Aims. We sought to determine whether cobalt-chromium alloy (CoCr) femoral stem tapers (trunnions) wear more than titanium (Ti) alloy stem tapers (trunnions) when used in a large diameter (LD) metal-on-metal (MoM) hip arthroplasty system. Patients and Methods. We performed explant analysis using validated methodology to determine the volumetric material loss at the taper surfaces of explanted LD CoCr MoM hip arthroplasties used with either a Ti alloy (n = 28) or CoCr femoral stem (n = 21). Only 12/14 taper constructs with a rough male taper surface and a nominal included angle close to 5.666° were included. Multiple regression modelling was undertaken using taper angle, taper roughness, bearing diameter (horizontal lever arm) as independent variables. Material loss was mapped using a coordinate measuring machine, profilometry and scanning electron microscopy. Results. After adjustment for other factors, CoCr stem tapers were found to have significantly greater volumetric material loss than the equivalent Ti stem tapers. Conclusion. When taper junction damage is identified during revision of a LD MoM hip, it should be suspected that a male taper composed of a standard CoCr alloy has sustained significant changes to the taper cone geometry which are likely to be more extensive than those affecting a Ti alloy stem. Cite this article: Bone Joint J 2017;99-B:1304–12

Aims. Asphericity of the femoral head-neck junction is common in cam-type femoroacetabular impingement (FAI) and usually quantified using the alpha angle on radiographs or MRI. The aim of this study was to determine the natural alpha angle in a large cohort of patients by continuous circumferential analysis with CT. Methods. CT scans of 1312 femurs of 656 patients were analyzed in this cross-sectional study. There were 362 men and 294 women. Their mean age was 61.2 years (18 to 93). All scans had been performed for reasons other than hip disease. Digital circumferential analysis allowed continuous determination of the alpha angle around the entire head-neck junction. All statistical tests were conducted two-sided; a p-value < 0.05 was considered statistically significant. Results. The mean maximum alpha angle for the cohort was 59.0° (. sd. 9.4). The maximum was located anterosuperiorly at 01:36 on the clock face, with two additional maxima of asphericity at the posterior and inferior head-neck junction. The mean alpha angle was significantly larger in men (59.4°, . sd. 8.0) compared with women (53.5°, . sd. 7.4°; p = 0.0005), and in Caucasians (60.7°, . sd. 9.0°) compared with Africans (56.3°, . sd. 8.0; p = 0.007) and Asians (50.8°, . sd. 7.2; p = 0.0005). The alpha angle showed a weak positive correlation with age (p < 0.05). If measured at commonly used planes of the radially reconstructed CT or MRI, the alpha angle was largely underestimated; measurement at the 01:30 and 02:00 positions showed a mean underestimation of 4° and 6°, respectively. Conclusion. This study provides important data on the normal alpha angle dependent on age, gender, and ethnic origin. The normal alpha angle in men is > 55°, and this should be borne in mind when making a diagnosis of cam-type morphology. Cite this article: Bone Joint J 2018;100-B:570–8

Aims. We wished to investigate the influence of metal debris exposure on the subsequent immune response and resulting soft-tissue injury following metal-on-metal (MoM) hip arthroplasty. Some reports have suggested that debris generated from the head-neck taper junction is more destructive than equivalent doses from metal bearing surfaces. . Patients and Methods. We investigated the influence of the source and volume of metal debris on chromium (Cr) and cobalt (Co) concentrations in corresponding blood and hip synovial fluid samples and the observed agglomerated particle sizes in excised tissues using multiple regression analysis of prospectively collected data. A total of 199 explanted MoM hips (177 patients; 132 hips female) were analysed to determine rates of volumetric wear at the bearing surfaces and taper junctions. . Results. The statistical modelling suggested that a greater source contribution of metal debris from the taper junction was associated with smaller aggregated particle sizes in the local tissues and a relative reduction of Cr ion concentrations in the corresponding synovial fluid and blood samples. Metal debris generated from taper junctions appears to be of a different morphology, composition and therefore, potentially, immunogenicity to that generated from bearing surfaces. Conclusion. The differences in debris arising from the taper and the articulating surfaces may provide some understanding of the increased incidence of soft-tissue reactions reported in patients implanted with MoM total hip arthroplasties compared with patients with hip resurfacings. Cite this article: Bone Joint J 2016;98-B:925–33

Introduction. Dual-mobility bearings increase the stable range of motion of total hip arthroplasty (THA) but are limited by the mechanical effects of a large diameter metal on polyethylene bearing which may cause high rates of wear from the surfaces of the polyethylene bearing and the head-stem taper. Improved polyethylene (PE) has reduced concern over bearing wear but the effects on the taper junction are unknown. We aimed to better understand the effect of dual mobility bearings on fretting-corrosion damage to the taper junction by comparison to standard bearings. Materials and Methods. We collected and analysed retrieved hips of one design with either dual mobility (n= 39) or standard bearings (n=30). The bearing size in the dual mobility group was 42mm whereas in the standard bearing group it had a median of 36mm. Stem trunnions had V40 tapers. Time of implantation and body mass index were comparable between the two groups. Fretting and corrosion at the stem trunnions was quantified by: 1) visual scoring and 2) surface profilometry. Results. Corrosion and fretting of the head-stem taper junction was lower in the dual mobility group when compared to the standard group as measured by both visual scoring (p=0.0002) and surface profilometry to measure material loss (p<0.0001). We did not see black debris, characteristic of severe corrosion processes, at the male surfaces in the dual mobility group. Discussion. In this study, visual damage at the male taper surfaces of dual mobility systems was less that that occurring at the male taper surfaces of standard articulating systems, measurements of wear rates were in agreements with the macroscopic evaluation. Conclusions. The frictional torque on the head-stem taper junction may be reduced with the use of a dual-mobility system when compared to a standard bearing system

We used Laser Doppler flowmetry to measure the effect on the blood flow to the femoral head/neck junction of two surgical approaches during resurfacing arthroplasty. We studied 24 hips undergoing resurfacing arthroplasty for osteoarthritis. Of these, 12 had a posterior approach and 12 a trochanteric flip approach. A Laser probe was placed under radiological control in the superolateral part of the femoral head/neck junction. The Doppler flux was measured at stages of the operation and compared with the initial flux. In both groups the main fall in blood flow occurred during the initial exposure and capsulotomy of the hip joint. There was a greater reduction in blood flow with the posterior (40%) than with the trochanteric flip approach (11%)

Aims. Surgeons have commonly used modular femoral heads and stems from different manufacturers, although this is not recommended by orthopaedic companies due to the different manufacturing processes. We compared the rate of corrosion and rate of wear at the trunnion/head taper junction in two groups of retrieved hips; those with mixed manufacturers (MM) and those from the same manufacturer (SM). . Materials and Methods. We identified 151 retrieved hips with large-diameter cobalt-chromium heads; 51 of two designs that had been paired with stems from different manufacturers (MM) and 100 of seven designs paired with stems from the same manufacturer (SM). We determined the severity of corrosion with the Goldberg corrosion score and the volume of material loss at the head/stem junction. We used multivariable statistical analysis to determine if there was a significant difference between the two groups. . Results. We found no significant difference in the corrosion scores of the two groups. The median rate of material loss at the head/stem junction for the MM and SM groups were 0.39 mm. 3. /year (0.00 to 4.73) and 0.46 mm. 3. /year (0.00 to 6.71) respectively; this difference was not significant after controlling for confounding factors (p = 0.06). . Conclusion. The use of stems with heads of another manufacturer does not appear to affect the amount of metal lost from the surfaces between these two components at total hip arthroplasty. Other surgical, implant and patient factors should be considered when determining the mechanisms of failure of large diameter metal-on-metal hip arthroplasties. Cite this article: Bone Joint J 2016;98-B:917–24

Objectives. An ongoing prospective study to investigate failing metal-on-metal hip prostheses was commenced at our centre in 2008. We report on the results of the analysis of the first consecutive 126 failed mated total hip prostheses from a single manufacturer. Methods. Analysis was carried out using highly accurate coordinate measuring to calculate volumetric and linear rates of the articular bearing surfaces and also the surfaces of the taper junctions. The relationship between taper wear rates and a number of variables, including bearing diameter and orientation of the acetabular component, was investigated. Results. The measured rates of wear and distribution of material loss from the taper surfaces appeared to show that the primary factor leading to taper failure is the increased lever arm acting on this junction in contemporary large-diameter metal-on-metal hip replacements. Conclusions. Our analysis suggests that varus stems, laterally engaging taper systems and larger head diameters all contribute to taper failure

Impingement by prominence at the femoral head-neck junction on the anterior acetabular rim may cause early osteoarthritis. Our aim was to develop a simple method to describe concavity at this junction, and then to test it by its ability to distinguish quantitatively a group of patients with clinical evidence of impingement from asymptomatic individuals who had normal hips on examination. MR scans of 39 patients with groin pain, decreased internal rotation and a positive impingement test were compared with those of 35 asymptomatic control subjects. The waist of the femoral head-neck junction was identified on tilted axial MR scans passing through the centre of the head. The anterior margin of the waist of the femoral neck was defined and measured by an angle (α). In addition, the width of the femoral head-neck junction was measured at two sites. Repeated measurements showed good reproducibility among four observers. The angle α averaged 74.0° for the patients and 42.0° for the control group (p < 0.001). Significant differences were also found between the patient and control groups for the scaled width of the femoral neck at both sites. Using standardised MRI, the symptomatic hips of patients who have impingement have significantly less concavity at the femoral head-neck junction than do normal hips. This test may be of value in patients with loss of internal rotation for which a cause is not found

We present a series of 35 patients (19 men and 16 women) with a mean age of 64 years (36.7 to 75.9), who underwent total hip replacement using the ESKA dual-modular short stem with metal on-polyethylene bearing surfaces. This implant has a modular neck section in addition to the modular head. Of these patients, three presented with increasing post-operative pain due to pseudotumour formation that resulted from corrosion at the modular neck-stem junction. These patients underwent further surgery and aseptic lymphocytic vaculitis associated lesions were demonstrated on histological analysis. Retrieval analysis of two modular necks showed corrosion at the neck-stem taper. Blood cobalt and chromium levels were measured at a mean of nine months (3 to 28) following surgery. These were compared with the levels in seven control patients (three men and four women) with a mean age of 53.4 years (32.1 to 64.1), who had an identical prosthesis and articulation but with a prosthesis that had no modularity at neck-stem junction. The mean blood levels of cobalt in the study group were raised at 50.75 nmol/l (5 to 145) compared with 5.6 nmol/l (2 to 13) in control patients. Corrosion at neck-stem tapers has been identified as an important source of metal ion release and pseudotumour formation requiring revision surgery. Finite element modelling of the dual modular stem demonstrated high stresses at the modular stem-neck junction. Dual modular cobalt-chrome hip prostheses should be used with caution due to these concerns

Objectives. This study aimed to characterise and qualitatively grade the severity of the corrosion particles released into the hip joint following taper corrosion. Methods. The 26 cases examined were CoC/ABG Modular (n = 13) and ASR/SROM (n = 13). Blood serum metal ion levels were collected before and after revision surgery. The haematoxylin and eosin tissue sections were graded on the presence of fibrin exudates, necrosis, inflammatory cells and corrosion products. The corrosion products were identified based on visible observation and graded on abundance. Two independent observers blinded to the clinical patient findings scored all cases. Elemental analysis was performed on corrosion products within tissue sections. X-Ray diffraction was used to identify crystalline structures present in taper debris. Results. The CoC/ABG Modular patients had a mean age of 64.6 years (49.4 to 76.5) and ASR/SROM patients had a mean age of 58.2 years (33.3 to 85.6). The mean time in situ for CoC/ABG was 4.9 years (2 to 6.4) and ASR/SROM was 6.1 years (2.5 to 8.1). The blood serum metal ion concentrations reduced following revision surgery with the exception of Cr levels within CoC/ABG. The grading of tissue sections showed that the macrophage response and metal debris were significantly higher for the ASR/SROM patients (p < 0.001). The brown/red particles were significantly higher for ASR/SROM (p < 0.001). The taper debris contained traces of titanium oxide, chromium oxide and aluminium nitride. Conclusion. This study characterised and qualitatively graded the severity of the corrosion particles released into the hip joint from tapers that had corrosion damage. Cite this article: S. Munir, R. A. Oliver, B. Zicat, W. L. Walter, W. K. Walter, W. R. Walsh. The histological and elemental characterisation of corrosion particles from taper junctions. Bone Joint Res 2016;5:370–378. DOI: 10.1302/2046-3758.59.2000507

The early failure and revision of bimodular primary total hip arthroplasty prostheses requires the identification of the risk factors for material loss and wear at the taper junctions through taper wear analysis. Deviations in taper geometries between revised and pristine modular neck tapers were determined using high resolution tactile measurements. A new algorithm was developed and validated to allow the quantitative analysis of material loss, complementing the standard visual inspection currently used. The algorithm was applied to a sample of 27 retrievals (in situ from 2.9 to 38.1 months) of the withdrawn Rejuvenate modular prosthesis. The mean wear volumes on the flat distal neck piece taper was 3.35 mm. 3. (0.55 to 7.57), mainly occurring in a characteristic pattern in areas with high mechanical loading. Wear volume tended to increase with time to revision (r² = 0.423, p = 0.001). Implant and patient specific data (offset, stem size, patient’s mass, age and body mass index) did not correlate with the amount of material loss observed (p >  0.078). Bilaterally revised implants showed higher amounts of combined total material loss and similar wear patterns on both sides. The consistent wear pattern found in this study has not been reported previously, suggesting that the device design and materials are associated with the failure of this prosthesis. Cite this article: Bone Joint J 2015;97-B:1350–7

Clinical graphics allows creation of three dimensional simulation based on CT or MRI that allows pre-operative planning. The software reports several hip morphological parameters routinely. Our aim was to validate the measurements of acetabular morphological parameters using CT based clinical graphics in patients presenting with symptomatic hip pain.

We reviewed standardised plain radiographs, CT scans and 3D clinical graphics outputs of 42 consecutive hips in 40 patients presenting with symptomatic hip pain. Acetabular index (AI), lateral centre edge angle (LCE), acetabular and femoral version measurements were analysed for the 3D clinical graphics with radiographs and CT as gold standard.

Significant differences were noted in measurements of AI, LCE, acetabular version and femoral version using the 3D motion analysis versus conventional measures, with only acetabular version showing comparable measurements. Correlation between 3D clinical graphics and conventional measures of acetabular morphology (AI, LCE) showed only slight agreement (ICC <0.4); while substantial agreement was noted for acetabular and femoral version (IC > 0.5).

Acetabular morphological parameters measured by 3D clinical graphics are not reliable or validated. While clinicians may pursue the use of 3D clinical graphics for preoperative non-invasive planning, caution should be exercised when interpreting the reports of hip morphological parameters such as AI and LCE.

Aims. We evaluated a large database with mechanical failure of a single uncemented modular femoral component, used in revision hip arthroplasty, as the end point and compared them to a control group treated with the same implant. Patient- and implant-specific risk factors for implant failure were analyzed. . Methods. All cases of a fractured uncemented modular revision femoral component from one manufacturer until April 2017 were identified and the total number of implants sold until April 2017 was used to calculate the fracture rate. The manufacturer provided data on patient demographics, time to failure, and implant details for all notified fractured devices. Patient- and implant-specific risk factors were evaluated using a logistic regression model with multiple imputations and compared to data from a previously published reference group, where no fractures had been observed. The results of a retrieval analysis of the fractured implants, performed by the manufacturer, were available for evaluation. Results. There were 113 recorded cases with fracture at the modular junction, resulting in a calculated fracture rate of 0.30% (113/37,600). The fracture rate of the implant without signs of improper use was 0.11% (41/37,600). In 79% (89/113) of cases with a failed implant, either a lateralized (high offset) neck segment, an extralong head, or the combination of both were used. Logistic regression analysis revealed male sex, high body mass index (BMI), straight component design, and small neck segments were significant risk factors for failure. Investigation of the implants (76/113) showed at least one sign of improper use in 72 cases. Conclusion. Implant failure at the modular junction is associated with patient- and implant-specific risk factors as well as technical errors during implantation. Whenever possible, the use of short and lateralized neck segments should be avoided with this revision system. Implantation instructions and contraindications need to be adhered to and respected. Cite this article: Bone Joint J 2020;102-B(5):573–579

The management of severe acetabular bone defects poses a complex challenge in revision hip arthroplasty. Although biological fixation materials are currently dominant, cage has played an important role in complex acetabular revision in the past decades, especially when a biological prosthesis is not available. The purpose of this study is to report the long-term clinical and radiographic results of Paprosky type Ⅲ acetabular bone defects revised with cage and morselized allografts. We retrospectively analyzed 45 patients who underwent revision hip arthroplasty with cage and morselized allografts between January 2007 and January 2019. Forty-three patients were followed up. There were 19 Paprosky type IIIA bone defect patients and 24 Paprosky type IIIB bone defect patients and 7 patients of the 24 were also with pelvic discontinuity. Clinical assessment included Harris Hip Score (HHS) and Short Form-12 (SF-12). Radiographic assessment included cage stability, allografts incorporation, and center of rotation. All patients were followed up with a mean follow-up of 10.6 years, HHS and SF-12 improved significantly at last follow-up in comparison to the preoperative. There were 2 re-revisions, one at 5 years after surgery, another at 13.6 years after surgery. Two patients had nonprogressive radiolucency in zone III and the junction of zone II and zone III at the bone implant interface. Allografts of 40 (93%) cases incorporated fully. The combination of cage and morselized allograft is an alternative option for acetabular revision with Paprosky type III bone defects with satisfactory long-term follow-up results

Introduction. Modularity in femoral stem designs allow surgeons to independently control leg length, offset, and femoral version in revision or complex primary THA cases. Initial enthusiasm in these modular stems has been tempered by recognition of modular junction failures. This study evaluates mean 5-year clinical results and survival rates of a 3-part titanium alloy modular femoral implant with unique taper geometries and a metaphyseal plasma spray surface. The current results are presented after pre-market independent fatigue testing performed by Orthopaedic Laboratory (Greenwald) and previously published early clinical results in 2006. Low plasticity burnishing (LPB) was added in 2005 to further strengthen the neck metaphyseal modular junction. The modular stem component is a polished cylindrical splined clothespin design. Our hypothesis is that these unique modular junctions succeed in offering the advantages of modularity without failure at this midterm follow-up period. Methods. Between May 2010 and July 2016, 32 total hip arthroplasties were performed using a 3-part femoral stem with neck-metaphyseal-stem modular junctions. Surgeries were either the final stage of a two-stage revision for infection, revision THR for loosening, or a revision of a previous non-prosthetic replacement procedure. Patients were entered into an IRB-approved registry and followed with x-rays, HHS, Oxford scores, and patient satisfaction scores. Patients who failed to return for routine follow-up were contacted by phone or email. Two patients had died with their implants intact. Six patients could not be reached for an updated follow-up. One stem was revised for loosening at 33 months due to failed osseointegration in a patient with chronic renal failure. This removed stem was submitted for taper exam and sectioning. Results. There were 23 patients for evaluation at a mean 61 months (range 21–98). Mean patient age at implantation was 56 (range 25–88), BMI was 27 (range 20–40). There were no modular junction failures. Modular junctions examined in the retrieved implant did not demonstrate any abnormalities other than normal wear properties. HHS and OHS scores both improved between pre-op and final follow-up, 23 to 85 and 17 to 43, respectively. Average patient satisfaction score at final follow-up was 9.8 out of 10 (min 8, max 10). Radiographic examination showed stem subsidence > 2mm and radiolucencies around the metaphyseal cone in 1 patient, the same patient who required implant removal. Radiolucencies were seen along the polished stem tip in 43% of cases, spot welding at the distal metaphyseal cone in 67% of cases, and mild proximal-medial stress shielding in 33% of cases. Conclusion. This unique 3-part modular stem with metaphyseal fixation shows good functional and radiographic results at 5-year follow-up. There were no junctional failures. One stem was removed due to failure to osseointegrate and showed no worrisome taper abnormalities. Spot welding is common around the plasma spray metaphyseal cone. Implant removal, if necessary, only requires disruption of the metaphyseal fixation. Further follow-up will be important to confirm our confidence in this unique stem design

Objectives. The use of ceramic femoral heads in total hip arthroplasty (THA) has increased due to their proven low bearing wear characteristics. Ceramic femoral heads are also thought to reduce wear and corrosion at the head-stem junction with titanium (Ti) stems when compared with metal heads. We sought to evaluate taper damage of ceramic compared with metal heads when paired with cobalt chromium (CoCr) alloy stems in a single stem design. Methods. This retrieval study involved 48 total hip arthroplasties (THAs) with CoCr V40 trunnions paired with either CoCr (n = 21) or ceramic (n = 27) heads. The taper junction of all hips was evaluated for fretting/corrosion damage and volumetric material loss using a roundness-measuring machine. We used linear regression analysis to investigate taper damage differences after adjusting for potential confounding variables. Results. We measured median taper material loss rates of 0.210 mm. 3. /year (0.030 to 0.448) for the metal head group and 0.084 mm. 3. /year (0.059 to 0.108) for the ceramic group. The difference was not significant (p = 0.58). Moreover, no significant correlation between material loss and implant or patient factors (p > 0.05) was found. Conclusions. Metal heads did not increase taper damage on CoCr trunnions compared with ceramic heads from the same hip design. The amount of material released at the taper junctions was very low when compared with available data regarding CoCr/Ti coupling in metal-on-metal bearings. Cite this article: A. Di Laura, H. Hothi, J. Henckel, I. Swiatkowska, M. H. L. Liow, Y-M. Kwon, J. A. Skinner, A. J. Hart. Retrieval analysis of metal and ceramic femoral heads on a single CoCr stem design. Bone Joint Res 2017;6:–350. DOI: 10.1302/2046-3758.65.BJR-2016-0325.R1

Introduction. Numerous studies have reported on clinically significant volumes of material loss and corrosion at the head-stem junction of metal-on-metal (MOM) hips; less is understood about metal-on-polyethylene (MOP) hips. We compared the effect of bearing type (MOM vs MOP) on taper material loss for a hip system of a single design (DePuy Pinnacle). Methods. We recruited retrieved MOM (n=30) and MOP (n=22) bearing hips that were consecutively received at our centre. We prospectively collected associated clinical and imaging data. We measured the severity of corrosion and volumes of material loss at each head taper surface and used multivariate statistical analysis to investigate differences between the two bearing types. Results. The median rate of material loss for the MOM and MOP groups was 0.81 mm. 3. /year (0.01–3.45) and 0.03 mm. 3. /year (0–1.07) respectively (p<0.001). 29 out of 30 MOM hips were revised for adverse metal reactions, compared with 1 out of 22 MOP hips. Discussion. MOP hips lost significantly less material from their taper junctions than MOM hips. We suggest that the metal-metal interaction at the bearing surface of MOM hips enhances the corrosive environment at the head-stem junction. Conclusion. Our results can reassure patients with MOP Pinnacle hips that they are unlikely to experience clinically significant problems related to material loss from the taper junction

Introduction. Improper seating during head/stem assembly can lead to unintended micromotion between the femoral head and stem taper—resulting in fretting corrosion and implant failure. 1. There is no consensus—either by manufacturers or by the surgical community—on what head/stem taper assembly method maximizes modular junction stability in total hip arthroplasty (THA). A 2018 clinical survey. 2. found that orthopedic surgeons prefer applying one strike or three, subsequent strikes when assembling head/stem taper. However, it has been suggested that additional strikes may lead to decreased interference strength. Additionally, the taper surface finish—micro-grooves—has been shown to affect taper interference strength and may be influenced by assembly method. The objective of this study was to employ a novel, micro-grooved finite element (FEA) model of the hip taper interface and assess the role of head/stem assembly method—one vs three strikes—on modular taper junction stability. Methods. A two-dimensional, axisymmetric FEA model representative of a CoCrMo femoral head taper and Ti6Al4V stem taper was created using median geometrical measurements taken from over 100 retrieved implants. 3. Surface finish—micro-grooves—of the head/stem taper were modeled using a sinusoidal function with amplitude and period corresponding to retrieval measurements of micro-groove height and spacing, respectively. Two stem taper micro-groove geometries— “rough” and “smooth”—were modeled corresponding to the median and 5. th. percentile height and spacing measurements from retrievals. All models had a 3' (0.05°), proximal-locked angular mismatch between the tapers. To simulate implant assembly during surgery, multiple dynamic loads (4kN, 8kN, and 12kN) were applied to the femoral head taper in a sequence of one or three strikes. The input load profile (Figure 1) used for both cases was collected from surgeons assembling an experimental setup with a three-dimensional load sensor. Models were assembled and meshed in ABAQUS Standard (v 6.17) using four-node linear hexahedral, reduced integration elements. Friction was modeled between the stem and head taper using surface-to-surface formulation with penalty contact (µ=0.2). A total of 12 implicit, dynamic simulations (3 loads × 2 assembly sequences × 2 stem taper surface finishes) were run, with 2 static simulations at 4kN for evaluating inertial effects. Outcome variables included contact area, contact pressure, equivalent plastic strain, and pull-off force. Results. As expected, increasing assembly load led to increased contact area, pressures, and plasticity for both taper finishes. Rough tapers exhibited less total contact area at each loading level as compared to the smooth taper. Contact pressures were relatively similar across the stem taper finishes, except the 3-strike smooth taper, which exhibited the lowest contact pressures (Figure 2) and pull-off forces. The models assembled with one strike exhibited the greatest contact pressures, pull-off forces, and micro-groove plastic deformation (Figure 3). Conclusion. Employing 1-strike loads led to greater contact areas, pressures, pull-off forces, and plastic deformation of the stem taper micro-grooves as compared to tapers assembled with three strikes. Residual energy may be lost with subsequent assembly strikes, suggesting that one, firm strike maximizes taper assembly mechanics. These models will be used to identify the optimal design factors and impaction method to maximize stability of modular taper junctions. For any tables or figures, please contact the authors directly

Tapered fluted titanium stems are increasingly used for femoral revision arthroplasty. They are available in modular and non-modular forms. Modularity has advantages when the bone loss is severe, the proximal femur is mis shapen or the surgeon is unfamiliar with the implant, but it introduces the risk of fracture of the stem at the junction between it and the proximal body segment. For that reason, and while awaiting intermediate-term results of more recently introduced designs of this junction, non-modularity has attracted attention, at least for straightforward revision cases. . We review the risks and causes of fracture of tapered titanium modular revision stems and present an argument in favour of the more selective use of modular designs. Cite this article: Bone Joint J 2016;98-B(1 Suppl A):50–3

Damage to and repair of the acetabular labral-chondral complex are areas of clinical interest in the treatment of young adults with pain in the hip and in the prevention of degenerative arthritis of the hip. There are varying theories as to why most acetabular tears are located anterosuperiorly. We have studied the prenatal development of the human acetabular labral-chondral complex in 11 fetal hips, aged from eight weeks of gestation to term. There were consistent differences between the anterior and posterior acetabular labral-chondral complex throughout all ages of gestation. The anterior labrum had a somewhat marginal attachment to the acetabular cartilage with an intra-articular projection. The posterior labrum was attached and continuous with the acetabular cartilage. Anteriorly, the labral-chondral transition zone was sharp and abrupt, but posteriorly it was gradual and interdigitated. The collagen fibres of the anterior labrum were arranged parallel to the labral-chondral junction, but at the posterior labrum they were aligned perpendicular to the junction. We believe that in the anterior labrum the marginal attachment and the orientation of the collagen fibres parallel to the labral-chondral junction may render it more prone to damage than the posterior labrum in which the collagen fibres are anchored in the acetabular cartilage. The anterior intra-articular projection of the labrum should not be considered to be a pathological feature