Aims. We sought to determine whether cobalt-chromium alloy (CoCr) femoral stem tapers (trunnions) wear more than titanium (Ti) alloy stem tapers (trunnions) when used in a large diameter (LD) metal-on-metal (MoM) hip arthroplasty system. Patients and Methods. We performed explant analysis using validated methodology to determine the volumetric material loss at the taper surfaces of explanted LD CoCr MoM hip arthroplasties used with either a Ti alloy (n = 28) or CoCr femoral stem (n = 21). Only 12/14 taper constructs with a rough male taper surface and a nominal included angle close to 5.666° were included. Multiple regression modelling was undertaken using taper angle, taper roughness, bearing diameter (horizontal lever arm) as independent variables. Material loss was mapped using a coordinate measuring machine, profilometry and scanning electron microscopy. Results. After adjustment for other factors, CoCr stem tapers were found to have significantly greater volumetric material loss than the equivalent Ti stem tapers. Conclusion. When taper junction damage is identified during revision of a LD MoM hip, it should be suspected that a male taper composed of a standard CoCr alloy has sustained significant changes to the taper cone geometry which are likely to be more extensive than those affecting a Ti alloy stem. Cite this article: Bone Joint J 2017;99-B:1304–12

Introduction. Total hip replacement failure due to fretting-corrosion remains a clinical concern. We recently described that damage within CoCrMo femoral heads can occur either by mechanically-dominated fretting processes leading to imprinting (via rough trunnions) and surface fretting (via smooth trunnions), or by a chemically-dominated etching process along preferential corrosion sites, termed “column damage”. These corrosion sites occur due to banding of the alloy microstructure. Banding is likely caused during thermo-mechanical processing of the alloy and is characterized by local molybdenum depletion. It was the objective of this study to quantify material loss from femoral heads with severe corrosion, identify the underlying damage modes, and to correlate the damage to the alloy's microstructure. Methods. 105 femoral heads with a Goldberg score 4 were evaluated. Coordinate measuring machine data was used to compute material loss and visualize damage features. Time in situ and stem alloy were identified. Metallographic samples were produced for each case. Grain size and banding were identified using light-microscopy. Mann-Whitney tests were conducted to compare material loss between groups. Results. Heads exhibited imprinting and column damage in 72 and 51 cases, respectively, with an overlap of 36 cases. 18 heads exhibited surface fretting only. All heads with column damage exhibited a banded microstructure. Heads with column damage had higher material loss (p=0.05) than those without. Also, heads with a banded microstructure had higher material loss (p=0.035) than those with a homogenous microstructure. Grain size, carbide content, and time did not correlate with material loss. Conclusion. Column damage is a detrimental damage mode within CoCrMo femoral heads that is directly linked to banding within its microstructure. It appears that banding even affects material loss before column damage is identifiable. These results indicate that implant alloy microstructure must be optimized to minimize the release of fretting-corrosion products and related implant failure

Objectives. The high revision rates of the DePuy Articular Surface Replacement (ASR) and the DePuy ASR XL (the total hip arthroplasty (THA) version) have led to questions over the viability of metal-on-metal (MoM) hip joints. Some designs of MoM hip joint do, however, have reasonable mid-term performance when implanted in appropriate patients. Investigations into the reasons for implant failure are important to offer help with the choice of implants and direction for future implant designs. One way to assess the performance of explanted hip prostheses is to measure the wear (in terms of material loss) on the joint surfaces. Methods. In this study, a coordinate measuring machine (CMM) was used to measure the wear on five failed cementless Biomet Magnum/ReCap/ Taperloc large head MoM THAs, along with one Biomet ReCap resurfacing joint. Surface roughness measurements were also taken. The reason for revision of these implants was pain and/or adverse reaction to metal debris (ARMD) and/or elevated blood metal ion levels. Results. The mean wear rate of the articulating surfaces of the heads and acetabular components of all six joints tested was found to be 6.1 mm. 3. /year (4.1 to 7.6). The mean wear rate of the femoral head tapers of the five THAs was 0.054 mm. 3. /year (0.021 to 0.128) with a mean maximum wear depth of 5.7 µm (4.3 to 8.5). Conclusion. Although the taper wear was relatively low, the wear from the articulating surfaces was sufficient to provide concern and was potentially large enough to have been the cause of failure of these joints. The authors believe that patients implanted with the ReCap system, whether the resurfacing prosthesis or the THA, should be closely monitored. Cite this article: S. C. Scholes, B. J. Hunt, V. M. Richardson, D. J. Langton, E. Smith, T. J. Joyce. Explant analysis of the Biomet Magnum/ReCap metal-on-metal hip joint. Bone Joint Res 2017;6:113–122. DOI: 10.1302/2046-3758.62.BJR-2016-0130.R2

Objectives. The aims of this piece of work were to: 1) record the background concentrations of blood chromium (Cr) and cobalt (Co) concentrations in a large group of subjects; 2) to compare blood/serum Cr and Co concentrations with retrieved metal-on-metal (MoM) hip resurfacings; 3) to examine the distribution of Co and Cr in the serum and whole blood of patients with MoM hip arthroplasties; and 4) to further understand the partitioning of metal ions between the serum and whole blood fractions. Methods. A total of 3042 blood samples donated to the local transfusion centre were analysed to record Co and Cr concentrations. Also, 91 hip resurfacing devices from patients who had given pre-revision blood/serum samples for metal ion analysis underwent volumetric wear assessment using a coordinate measuring machine. Linear regression analysis was carried out and receiver operating characteristic curves were constructed to assess the reliability of metal ions to identify abnormally wearing implants. The relationship between serum and whole blood concentrations of Cr and Co in 1048 patients was analysed using Bland-Altman charts. This relationship was further investigated in an in vitro study during which human blood was spiked with trivalent and hexavalent Cr, the serum then separated and the fractions analysed. Results. Only one patient in the transfusion group was found to have a blood Co > 2 µg/l. Blood/Serum Cr and Co concentrations were reliable indicators of abnormal wear. Blood Co appeared to be the most useful clinical test, with a concentration of 4.5 µg/l showing sensitivity and specificity for the detection of abnormal wear of 94% and 95%, respectively. Generated metal ions tended to fill the serum compartment preferentially in vivo and this was replicated in the in vitro study when blood was spiked with trivalent Cr and bivalent Co. Conclusions. Blood/serum metal ion concentrations are reliable indicators of abnormal wear processes. Important differences exist however between elements and the blood fraction under study. Future guidelines must take these differences into account

Introduction. Retrieved metal-on-metal acetabular components are invaluable resources from which to investigate the wear behaviour of failed hip implants. New forensic and investigative techniques continue to be developed to help the surgeon further understand factors which contribute to early failure. We have developed a novel technique to locate the in vivo location of the primary wear scar of an explanted cup. Patients/Materials & Methods. Thirteen (13) patients with failed metal hip resurfacings were recruited and their acetabular components retrieved. A 3D wear map was generated and the precise location of the primary wear scar in each cup was identified using a coordinate measuring machine (CMM). This wear scar position and location was noted in relation to standard landmarks on the acetabular cup. All patients underwent a computerised tomography (CT) scan prior to revision surgery. The 3D positional map from the CMM was then co-registered with the implant on the patient's pelvic 3D CT scan. Results. A schematic diagram was generated revealing the 3D orientation and location in the patient of the acetabular primary wear scars for all 13 subjects. The distribution of the location of the in vivo primary wear scars was variable and unique for each of the patient's acetabular cup. Discussion. We were able to identify the location of the in vivo primary wear scar of all thirteen acetabular cups successfully with this novel method. This technique can only be recruited for acetabular components that have clearly identifiable features which can be identified on CT. This is the first study to co-relate the point of highest wear on the acetabular cup to its pre-failure position in vivo. Conclusion. This technique has made it possible to better understand the three-dimensional properties of wear behaviour and can be used in further studies to investigate variables that determine the orientation and position of the primary wear scar

Introduction. In this study, we aimed to investigate the effect of the topography of the female taper surface on taper wear. Patients/Materials & Methods. We measured volumetric material loss at the female taper surface of the first consecutive 36mm MoM hips received at our centre. The MoM hips were from a single manufacturer and possessed matching: head size (36mm); taper geometry (5.65 degree 12 14 tapers); and metallurgy (cobalt chrome female taper mated with a titanium stem). Volume loss was measured with a coordinate measuring machine using validated methods. Surface roughness was measured using a Surftest SJ400. There were 111 head tapers available for analysis. The majority had been revised secondary to ARMD, and a minority for loosening. The mean duration of implantation was 56 months. Volumetric wear values were log normalised in order to construct a multiple regression model to investigate the interaction of head offset, the head taper angle and the Rp value of the female taper surface. Rp is a roughness parameter, which is a measure of the peaks above the plateau of a surface. Results. The median (range) volumetric loss from the female taper surfaces was 0.132mm3 (0.008–2.149). Median Rp value was 1.94 microns (0.50 to 6.01). Multiple regression model returned an R2 value of 0.43 (p < 0.001) meaning that the Rp value of the female surface, the head offset, duration of implantation and the taper angle explained 43% of the variation in volumetric wear rates. Rp was the dominant variable. Discussion & Conclusion. The topography of the female taper surface appears to be an important factor in material loss from the taper junction in MoM hips. There was an unexpectedly wide variation in surface finishes in our sample set despite the fact that a single product from a single manufacturer was analysed

Introduction. Historical studies have reported incidences of taper corrosion in retrieved MoP hips of 20–50%. These studies relied on visual assessments, rather than using modern analytical techniques. Patients/Materials and Methods. The Northern Retrieval Registry was initiated to routinely analyse all retrieved hips. The volumetric wear rates of retrieved Exeter head tapers were measured using a coordinate measuring machine using validated methods and compared to the available results obtained from an ongoing study of failed MoM prostheses. Power analysis suggested that we would need at least fifty Exeter head tapers to provide significant results. Non-parametric tests were used to assess differences. We have previously identified head diameter/offset/taper angle and taper surface roughness as variables associated with taper wear. The effect of bearing material combination remains unquantified. These design variables were entered into a multiple regression model following log normalisation of taper wear. Results. 56 consecutively retrieved Exeter head tapers underwent assessment. 36 were of size 28mm. Primary causes for revision were acetabular loosening/periprosthetic fractures. Mean duration in vivo was 87 (1 – 252) months. Median total volumetric wear was 0.29mm. 3. with a wear rate of 0.07mm. 3. /year. There were 353 MoMs. Median taper wear rates for 28mm MoM was 0.07, for 36mm was 0.11, for 38–44mm was 0.31, for 45 – 48mm was 0.52, for 49–52 was 0.55mm and for >52mm was 1.36mm. 3. /year. While Exeter taper wear was significantly lower than the MoM group as a whole (p<0.001), regression modelling indicated that bearing diameter had the greatest influence on taper wear. Discussion. Contrary to previous literature reports, significant material loss at the taper junction of conventional arthroplasties is not commonly observed. Exeter hips appear to be protected to some extent by the smaller head size and lower taper roughness when compared to contemporary MoM devices. The effect of the bearing combination remains under investigation

Aims

Acetabular edge-loading was a cause of increased wear rates in metal-on-metal hip arthroplasties, ultimately contributing to their failure. Although such wear patterns have been regularly reported in retrieval analyses, this study aimed to determine their in vivo location and investigate their relationship with acetabular component positioning.

Aims

This study investigates head-neck taper corrosion with varying head size in a novel hip simulator instrumented to measure corrosion related electrical activity under torsional loads.

Aims

The optimum clearance between the bearing surfaces of hip arthroplasties is unknown. Theoretically, to minimize wear, it is understood that clearances must be low enough to maintain optimal contact pressure and fluid film lubrication, while being large enough to allow lubricant recovery and reduce contact patch size. This study aimed to identify the relationship between diametrical clearance and volumetric wear, through the analysis of retrieved components.

Objectives

Previous studies have suggested that metal-on-metal (MoM) Pinnacle (DePuy Synthes, Warsaw, Indiana) hip arthroplasties implanted after 2006 exhibit higher failure rates. This was attributed to the production of implants with reduced diametrical clearances between their bearing surfaces, which, it was speculated, were outside manufacturing tolerances. This study aimed to better understand the performance of Pinnacle Systems manufactured before and after this event.

Objectives

We investigated the reliability of the cobalt-chromium (CoCr) synovial joint fluid ratio (JFR) in identifying the presence of a severe aseptic lymphocyte-dominated vasculitis-associated lesion (ALVAL) response and/or suboptimal taper performance (SOTP) following metal-on-metal (MoM) hip arthroplasty. We then examined the possibility that the CoCr JFR may influence the serum partitioning of Co and Cr.

Objectives

We have encountered patients who developed large joint fluid collections with massive elevations in chromium (Cr) and cobalt (Co) concentrations following metal-on-metal (MoM) hip arthroplasties. In some cases, retrieval analysis determined that these ion concentrations could not be explained simply by the wear rates of the components. We hypothesized that these effects may be associated with aseptic lymphocyte-dominated vasculitis-associated lesion (ALVAL).

Alumina–alumina bearings are among the most resistant to wear in total hip replacement. Examination of their surfaces is one way of comparing damage caused by wear of hip joints simulated in vitro to that seen in explanted bearings. The aim of this study was to determine whether second-generation ceramic bearings exhibited a better pattern of wear than those reported in the literature for first-generation bearings. We considered both macro- and microscopic findings.

We found that long-term alumina wear in association with a loose acetabular component could be categorised into three groups. Of 20 specimens, four had ‘low wear’, eight ‘crescent wear’ and eight ‘severe wear’, which was characterised by a change in the physical shape of the bearing and a loss of volume. This suggests that the wear in alumina–alumina bearings in association with a loose acetabular component may be variable in pattern, and may explain, in part, why the wear of a ceramic head in vivo may be greater than that seen after in vitro testing.

Aims

Surgeons have commonly used modular femoral heads and stems from different manufacturers, although this is not recommended by orthopaedic companies due to the different manufacturing processes.

We compared the rate of corrosion and rate of wear at the trunnion/head taper junction in two groups of retrieved hips; those with mixed manufacturers (MM) and those from the same manufacturer (SM).

There is widespread concern regarding the incidence of adverse soft-tissue reactions after metal-on-metal (MoM) hip replacement. Recent National Joint Registry data have shown clear differences in the rates of failure of different designs of hip resurfacing. Our aim was to update the failure rates related to metal debris for the Articular Surface Replacement (ASR). A total of 505 of these were implanted.

Kaplan-Meier analysis showed a failure rate of 25% at six years for the ASR resurfacing and of 48.8% for the ASR total hip replacement (THR). Of 257 patients with a minimum follow-up of two years, 67 (26.1%) had a serum cobalt concentration which was greater than 7 μg/l. Co-ordinate measuring machine analysis of revised components showed that all patients suffering adverse tissue reactions in the resurfacing group had abnormal wear of the bearing surfaces. Six THR patients had relatively low rates of articular wear, but were found to have considerable damage at the trunion-taper interface. Our results suggest that wear at the modular junction is an important factor in the development of adverse tissue reactions after implantation of a large-diameter MoM THR.

Objectives

An ongoing prospective study to investigate failing metal-on-metal hip prostheses was commenced at our centre in 2008. We report on the results of the analysis of the first consecutive 126 failed mated total hip prostheses from a single manufacturer.

This study reports the mid-term results of a large-bearing hybrid metal-on-metal total hip replacement in 199 hips (185 patients) with a mean follow-up of 62 months (32 to 83).

Two patients died of unrelated causes and 13 were lost to follow-up. In all, 17 hips (8.5%) have undergone revision, and a further 14 are awaiting surgery. All revisions were symptomatic. Of the revision cases, 14 hips showed evidence of adverse reactions to metal debris. The patients revised or awaiting revision had significantly higher whole blood cobalt ion levels (p = 0.001), but no significant difference in acetabular component size or position compared with the unrevised patients. Wear analysis (n = 5) showed increased wear at the trunnion-head interface, normal levels of wear at the articulating surfaces and evidence of corrosion on the surface of the stem.

The cumulative survival rate, with revision for any reason, was 92.4% (95% confidence interval 87.4 to 95.4) at five years. Including those awaiting surgery, the revision rate would be 15.1% with a cumulative survival at five years of 89.6% (95% confidence interval 83.9 to 93.4).

This hybrid metal-on-metal total hip replacement series has shown an unacceptably high rate of failure, with evidence of high wear at the trunnion-head interface and passive corrosion of the stem surface. This raises concerns about the use of large heads on conventional 12/14 tapers.

Two Durasul highly crosslinked polyethylene liners were exchanged during revision surgery four and five years after implantation, respectively. The retrieved liners were evaluated macroscopically and surface analysis was performed using optical and electron microscopy. A sample of each liner was used to determine the oxidation of the material by Fourier transform infrared spectroscopy. Samples of the capsule were examined histologically.

The annual wear rate was found to be 0.010 and 0.015 mm/year, respectively. Surface analysis showed very little loss of material caused by wear. Histological evaluation revealed a continuous neosynovial lining with single multinucleated foreign-body giant cells. Our findings showed no unexpected patterns of wear on the articulating surfaces up to five years after implantation and no obvious failure of material.