Since the Oxford knee was first used unicompartmentally in 1982, a small number of bearings have fractured. Of 14 retrieved bearings, we examined ten samples with known durations in situ (four Phase 1, four Phase 2 and two Phase 3). Evidence of impingement and associated abnormally high wear (> 0.05 mm per year) as well as oxidation was observed in all bearings. In four samples the fracture was associated with the posterior radio-opaque wire. Fracture surfaces indicated fatigue failure, and scanning electron microscopy suggested that the crack initiated in the thinnest region. The estimated incidence of fracture was 3.20% for Phase 1, 0.74% for Phase 2, 0.35% for Phase 3, and 0% for Phase 3 without the posterior marker wire. The important aetiological factors for bearing fracture are impingement leading to high wear, oxidation, and the posterior marker wire. With improved surgical technique, impingement and high wear should be prevented and modern polyethylene may reduce the oxidation risk. A posterior marker wire is no longer used in the polyethylene meniscus. Therefore, the rate of fracture, which is now very low, should be reduced to a negligible level.

We present a comparison of the results of the Oxford unicompartmental knee arthroplasty in patients younger and older than 60 years of age. The ten-year all-cause survival of the < 60 years of age group (52) was 91% (95% confidence interval (CI) 12), while in the ≥ 60 years of age group (512), the figure was 96% (95% CI 3). For the younger group, the mean Hospital for Special Surgery score at ten-year follow-up (n = 21) was 94 of 100, compared with a mean of 86 of 100 for the older group (n = 135). The results show that the Oxford unicompartmental arthroplasty can achieve ten-year results that are comparable to total knee arthroplasty in patients < 60 years of age. We conclude that for patients aged over 50, age should not be considered a contraindication for this procedure.