to measure five-year polyethylene wear and acetabular component stability of a cemented VEPE acetabular component compared with a ModXLPE cemented acetabular component. Methods. In a prospective randomized controlled trial (RCT), we assessed polyethylene wear and acetabular component stability (primary outcome) with radiostereometric analysis (RSA) in 68 patients with reverse hybrid THA at five years follow-up. Patients were randomized to either a VEPE or a ModXLPE cemented acetabular component. Results. Mean polyethylene wear in the proximal direction was 0.17 mm (SD 0.15) for the VEPE group and 0.20 mm (SD 0.09) for the ModXLPE group (p = 0.005) at five years. Annual proximal wear rates were 0.03 mm/year (VEPE) and 0.04 mm/year (ModXLPE). Total 3D wear was 0.21 mm (SD 0.26) and 0.23 mm (SD 0.10) for the VEPE and ModXLPE groups, respectively (p = 0.009). Total 3D cup translation was 0.72 mm (SD 0.70) (VEPE) and 0.50 mm (SD 0.44) (ModXLPE) (p = 0.409). Conclusion. At five years, there was less polyethylene wear in the VEPE group than in the ModXLPE group. Both VEPE and ModXLPE cemented components showed low annual wear rates. Component stability was similar in the two groups and remained constant up to five years. Whether these results will equate to a lower long-term revision rate is still unknown. Cite this article: Bone Joint J 2020;102-B(12):1646–1653

Aims. Highly cross-linked polyethylene (HXLPE) has greatly improved the durability of total hip arthroplasty (THA) in young patients because of its improved wear characteristics. Few studies have followed this population into the second decade, and therefore the purpose of this investigation was to evaluate the clinical outcome for THA patients 50 years of age and younger at a minimum of 15 years postoperatively. The second purpose was to evaluate the radiological findings secondary to wear or mechanical failure of the implant. Methods. Between October 1999 and December 2005, 105 THAs were performed in 95 patients (53 female, 42 male) aged 50 years and younger (mean 42 years (20 to 50)). There were 87 patients (96 hips) that were followed for a minimum of 15 years (mean 17.3 years (15 to 21)) for analysis. Posterior approach was used with cementless fixation with a median head size of 28 mm. HXLPE was the acetabular bearing for all hips. Radiographs were evaluated for polyethylene wear, radiolucent lines, and osteolysis. Results. Clinical outcomes showed significant improvement of mean Harris Hip Scores from 52.8 (SD 13.5) preoperatively to 94.8 (SD 7.6) postoperatively. One hip was revised for recurrent instability, and there were no infections. No hips were revised for mechanical loosening or osteolysis. Mean polyethylene linear wear was 0.04 mm/year and volumetric wear was 6.22 mm. 3. /year, with no significant differences between head size or material. Osteolysis was not present in any of the hips. Conclusion. The use of HXLPE in THA for patients aged 50 years and younger has performed exceptionally well without evidence of significant wear causing mechanical loosening or necessitating revision. The radiolucent lines of the acetabular component must be followed to determine the prognostic significance. This investigation represents the longest clinical follow-up of a large, consecutive cohort of patients aged 50 years or younger with THA using HXLPE. This long-term analysis found negligible polyethylene wear, no incidence of aseptic loosening, and excellent clinical outcomes at and beyond 15 years of follow-up. Cite this article: Bone Joint J 2021;103-B(7 Supple B):78–83

Aims. We aimed to investigate if the use of the largest possible cobalt-chromium head articulating with polyethylene acetabular inserts would increase the in vivo wear rate in total hip arthroplasty. Methods. In a single-blinded randomized controlled trial, 96 patients (43 females), at a median age of 63 years (interquartile range (IQR) 57 to 69), were allocated to receive either the largest possible modular femoral head (36 mm to 44 mm) in the thinnest possible insert or a standard 32 mm head. All patients received a vitamin E-doped cross-linked polyethylene insert and a cobalt-chromium head. The primary outcome was proximal head penetration measured with radiostereometric analysis (RSA) at two years. Secondary outcomes were volumetric wear, periacetabular radiolucencies, and patient-reported outcomes. Results. At two years, 44 patients in each group were available for RSA assessment. The median total two-year proximal head penetration was -0.02 mm (IQR -0.09 to 0.07; p = 0.548) for the largest possible head and -0.01 mm (IQR -0.07 to 0.10; p = 0.525) for 32 mm heads. Their difference was not statistically significant (p = 0.323). Neither group demonstrated a bedding-in period. The median steady-state volumetric wear rates were 6.1 mm. 3. /year (IQR -59 to 57) and 3.5 mm. 3. /year (-21 to 34) respectively, and did not differ between the groups (p = 0.848). There were no statistically significant differences in periacetabular radiolucencies or patient-reported outcomes. Conclusion. The use of the largest possible metal head did not increase vitamin E-doped cross-linked polyethylene wear compared with 32 mm heads at two years. Linear wear was negligible and volumetric wear rates were very low in both head size groups. There was a tendency towards higher values of volumetric wear in large heads that warrants longer-term evaluation before any definite conclusions about the association between head size and wear can be drawn. Cite this article: Bone Joint J 2021;103-B(7):1206–1214