Introduction. We aimed to identify genes associated with the development of ALVAL at relatively low levels of wear. Methods. At our unit all patients undergoing revision of a MoM hip prosthesis have periprosthetic tissue samples graded for ALVAL. Explants undergo volumetric wear testing of the bearing and taper surfaces. We identified patients with moderate/severe ALVAL who had been exposed to lower than the median wear rate of all recorded patients who had developed ALVAL (<3mm. 3. /year). This was termed the “ALVAL” group. We then identified all patients whose tissues had shown no signs of ALVAL. The patients in the two groups were sent buccal DNA collection kits. DNA was examined using next generation sequencing. Alleleic frequencies in the two groups were compared using Fisher's test and compared to a background UK population group (n=8514). We then conducted binary logistic regression with patient age, sex, primary source of debris (taper/bearing) and HLA genotype as the predictors. With the hypothesis that a cobalt/albumin metalloprotein acts as the epitope, we used validated binding prediction software to determine the relative affinities of the binding grooves created by different DQA1/DQB1 genetic combinations for albumin derived peptides. Given the protection that male sex and younger age appears to confer against ALVAL, we hypothesized that testosterone peptides may compete for these binding sites. Results. 28 ALVAL and 37 non ALVAL patients returned their samples for testing. The frequencies of DQA1∗05:05 and DQB1∗03:01 were significantly greater in the ALVAL groups(p=0.018). The variables positively associated with ALVAL were female sex(0.021), increasing age(0.003) and DQA1/DQB1 combinations with greater binding affinity for albumin fragments(0.03). Greater binding affinities for testosterone peptides were inversely related to ALVAL(0.05). Discussion. Common immune genotypes are associated with a greater risk of ALVAL. Conclusion. The evidence base on which MoM follow up protocols are based should be re-evaluated in light of these findings and future studies designed accordingly

Aims. Hip resurfacing remains a potentially valuable surgical procedure for appropriately-selected patients with optimised implant choices. However, concern regarding high early failure rates continues to undermine confidence in use. A large contributor to failure is adverse local tissue reactions around metal-on-metal (MoM) bearing surfaces. Such phenomena have been well-explored around MoM total hip arthroplasties, but comparable data in equivalent hip resurfacing procedures is lacking. In order to define genetic predisposition, we performed a case-control study investigating the role of human leucocyte antigen (HLA) genotype in the development of pseudotumours around MoM hip resurfacings. Methods. A matched case-control study was performed using the prospectively-collected database at the host institution. In all, 16 MoM hip resurfacing 'cases' were identified as having symptomatic periprosthetic pseudotumours on preoperative metal artefact reduction sequence (MARS) MRI, and were subsequently histologically confirmed as high-grade aseptic lymphocyte-dominated vasculitis-associated lesions (ALVALs) at revision surgery. ‘Controls’ were matched by implant type in the absence of evidence of pseudotumour. Blood samples from all cases and controls were collected prospectively for high resolution genetic a nalysis targeting 11 separate HLA loci. Statistical significance was set at 0.10 a priori to determine the association between HLA genotype and pseudotumour formation, given the small sample size. Results. Using a previously-reported ALVAL classification, the majority of pseudotumour-positive caseswere found to have intermediate-grade group 2 (n = 10; 63%) or group 3 (n = 4; 25%) histological findings. Two further patients (13%) had high-grade group 4 lesions. HLA-DQB1*05:03:01 (p = 0.0676) and HLA-DRB1*14:54:01 (p = 0.0676) alleles were significantly associated with a higher risk of pseudotumour formation, while HLA-DQA1*03:01:01 (p = 0.0240), HLA-DRB1*04:04:01 (p = 0.0453), HLA-C*01:02:01 (p = 0.0453), and HLA-B*27:05:02 (p = 0.0855) were noted to confer risk reduction. Conclusion. These findings confirm the association between specific HLA genotypes and the risk of pseudotumour development around MoM hip resurfacings. Specifically, the two ‘at risk’ alleles (DQB1*05:03:01 and DRB1*14:54:01) may hold clinical value in preoperative screening and prospective surgical decision-making. Cite this article: Bone Jt Open 2023;4(3):182–187

We present a series of 35 patients (19 men and 16 women) with a mean age of 64 years (36.7 to 75.9), who underwent total hip replacement using the ESKA dual-modular short stem with metal on-polyethylene bearing surfaces. This implant has a modular neck section in addition to the modular head. Of these patients, three presented with increasing post-operative pain due to pseudotumour formation that resulted from corrosion at the modular neck-stem junction. These patients underwent further surgery and aseptic lymphocytic vaculitis associated lesions were demonstrated on histological analysis.

Retrieval analysis of two modular necks showed corrosion at the neck-stem taper. Blood cobalt and chromium levels were measured at a mean of nine months (3 to 28) following surgery. These were compared with the levels in seven control patients (three men and four women) with a mean age of 53.4 years (32.1 to 64.1), who had an identical prosthesis and articulation but with a prosthesis that had no modularity at neck-stem junction. The mean blood levels of cobalt in the study group were raised at 50.75 nmol/l (5 to 145) compared with 5.6 nmol/l (2 to 13) in control patients.

Corrosion at neck-stem tapers has been identified as an important source of metal ion release and pseudotumour formation requiring revision surgery. Finite element modelling of the dual modular stem demonstrated high stresses at the modular stem-neck junction. Dual modular cobalt-chrome hip prostheses should be used with caution due to these concerns.

Objectives. We have encountered patients who developed large joint fluid collections with massive elevations in chromium (Cr) and cobalt (Co) concentrations following metal-on-metal (MoM) hip arthroplasties. In some cases, retrieval analysis determined that these ion concentrations could not be explained simply by the wear rates of the components. We hypothesized that these effects may be associated with aseptic lymphocyte-dominated vasculitis-associated lesion (ALVAL). Patients and Methods. We examined the influence of the ALVAL grade on synovial fluid Co and Cr concentrations following adjustment for patient and device variables, including volumetric wear rates. Initially restricting the analysis to include only patients with one MoM hip resurfacing device, we performed multiple regression analyses of prospectively collected data. We then repeated the same statistical approach using results from a larger cohort with different MoM designs, including total hip arthroplasties. Results. In the resurfacing cohort (n = 76), the statistical modelling indicated that the presence of severe ALVAL and a large fluid collection were associated with greater joint fluid Co concentrations after adjustment for volumetric wear rates (p = 0.005). These findings were replicated in the mixed implant group (n = 178), where the presence of severe ALVAL and a large fluid collection were significantly associated with greater fluid Co concentrations (p < 0.001). Conclusion. The development of severe ALVAL is associated with elevations in metal ion concentrations far beyond those expected from the volumetric loss from the prosthetic surfaces. This finding may aid the understanding of the sequence of events leading to soft-tissue reactions following MoM hip arthroplasties. Cite this article: D. J. Langton, R. P. Sidaginamale, T. J. Joyce, J. G. Bowsher, J. P. Holland, D. Deehan, A. V. F. Nargol, S. Natu. Aseptic lymphocyte-dominated vasculitis-associated lesions are related to changes in metal ion handling in the joint capsules of metal-on-metal hip arthroplasties. Bone Joint Res 2018;7:388–396. DOI: 10.1302/2046-3758.76.BJR-2018-0037

Objectives. We investigated the reliability of the cobalt-chromium (CoCr) synovial joint fluid ratio (JFR) in identifying the presence of a severe aseptic lymphocyte-dominated vasculitis-associated lesion (ALVAL) response and/or suboptimal taper performance (SOTP) following metal-on-metal (MoM) hip arthroplasty. We then examined the possibility that the CoCr JFR may influence the serum partitioning of Co and Cr. Methods. For part A, we included all revision surgeries carried out at our unit with the relevant data, including volumetric wear analysis, joint fluid (JF) Co and Cr concentrations, and ALVAL grade (n = 315). Receiver operating characteristic curves were constructed to assess the reliability of the CoCr JFR in identifying severe ALVAL and/or SOTP. For part B, we included only patients with unilateral prostheses who had given matched serum and whole blood samples for Co and Cr analysis (n = 155). Multiple regression was used to examine the influence of JF concentrations on the serum partitioning of Co and Cr in the blood. Results. A CoCr JFR > 1 showed a specificity of 83% (77% to 88%) and sensitivity of 63% (55% to 70%) for the detection of severe ALVAL and/or SOTP. In patients with CoCr JFRs > 1, the median blood Cr to serum Cr ratio was 0.99, compared with 0.71 in patients with CoCr JFRs < 1 (p < 0.001). Regression analysis demonstrated that the blood Cr to serum Cr value was positively associated with the JF Co concentration (p = 0.011) and inversely related to the JF Cr concentration (p < 0.001). Conclusion. Elevations in CoCr JFRs are associated with adverse biological (severe ALVAL) or tribocorrosive processes (SOTP). Comparison of serum Cr with blood Cr concentrations may be a useful additional clinical tool to help to identify these conditions. Cite this article: D. J. Langton, S. Natu, C. F. Harrington, J. G. Bowsher, A. V. F. Nargol. Is the synovial fluid cobalt-to-chromium ratio related to the serum partitioning of metal debris following metal-on-metal hip arthroplasty? Bone Joint Res 2019;8:146–155. DOI: 10.1302/2046-3758.83.BJR-2018-0049.R1

Cobalt chrome alloy is commonly used in joint replacement surgery. However, it is recognised that some patients develop lymphocyte mediated delayed type hypersensitivity (DTH) responses to this material, which may result in extensive bone and soft tissue destruction. Phase 1. United Kingdom: From an existing database, we identified extreme phenotype patient groups following metal on metal (MoM) hip resurfacing or THR: ALVAL with low wearing prostheses; ALVAL with high wear; no ALVAL with high wear; and asymptomatic patients with implants in situ for longer than ten years. Class I and II HLA genotype frequency distributions were compared between these patients’ groups, and in silico peptide binding studies were carried out using validated methodology. Phase 2. United Kingdom: We expanded the study to include more patients, including those with intermediary phenotypes to test whether an algorithm could be developed incorporating “risk genotypes”, patient age, sex and metal exposure. This model was trained in phase 3. Phase 3. United Kingdom, Australia, United States. Patients from other centres were invited to give DNA samples. The data set was split in two. 70% was used to develop machine learning models to predict failure secondary to DTH. The predictions were tested using the remaining blinded 30% of data, using time-dependent AUROCs, and integrated calibration index performance statistics. A total of 606 DNA samples, from 397 males and 209 female patients, were typed. This included 176 from patients with failed prostheses, and 430 from asymptomatic patients at a mean of >10 years follow up. C-index and ROC(t) scores suggested a high degree of discrimination, whilst the IBS indicated good calibration and further backed up the indication of high discriminatory ability. At ten years, the weighted mean survival probability error was < 4%. At present, there are no tests in widespread clinical use which use a patient's genetic profile to guide implant selection or inform post-operative management. The algorithm described herein may address this issue and we suggest that the application may not be restricted to the field of MoM hip arthroplasty

Introduction. In 2010, a widely used metal-on-metal hip implant was voluntarily recalled from the market by the manufacturer. Our lab performed detailed retrieval analysis of 548 of the explanted devices and 165 periprosthetic tissue specimens. We reported a high degree of variability in the multiple measurements that we performed on the components, including volumetric wear. Other studies using semi-quantitative tissue grading methods to describe the histology of the periprosthetic tissues from metal-on-metal hips have looked for relationships between component wear and histological features. Grammatopoulos et al found higher ALVAL scores in 45 hip resurfacing patients with pseudotumors compared to 11 without pseudotumors and a moderately positive correlation between wear and the histological rankings for tissue necrosis and lymphocytic response. We examined correlations between the component wear measurements from retrieval analysis and the tissue features in this large group of one metal-on-metal hip design. Materials and Methods. Tissues were processed routinely into paraffin sections, stained with H&E and characterized with light microscopic semi-quantitative scores for ALVAL features and for the number of macrophages and lymphocytes, extent of metal debris and the estimated percentage of necrosis per slide. Spearman correlation analysis was conducted to evaluate any correlations between retrieval wear measurements and histological findings. Results. The median combined cup and ball wear volume was 17.5mm3 in these 165 cases. The median tissue ALVAL score was 5.5 out of 10. Component total wear volume was not predictive of the ALVAL score (P = 0.09, R = −0.007) or the number of lymphocytes (P= 0.170, R= −0.077) but there was a positive correlation between wear volume and the ranking for macrophages in the tissues (P< 0.001, R=0.215). No other correlations were found for component wear. The median time to revision was 4.84 years. There was a negative correlation between tissue inflammation ranking (P=0.002, R=−0.183) and for lymphocyte ranking and time to revision (P=0.003, R=−0.173). There was a positive correlation between time to revision and the macrophage ranking (P=0.005, R=0.166). Conclusion. From this large-scale retrieval analysis of one design of metal-on-metal total hip, a high degree of variability was observed over the multiple analyses performed, including volumetric wear and tissue features. This likely reflects our previous observation that no single particular failure mechanism was predominant in this large cohort. Funded by DePuy Synthes Companies of Johnson & Johnson

Background. Some reports have suggested that debris generated from the head neck taper junction is more destructive than equivalent doses from metal bearing surfaces. Methods. Part 1. We examined the relationship between the source (taper/bearing) and volume of metal debris on Cr and Co concentrations in corresponding blood and hip synovial fluid samples and the observed agglomerated particle sizes in excised tissues using regression analysis of prospectively collected data at a single revision unit. Part 2. We investigated variables most strongly associated with macroscopic soft tissue injury as documented at revision surgery using ordinal logistic regression. Independent variables included source and volume of CoCr exposure, Cr and Co joint fluid concentrations, joint fluid grade, ALVAL (Aseptic Lymphocytic Vasculitis Associated Lesion) grade, presence of vascular hyalinisation, agglomerated particle size, implant type, patient sex and age. Results. A total of 199 explanted MoM hips were analysed. Multiple regression statistical modelling suggested that a greater source contribution of metal debris from the taper junction was associated with smaller aggregated particle sizes in the local tissues and a relative reduction of Cr ion concentrations in the corresponding synovial fluid and blood samples. There was an association between increasing Co concentrations in the joint fluid and an increasing ALVAL score (p<0.001). In contrast, higher Cr concentrations were inversely related to ALVAL (p<0.001). The ALVAL response was itself strongly associated with larger fluid collections (p<0.001). Vascular hyalinisation and larger fluid collections were significantly associated with macroscopic tissue injury (coefficient 2.22, p<0.001 for fluid grade and 4.35, p<0.001 for hyalinisation). Discussion. Metal debris generated from taper junctions appears to be associated with a different biochemical environment than debris generated from bearing surfaces. We believe that this finding may provide some explanation as to the poor performance of MoM THRs compared to the equivalent resurfacing devices and the confusion surrounding the significance of blood metal testing. Conclusion. Chromium does seem to inhibit the development of ALVAL

Despite the increasing interest and subsequent published literature on hip resurfacing arthroplasty, little is known about the prevalence of its complications and in particular the less common modes of failure. The aim of this study was to identify the prevalence of failure of hip resurfacing arthroplasty and to analyse the reasons for it. From a multi-surgeon series (141 surgeons) of 5000 Birmingham hip resurfacings we have analysed the modes, prevalence, gender differences and times to failure of any hip requiring revision. To date 182 hips have been revised (3.6%). The most common cause for revision was a fracture of the neck of the femur (54 hips, prevalence 1.1%), followed by loosening of the acetabular component (32 hips, 0.6%), collapse of the femoral head/avascular necrosis (30 hips, 0.6%), loosening of the femoral component (19 hips, 0.4%), infection (17 hips, 0.3%), pain with aseptic lymphocytic vascular and associated lesions (ALVAL)/metallosis (15 hips, 0.3%), loosening of both components (five hips, 0.1%), dislocation (five hips, 0.1%) and malposition of the acetabular component (three hips, 0.1%). In two cases the cause of failure was unknown. Comparing men with women, we found the prevalence of revision to be significantly higher in women (women = 5.7%; men = 2.6%, p < 0.001). When analysing the individual modes of failure women had significantly more revisions for loosening of the acetabular component, dislocation, infection and pain/ALVAL/metallosis (p < 0.001, p = 0.004, p = 0.008, p = 0.01 respectively). The mean time to failure was 2.9 years (0.003 to 11.0) for all causes, with revision for fracture of the neck of the femur occurring earlier than other causes (mean 1.5 years, 0.02 to 11.0). There was a significantly shorter time to failure in men (mean 2.1 years, 0.4 to 8.7) compared with women (mean 3.6 years, 0.003 to 11.0) (p < 0.001)

Aims

This study aims to assess the relationship between history of pseudotumour formation secondary to metal-on-metal (MoM) implants and periprosthetic joint infection (PJI) rate, as well as establish ESR and CRP thresholds that are suggestive of infection in these patients. We hypothesized that patients with a pseudotumour were at increased risk of infection.

Aims

Metal-on-metal hip resurfacing (MoM-HR) has seen decreased usage due to safety and longevity concerns. Joint registries have highlighted the risks in females, smaller hips, and hip dysplasia. This study aimed to identify if reported risk factors are linked to revision in a long-term follow-up of MoM-HR performed by a non-designer surgeon.

Aims

The aims of this study were to determine if an increasing serum cobalt (Co) and/or chromium (Cr) concentration is correlated with a decreasing Harris Hip Score (HHS) and Hip disability and Osteoarthritis Outcome Score (HOOS) in patients who received the Articular Surface Replacement (ASR) hip resurfacing arthroplasty (HRA), and to evaluate the ten-year revision rate and show if sex, inclination angle, and Co level influenced the revision rate.

Aims

Dual mobility implants in total hip arthroplasty are designed to increase the functional head size, thus decreasing the potential for dislocation. Modular dual mobility (MDM) implants incorporate a metal liner (e.g. cobalt-chromium alloy) in a metal shell (e.g. titanium alloy), raising concern for mechanically assisted crevice corrosion at the modular liner-shell connection. We sought to examine fretting and corrosion on MDM liners, to analyze the corrosion products, and to examine histologically the periprosthetic tissues.

Aims

Adverse local tissue reactions associated with abnormal wear considerably slowed down the general use of metal-on-metal (MoM) hip resurfacing arthroplasty (HRA), now limited to a few specialized centres. In this study, we provide the clinical results of 400 consecutive MoM HRAs implanted more than 20 years ago in one such centre.

Lately, concerns have arisen following the use of large metal-on-metal bearings in hip replacements owing to reports of catastrophic soft-tissue reactions resulting in implant failure and associated complications. This review examines the literature and contemporary presentations on current clinical dilemmas in metal-on-metal hip replacement.

The rate and mode of early failure in 463 Birmingham hip resurfacings in a two-centre, multisurgeon series were examined. Of the 463 patients two have died and three were lost to follow-up. The mean radiological and clinical follow-up was for 43 months (6 to 90).

We have revised 13 resurfacings (2.8%) including seven for pain, three for fracture, two for dislocation and another for sepsis. Of these, nine had macroscopic and histological evidence of metallosis. The survival at five years was 95.8% (95% confidence interval (CI) 94.1 to 96.8) for revision for all causes and 96.9% (95% CI 95.5 to 98.3) for metallosis.

The rate of metallosis related revision was 3.1% at five years. Risk factors for metallosis were female gender, a small femoral component, a high abduction angle and obesity. We do not advocate the use of the Birmingham Hip resurfacing procedure in patients with these risk factors.

Adverse reaction to wear and corrosion debris is a cause for concern in total hip arthroplasty (THA). Modular junctions are a potential source of such wear products and are associated with secondary pseudotumour formation.

We present a consecutive series of 17 patients treated at our unit for this complication following metal-on-highly cross-linked polyethylene (MoP) THA. We emphasise the risk of misdiagnosis as infection, and present the aggregate laboratory results and pathological findings in this series.

The clinical presentation was pain, swelling or instability. Solid, cystic and mixed soft-tissue lesions were noted on imaging and confirmed intra-operatively. Corrosion at the head–neck junction was noted in all cases. No bacteria were isolated on multiple pre- and intra-operative samples yet the mean erythrocyte sedimentation rate was 49 (9 to 100) and C-reactive protein 32 (0.6 to 106) and stromal polymorphonuclear cell counts were noted in nine cases.

Adverse soft–tissue reactions can occur in MoP THA owing to corrosion products released from the head–neck junction. The diagnosis should be carefully considered when investigating pain after THA. This may avoid the misdiagnosis of periprosthetic infection with an unidentified organism and mitigate the unnecessary management of these cases with complete single- or two-stage exchange.

Cite this article: Bone Joint J 2015;97-B:1024–1030.

Early failure associated with adverse reactions to metal debris is an emerging problem after hip resurfacing but the exact mechanism is unclear. We analysed our entire series of 660 metal-on-metal resurfacings (Articular Surface Replacement (ASR) and Birmingham Hip Resurfacing (BHR)) and large-bearing ASR total hip replacements, to establish associations with metal debris-related failures. Clinical and radiological outcomes, metal ion levels, explant studies and lymphocyte transformation tests were performed. A total of 17 patients (3.4%) were identified (all ASR bearings) with adverse reactions to metal debris, for which revision was required. This group had significantly smaller components, significantly higher acetabular component anteversion, and significantly higher whole concentrations of blood and joint chromium and cobalt ions than asymptomatic patients did (all p < 0.001). Post-revision lymphocyte transformation tests on this group showed no reactivity to chromium or cobalt ions. Explants from these revisions had greater surface wear than retrievals for uncomplicated fractures. The absence of adverse reactions to metal debris in patients with well-positioned implants usually implies high component wear.

Surgeons must consider implant design, expected component size and acetabular component positioning in order to reduce early failures when performing large-bearing metal-on-metal hip resurfacing and replacement.

Surface hip replacement (SHR) is generally used in younger, active patients as an alternative conventional total hip replacement in part because of the ability to preserve femoral bone. This major benefit of surface replacement will only hold true if revision procedures of SHRs are found to provide good clinical results.

A retrospective review of SHR revisions between 2007 and 2012 was presented, and the type of revision and aetiologies were recorded. There were 55 SHR revisions, of which 27 were in women. At a mean follow-up of 2.3 years (0.72 to 6.4), the mean post-operative Harris hip score (HHS) was 94.8 (66 to 100). Overall 23 were revised for mechanical reasons, nine for impingement, 13 for metallosis, nine for unexplained pain and one for sepsis. Of the type of revision surgery performed, 14 were femoral-only revisions; four were acetabular-only revisions, and 37 were complete revisions.

We did not find that clinical scores were significantly different between gender or different types of revisions. However, the mean post-operative HHS was significantly lower in patients revised for unexplained pain compared with patients revised for mechanical reasons (86.9 (66 to 100) versus 99 (96 to 100); p = 0.029). There were two re-revisions for infection in the entire cohort.

Based on the overall clinical results, we believe that revision of SHR can have good or excellent results and warrants a continued use of the procedure in selected patients. Close monitoring of these patients facilitates early intervention, as we believe that tissue damage may be related to the duration of an ongoing problem. There should be a low threshold to revise a surface replacement if there is component malposition, rising metal ion levels, or evidence of soft-tissue abnormalities.

Cite this article: Bone Joint J 2013;95-B, Supple A:88–91.

We systematically reviewed the peer-reviewed literature to relate the survival of hybrid metal-on-metal hip resurfacing arthroplasty devices to a National Institute of Clinical Excellence (NICE) benchmark for choosing a primary total hip replacement, which is a survival rate of 90% at a follow-up of ten years.

A total of 29 articles (10 621 resurfaced hips) met the inclusion criteria. The mean follow-up ranged from 0.6 to 10.5 years and the survival of the implant ranged from 84% to 100%. Of the 10 621 hips, 370 were revised (3.5%), with aseptic loosening as the most frequent mode of failure.

None of the hip resurfacing arthroplasty implants used to date met the full ten-year NICE benchmark of survival. A total of 13 studies showed satisfactory survival compared with the three-year NICE benchmark.