Retained polymethylmethacrylate (PMMA) debris in surgical instrument trays is a rare, but disquieting situation for the arthroplasty surgeon. Although retained debris could be considered to be sterile after autoclaving, there is no peer-reviewed literature to support this assumption. This uncertainty and subsequent fear of contamination from this bioburden often leads to operating room personnel turning over entire surgical tables and opening new surgical instruments, which consumes time and burdens a hospital's sterilization infrastructure. Consequently, the purpose of the current study was to determine if retained, heavily contaminated PMMA in surgical trays could be effectively sterilized through clinically utilized autoclave protocols.

MSSA (Xen36, Perkin Elmer) biofilm was grown on identically sized PMMA (Palacos R) coupons for 72-hour duration. Following incubation, coupons were exposed to three commonly used sterilization protocols. Cobalt-Chrome (CC) coupons were included in the same tray, replicating instruments in proximity to retained PMMA. Autoclave protocols included: 1.) Single Instrument Flash protocol: Pre-vac, 270° F, 10 min exposure, 1 min drying, 2.) One Tray OR protocol: Pre-vac, 270° F, 4 min exposure, 1 min drying, and 3.) Standard Post-Operative protocol: Pre-vac, 270° F, 10 min exposure, 60 min drying. Control coupons did not undergo autoclaving. Coupons were then sonicated for 30 minutes in tryptic soy broth and plated to count CFUs. Experiments were performed in quadruplicate.

Control coupons showed significant contamination with CFU counts in the range of 10⁶ CFU/mL. CFU counts of zero across all autoclaved PMMA and CC coupons revealed that each protocol was effective in completely eradicating culturable S. aureus, confirming clinical efficacy on orthopaedic cement sterilized in surgical trays.

Our findings demonstrate that heavily contaminated PMMA and exposed metal in surgical trays can be effectively sterilized through several autoclaving protocols.

Clinicians should feel confident in the efficacy of autoclave protocols in removing bacteria and its associated biofilm from othopaedic materials.

Aims

Periprosthetic femoral fractures (PFF) following total hip arthroplasty (THA) are devastating complications that are associated with functional limitations and increased overall mortality. Although cementless implants have been associated with an increased risk of PFF, the precise contribution of implant geometry and design on the risk of both intra-operative and post-operative PFF remains poorly investigated. A systematic review was performed to aggregate all of the PFF literature with specific attention to the femoral implant used.