Alumina–alumina bearings are among the most resistant to wear in total hip replacement. Examination of their surfaces is one way of comparing damage caused by wear of hip joints simulated in vitro to that seen in explanted bearings. The aim of this study was to determine whether second-generation ceramic bearings exhibited a better pattern of wear than those reported in the literature for first-generation bearings. We considered both macro- and microscopic findings.

We found that long-term alumina wear in association with a loose acetabular component could be categorised into three groups. Of 20 specimens, four had ‘low wear’, eight ‘crescent wear’ and eight ‘severe wear’, which was characterised by a change in the physical shape of the bearing and a loss of volume. This suggests that the wear in alumina–alumina bearings in association with a loose acetabular component may be variable in pattern, and may explain, in part, why the wear of a ceramic head in vivo may be greater than that seen after in vitro testing.

Introduction. Retrieved metal-on-metal acetabular components are invaluable resources from which to investigate the wear behaviour of failed hip implants. New forensic and investigative techniques continue to be developed to help the surgeon further understand factors which contribute to early failure. We have developed a novel technique to locate the in vivo location of the primary wear scar of an explanted cup. Patients/Materials & Methods. Thirteen (13) patients with failed metal hip resurfacings were recruited and their acetabular components retrieved. A 3D wear map was generated and the precise location of the primary wear scar in each cup was identified using a coordinate measuring machine (CMM). This wear scar position and location was noted in relation to standard landmarks on the acetabular cup. All patients underwent a computerised tomography (CT) scan prior to revision surgery. The 3D positional map from the CMM was then co-registered with the implant on the patient's pelvic 3D CT scan. Results. A schematic diagram was generated revealing the 3D orientation and location in the patient of the acetabular primary wear scars for all 13 subjects. The distribution of the location of the in vivo primary wear scars was variable and unique for each of the patient's acetabular cup. Discussion. We were able to identify the location of the in vivo primary wear scar of all thirteen acetabular cups successfully with this novel method. This technique can only be recruited for acetabular components that have clearly identifiable features which can be identified on CT. This is the first study to co-relate the point of highest wear on the acetabular cup to its pre-failure position in vivo. Conclusion. This technique has made it possible to better understand the three-dimensional properties of wear behaviour and can be used in further studies to investigate variables that determine the orientation and position of the primary wear scar

Aims

This study investigates head-neck taper corrosion with varying head size in a novel hip simulator instrumented to measure corrosion related electrical activity under torsional loads.

Aims

Acetabular edge-loading was a cause of increased wear rates in metal-on-metal hip arthroplasties, ultimately contributing to their failure. Although such wear patterns have been regularly reported in retrieval analyses, this study aimed to determine their in vivo location and investigate their relationship with acetabular component positioning.

Aims

The optimum clearance between the bearing surfaces of hip arthroplasties is unknown. Theoretically, to minimize wear, it is understood that clearances must be low enough to maintain optimal contact pressure and fluid film lubrication, while being large enough to allow lubricant recovery and reduce contact patch size. This study aimed to identify the relationship between diametrical clearance and volumetric wear, through the analysis of retrieved components.

Objectives

The high revision rates of the DePuy Articular Surface Replacement (ASR) and the DePuy ASR XL (the total hip arthroplasty (THA) version) have led to questions over the viability of metal-on-metal (MoM) hip joints. Some designs of MoM hip joint do, however, have reasonable mid-term performance when implanted in appropriate patients. Investigations into the reasons for implant failure are important to offer help with the choice of implants and direction for future implant designs. One way to assess the performance of explanted hip prostheses is to measure the wear (in terms of material loss) on the joint surfaces.

Aims

There are limited published data detailing the volumetric material loss from tapers of conventional metal-on-polyethylene (MoP) total hip arthroplasties (THAs). Our aim was to address this by comparing the taper wear rates measured in an explanted cohort of the widely used Exeter THA with those measured in a group of metal-on-metal (MoM) THAs.

Aims

We sought to determine whether cobalt-chromium alloy (CoCr) femoral stem tapers (trunnions) wear more than titanium (Ti) alloy stem tapers (trunnions) when used in a large diameter (LD) metal-on-metal (MoM) hip arthroplasty system.

Restoration of leg length and offset is an important goal in total hip replacement. This paper reports a calliper-based technique to help achieve these goals by restoring the location of the centre of the femoral head. This was validated first by using a co-ordinate measuring machine to see how closely the calliper technique could record and restore the centre of the femoral head when simulating hip replacement on Sawbone femur, and secondly by using CT in patients undergoing hip replacement.

Results from the co-ordinate measuring machine showed that the centre of the femoral head was predicted by the calliper to within 4.3 mm for offset (mean 1.6 (95% confidence interval (CI) 0.4 to 2.8)) and 2.4 mm for vertical height (mean -0.6 (95% CI -1.4 to 0.2)). The CT scans showed that offset and vertical height were restored to within 8 mm (mean -1 (95% CI -2.1 to 0.6)) and -14 mm (mean 4 (95% CI 1.8 to 4.3)), respectively.

Accurate assessment and restoration of the centre of the femoral head is feasible with a calliper. It is quick, inexpensive, simple to use and can be applied to any design of femoral component.

Objectives

An ongoing prospective study to investigate failing metal-on-metal hip prostheses was commenced at our centre in 2008. We report on the results of the analysis of the first consecutive 126 failed mated total hip prostheses from a single manufacturer.

The Articular Surface Replacement (ASR) hip resurfacing arthroplasty has a failure rate of 12.0% at five years, compared with 4.3% for the Birmingham Hip Resurfacing (BHR). We analysed 66 ASR and 64 BHR explanted metal-on-metal hip replacements with the aim of understanding their mechanisms of failure. We measured the linear wear rates of the acetabular and femoral components and analysed the clinical cause of failure, pre-revision blood metal ion levels and orientation of the acetabular component.

There was no significant difference in metal ion levels (chromium, p = 0.82; cobalt, p = 0.40) or head wear rate (p = 0.14) between the two groups. The ASR had a significantly increased rate of wear of the acetabular component (p = 0.03) and a significantly increased occurrence of edge loading (p < 0.005), which can be attributed to differences in design between the ASR and BHR. The effects of differences in design on the in vivo wear rates are discussed: these may provide an explanation as to why the ASR is more sensitive to suboptimal positioning than the BHR.

Objectives

The aims of this piece of work were to: 1) record the background concentrations of blood chromium (Cr) and cobalt (Co) concentrations in a large group of subjects; 2) to compare blood/serum Cr and Co concentrations with retrieved metal-on-metal (MoM) hip resurfacings; 3) to examine the distribution of Co and Cr in the serum and whole blood of patients with MoM hip arthroplasties; and 4) to further understand the partitioning of metal ions between the serum and whole blood fractions.