Sequentially annealed highly crosslinked polyethylenes (HXLPEs) were introduced in total knee replacement (TKR) starting in 2005 to reduce wear and particle-induced osteolysis. Few studies have reported on the clinical performance of HXLPE knees. In this study, we hypothesized that due to the reduced free radicals, sequentially annealed HXLPE would have lower oxidation levels than gamma inert-sterilized controls. 145 tibial components were retrieved at consecutive revision surgeries at 7 different surgical centers. 74 components were identified as sequentially annealed HXLPE (X3, Stryker) while the remainder (n = 71) were conventional gamma inert sterilized polyethylene. The sterilization method was confirmed by tracing the lot numbers by the manufacturer. The conventional inserts were implanted for 1.7 years (Range: 0.0–9.3 years), while the X3 components were implanted 1.1 years (Range: 0.0–4.5 years). Surface damage was assessed using the Hood method. Oxidation analysis was performed in accordance with ASTM 2102 following submersion in boiling heptane for 6 hours to remove absorbed lipids. 30 of the conventional and 29 of the HXLPE inserts were available for oxidation analysis.Introduction
Methods