When reversing the hard-soft articulation in inverse shoulder replacement, i.e. hard inlay and soft glenosphere, the tribological behaviour of such a pairing has to be tested thoroughly. Therefore, two hard materials for the inlay, CoCr alloy and alumina toughened zirconia ceramic (ATZ) articulating on two soft materials, conventional UHMWPE and vitamin E stabilised, highly cross-linked PE (E-XLPE) were tested. The simulator tests were performed analogue to standardised gravimetric wear tests for hip prosthesis (ISO 14242-1) with load and motion curves adapted to the shoulder. The test parameters differing from the standard were the maximum force (1.0 kN) and the range of motion. A servo-hydraulic six station joint simulator (EndoLab, Rosenheim) was used to run the tests up to 5 times 106 cycles with diluted calf serum at 37° C as lubricant.Background
Methods
When reversing the hard-soft articulation in inverse shoulder replacement, i.e. hard inlay and soft glenosphere (cf. Figure 1), the tribological behaviour of such a pairing has to be tested thoroughly. Therefore, two hard materials for the inlay, CoCr alloy and alumina toughened zirconia ceramic (ceramys®) articulating on two soft materials, conventional UHMWPE and vitamin E stabilised, highly cross-linked PE (vitamys®) were tested in a joint simulator. The simulator tests were performed at Endolab GmbH, Rosenheim, Germany, analogue to standardised gravimetric wear tests for hip prosthesis (ISO 14242-1) with load and motion curves adapted to the shoulder. The test parameters differing from the standard were the maximum force (1.0 kN) and the range of motion. A servo-hydraulic six station joint simulator (EndoLab) was used to run the tests up to 5*106 cycles with diluted calf serum at 37° C as lubricant. Visual inspection and mass measurements were done at 0.1, 0.5, 1, 2, 3, 4 and 5 million cycles using a high precision scale and a stereo microscope, respectivly.Background
Methods