Introduction: The aim of this study is to investigate whether MoM implants result in more chromosome aberrations and increased blood metal ions post-operatively when compared to MoP implants. Large head metal-on-metal articulating surfaces of the hip are being used in increasing numbers of patients for oncological purposes due to the increased stability and reduced dislocation rate. Recent studies have raised many concerns over possible genotoxicity of MoM implants. Methods: This is a prospective study of patients who have undergone elective total hip replacement. Patients were randomised into two groups (MoP and MoM). Patients are reviewed pre-operatively (control group), at 3 months, 6 months, 1 year and 2 years post-operatively. On each occasion blood tests are taken to quantify metal ion levels (chromium, cobalt, titanium, nickel and vanadium) using HR-ICPMS and chromosome aberrations in T lymphocytes using 24 colour fluorescent in situ hybridisation (FISH). Results: 24 patients had MoP prosthesis and 29 a MoM. Cobalt and chromium concentration increased during the first 6 months in both MoM and MoP groups, in the MoM group the chromium levels were twice that of MoP group and 12x that of the preoperative samples. There was no difference with the levels of titanium, nickel and vanadium. Chromosome aberrations occurred in both groups. At 6 months both the MoM and MoP groups showed increase frequency of aneuploidy aberrations with further increases after one year. Structural damage in the form of translocations occurred in the MoM group after one year, but not in the MoP group. Discussion: Results of this study show that the levels of chromium and cobalt are significantly higher in the MoM group compared to the MoP group. This corresponds to increases in chromosome aberrations between the groups particularly in aneuploidy and translocations present in the MoM group at 1 year

Introduction. The identification of biological markers associated to implant failure in THA (total hip arthroplasty) patients remains a challenge in orthopedic surgery. In this search, previous studies have been mainly focused on typical mediators associated to bone metabolism and inflammation. Our group has evaluated changes in serum levels of insulin-like growth factor binding protein-1 (IGFBP-1), a protein which is not directly related to bone homeostasis, in patients undergoing THA. Method. We assessed IGFBP-1 levels in serum obtained from 131 patients (58% female, 42 % male; age: 68 ± 13 years) who underwent THA in the Orthopedic Surgery and Traumatology Department of our institution. In this cohort, 57% of patients had metal on polyethylene (MoP) as hip-bearing surface combination, 17 % had ceramic on ceramic (CoC) and 26% of them did not have any prosthesis. A test based on an enzyme-linked immunosorbent assay (ELISA) was used to determine IGFBP-1 levels in serum obtained from these patients. Result. Our results showed a significant increase in IGFBP- 1 levels in MoP group as compared to CoC and control groups, in which no differences in quantified levels were detected. Further analysis revealed no significant differences in IGFBP-1 between cemented and non-cemented MoP bearings. We performed a ROC curve to evaluate the accuracy of serum IGFBP-1 in discriminating MoP from the rest of patients (area under the curve: 0.7; 95% confidence interval: 0,6-0.8; p<0.05) and established a cut-off value of 10.2 ng/ml, according to the Youden´s Index. Logistic regression analysis showed that patients with MoP bearing surfaces had a higher risk of increased IGFBP- 1 levels in serum (p<0.05, Odds Ratio: 6.7, 95% Confidence Interval 3.1 to 14.8). Conclusion. IGFBP- 1 levels are significantly elevated in THA patients with MoP bearing surfaces, suggesting that this protein might be a reliable biomarker for the outcome of patients implanted with MoP

In metal-on-polyethylene (MoP) THA large femoral metal heads are designed to increase stability and to reduce dislocation risk. The increased head size could lead to increased taper corrosion with the release of metal ions and adverse reactions. Using blood ion measurements, we aimed to investigate the association between femoral head size and metal-ion release after MoP THA. 96 patients were enrolled at two centers and randomized to receive either a 32-mm metal head or a 36–44 mm metal head (the largest possible fitting the thinnest available polyethylene insert). Blood metal ions and PROMs (OHS, UCLA) were measured at two- and five-year follow-ups. Both 2- and 5-year median chrome, cobalt, and titanium levels were below taper corrosion indicative ion levels. At 5 years, median chrome, cobalt, and titanium levels were 0.5 μg/L (0.50–0.62), 0.24 μg/L (0.18–0.30), and 1.16 μg/L (1.0–1.68) for the 32-mm group, and 0.5 μg/L (0.5–0.54), 0.23 μg/L (0.17–0.39), and 1.30 μg/L (1–2.05) for the 36–44 mm group, with no difference between groups (p=0.825, p=1.000, p=0.558). At 2 years, 7 (32-mm) versus 4 (36–44-mm) patients had elevated ions. At 5 years, 6 (32-mm) versus 7 (36–44-mm) patients had elevated ions. There was no difference in either OHS (p=0.665) or UCLA (p=0.831) between patients with or without elevated blood metal ions. 5 years after the insertion of MoP THAs, we found no differences in the blood metal ion levels between 32 mm heads and 36–44 mm heads and no corrosion-related revisions. As taper corrosion can debut after 5 years, there is still a need for long-term follow-up studies on the association between head size and corrosion in MoP THA

Objectives. T-cells are considered to play an important role in the inflammatory response causing arthroplasty failure. The study objectives were to investigate the composition and distribution of CD4+ T-cell phenotypes in the peripheral blood (PB) and synovial fluid (SF) of patients undergoing revision surgery for failed metal-on-metal (MoM) and metal-on-polyethylene (MoP) hip arthroplasties, and in patients awaiting total hip arthroplasty. Methods. In this prospective case-control study, PB and SF were obtained from 22 patients (23 hips) undergoing revision of MoM (n = 14) and MoP (n = 9) hip arthroplasties, with eight controls provided from primary hip osteoarthritis cases awaiting arthroplasty. Lymphocyte subtypes in samples were analysed using flow cytometry. Results. The percentages of CD4+ T-cell subtypes in PB were not different between groups. The CD4+ T-cells in the SF of MoM hips showed a completely different distribution of phenotypes compared with that found in the PB in the same patients, including significantly decreased CD4+ T-central memory cells (p < 0.05) and increased T-effector memory cells (p < 0.0001) in the SF. Inducible co-stimulator (ICOS) was the only co-stimulatory molecule with different expression on CD4+ CD28+ cells between groups. In PB, ICOS expression was increased in MoM (p < 0.001) and MoP (p < 0.05) cases compared with the controls. In SF, ICOS expression was increased in MoM hips compared with MoP hips (p < 0.05). Conclusions. Increased expression of ICOS on CD4+ T-cells in PB and SF of patients with failed arthroplasties suggests that these cells are activated and involved in generating immune responses. Variations in ICOS expression between MoM and MoP hips may indicate different modes of arthroplasty failure. Cite this article: Professor P. A. Revell. Increased expression of inducible co-stimulator on CD4+ T-cells in the peripheral blood and synovial fluid of patients with failed hip arthroplasties. Bone Joint Res 2016;5:52–60. doi: 10.1302/2046-3758.52.2000574

Background. Adverse local tissue reactions (ALTR) in metal-on-polyethylene (MoP) total hip arthroplasty (THA) with head-neck taper corrosion is likely to be multifactorial involving implant and patient factors. However, there is a paucity of clinical data on implant parameters as predisposing factors in MoP head-neck taper corrosion. The aim of this study was to identify any potential implant factors associated with failed MoP THA due to head-neck taper corrosion. Methods. A total of 67 MoP THA patients in two groups was investigated: 1) ALTR (n=38) on MARS MRI and 2) non-ALTR (n=29) on MARS MRI. All patients had highly cross-linked polyethylene liners with cobalt-chromium femoral heads with a single head-neck modularity. Parameters compared between groups included: acetabular component orientation, femoral neck shaft angle, radiographic measurement of medial and vertical femoral offsets, limb length discrepancy, component size, femoral head offset, implant type, femoral stem alloy and taper design. Results. The occurrence of ALTR was associated with increased femoral head offset (non-ALTR vs. ALTR, 0.5 ± 3.7 vs. 4.1 ± 3.6, p = 0.008), increased radiographic femoral stem offset (35.9 ± 7.4 mm vs 40.7 ± 7.1mm, p = 0.018), and the use of TMZF alloy stems (p = 0.051). The presence of ALTR was significantly associated with higher cobalt (9.1 µg/L vs. 0.4µg/L, p=0.001) and chromium (2.6µg/L vs. 0.4µg/L). A significant correlation was identified between the serum cobalt level and the femoral stem offset (R=0.375, p=0.009). Conclusions. Although the occurrence of head-neck taper corrosion in MoP THA is likely to be an interplay between implant and patient factors, the results of this study identified increased femoral head and stem offset and the use of TMZF alloy stems as risk factors associated with clinically relevant ALTR due to head-neck taper corrosion in MoP THA patients. The study provides evidenced-based information in risk stratification of symptomatic MoP THA patients for head-neck taper corrosion. For any tables or figures, please contact the authors directly

Objectives. Hips with metal-on-metal total hip arthroplasty (MoM THA) have a high rate of adverse local tissue reactions (ALTR), often associated with hypersensitivity reactions. Dynamic contrast-enhanced magnetic resonance imaging (DCE-MRI) measures tissue perfusion with the parameter Ktrans (volume transfer constant of contrast agent). Our purpose was 1) to evaluate the feasibility of DCE-MRI in patients with THA and 2) to compare DCE-MRI in patients with MoM bearings with metal-on-polyethylene (MoP) bearings, hypothesising that the perfusion index Ktrans in hips with MoM THA is higher than in hips with MoP THA. Methods. In this pilot study, 16 patients with primary THA were recruited (eight MoM, eight MoP). DCE-MRI of the hip was performed at 1.5 Tesla (T). For each patient, Ktrans was computed voxel-by-voxel in all tissue lateral to the bladder. The mean Ktrans for all voxels was then calculated. These values were compared with respect to implant type and gender, and further correlated with clinical parameters. Results. There was no significant difference between the two bearing types with both genders combined. However, dividing patients by THA bearing and gender, women with MoM bearings had the highest Ktrans values, exceeding those of women with MoP bearings (0.067 min. −1. versus 0.053 min. −1. ; p-value < 0.05) and men with MoM bearings (0.067 min. −1. versus 0.034 min. −1. ; p-value < 0.001). Considering only the men, patients with MoM bearings had lower Ktrans than those with MoP bearings (0.034 min. −1. versus 0.046 min. −1. ; p < 0.05). Conclusion. DCE-MRI is feasible to perform in tissues surrounding THA. Females with MoM THA show high Ktrans values in DCE-MRI, suggesting altered tissue perfusion kinematics which may reflect relatively greater inflammation. Cite this article: Dr P. E. Beaule. Perfusion MRI in hips with metal-on-metal and metal-on-polyethylene total hip arthroplasty: A pilot stud. Bone Joint Res 2016;5:73–79. DOI: 10.1302/2046-3758.53.2000572

Introduction. Metal-on-polyethylene (MoP) is the most commonly used bearing couple in total hip replacements (THRs). Retrieval studies (Cooper et al, 2012, JBJS, Lindgren et al, 2011, JBJS) report adverse reactions to metal debris (ARMD) due to debris produced from the taper-trunnion junction of the modular MoP THRs. A recent retrospective observational study (Matharu et al, 2016, BMC Musc Dis) showed that the risk of ARMD revision surgery is increasing in MoP THRs. To the authors' best knowledge, no hip simulator tests have investigated material loss from the taper-trunnion junction of contemporary MoP THRs. Methods. A 6-station anatomical hip joint simulator was used to investigate material loss at the articulating and taper-trunnion surfaces of 32mm diameter metal-on-cross-linked polyethylene (MoXLPE) joints for 5 million cycles (Mc) with a sixth joint serving as a dynamically loaded soak control. Commercially available cobalt-chromium-molybdenum (CoCrMo) femoral heads articulating against XLPE acetabular liners (7.5Mrad) were used with a diluted new-born-calf-serum lubricant. Each CoCrMo femoral head was mounted on a 12/14 titanium alloy trunnion. The test was stopped every 0.5Mc, components were cleaned and gravimetric measurements performed following ISO 14242-2 and the lubricant was changed. Weight loss (mg) obtained from gravimetric measurements was converted into volume loss (mm. 3. ) and wear rates were calculated from the slopes of the linear regression lines in the volumetric loss versus number of cycles plot for heads, liners and trunnions. Additionally, volumetric measurements of the head tapers were obtained using a coordinate measuring machine (CMM) post-test. The surface roughness (Sa) of all heads and liners was measured pre and post-test. At the end of the test, the femoral heads were cut and the roughness of the worn and unworn area was measured. Statistical analysis was performed using a paired-t-test (for roughness measurements) and an independent sample t-test (for wear rates). Results and Discussion. The mean volumetric wear rates for CoCrMo heads, XLPE liners and titanium trunnions were 0.019, 2.74 and 0.013 mm. 3. /Mc respectively. There was a statistically significant decrease (p<0.001) in the Sa of the liners post-test. This is in contrast to the femoral heads roughness in which no change was observed (p = 0.338). This head roughness result matches with a previous MoP in vitro test (Saikko, 2005, IMechE-H). The Sa of the head tapers on the worn area showed a statistically significant increase (p<0.001) compared with unworn, with an associated removal of the original machining marks. The mean volumetric wear rate of the head tapers obtained using the CMM (0.028 ± 0.016 mm. 3. /Mc) was not statistically different (p=0.435) to the mean volumetric wear rate obtained gravimetrically (0.019 ± 0.020 mm. 3. /Mc) for the femoral heads. Therefore, wear of the heads arose mainly from the internal taper. The mean wear rates of the CoCrMo taper and titanium trunnion are in agreement with a MoP explant study (Kocagoz et al, 2016, CORR). Conclusion. This is the first long-term hip simulator study to report wear generated from the taper-trunnion junction of MoP hips

We questioned about bearing surface and infection in two populations of patients who had bilateral THA with different bearings performed in the same hospital by the same surgical team from the year 1981 to the year 2010 (mean followup 15 years; 7 to 35). 1) first population (mean age 32 years): 325 patients (650 hips) with sickle cell disease (SCD) with two different bearing on each side. 116 patients had Metal on PE (MoP) on one side and Ceramic on PE (CoP) on the contralateral; 106 patients had (CoP) and Ceramic on Ceramic (CoC); 103 patients had MoP and CoC. 2) matched control population (same age, same period) of 820 patients without co-morbidities: 354 patients had MoP and CoP; 237 had CoP and CoC; 229 had MoP and CoC. Among the 2290 hips, 3 early (less than 12 months) unilateral infections (2 in the controls, 1 in the SCD), and 59 late unilateral infections: 23 (1.4%) in 1640 THAs control, versus 36 (5.5%) in the SCD 650 THAs (P < 0.0001) during the observation period of 35 years. In control group with the Kaplan-Meier analysis, increase infections over time but different (p=0.02) for each bearing surfaces, respectively from 0% at one year to 0.4% revision (2 cases) at most recent follow-up for 466 CoC hips, from 0% to 1.1% (7 cases) for 591 CoP hips, and from 0.3% to 2.4% (14 cases) for 583 MoP hips. In sickle cell disease group MoP hips had higher risk of infection (26 among 219) when compared with CoP (9 among 222; p=0.002), and CoC (1 among 209 hips; p=0.0004); with increase over time from 1% at one year to 4% with CoP, and from 1% to 11.8% with MoP. When contralateral hip of same patient is control, PE components are more prone to infection than those involving ceramic-on-ceramic

Objectives. To quantify and compare peri-acetabular bone mineral density (BMD) between a monoblock acetabular component using a metal-on-metal (MoM) bearing and a modular titanium shell with a polyethylene (PE) insert. The secondary outcome was to measure patient-reported clinical function. Methods. A total of 50 patients (25 per group) were randomised to MoM or metal-on-polyethlene (MoP). There were 27 women (11 MoM) and 23 men (14 MoM) with a mean age of 61.6 years (47.7 to 73.2). Measurements of peri-prosthetic acetabular and contralateral hip (covariate) BMD were performed at baseline and at one and two years’ follow-up. The Western Ontario and McMaster Universities osteoarthritis index (WOMAC), University of California, Los Angeles (UCLA) activity score, Harris hip score, and RAND-36 were also completed at these intervals. Results. At two years, only zone 1 showed a loss in BMD (-2.5%) in MoM group compared with a gain in the MoP group (+2.2%). Zone 2 showed loss in both groups (-2.2% for MoM; -3.9% for MoP) and zones 3 and 4 a gain in both groups (+0.1% for MoM; +3.3% for MoP). No other between-group differences were detected. When adjusting for BMD of the contralateral hip, no differences in BMD were observed. The only significant differences in functional scores at two years were higher UCLA activity (7.3 (. sd. 1.2) vs 6.1 (. sd. 1.5); p = 0.01) and RAND-36 physical function (82.1 (. sd. 13.0) vs 64.5 (. sd. 26.4); p = 0.02) for MoM bearings versus MoP. One revision was performed in the MoM group, for aseptic acetabular loosening at 11 months. Conclusions. When controlling for systemic BMD, there were no significant differences between MoM and MoP groups in peri-acetabular BMD. However, increasing reports of adverse tissue reactions with large head MoM THR have restricted the use of the monoblock acetabular component to resurfacing only

Introduction. Adverse local tissue reactions (ALTR) can result in devastating soft tissue and osseous destruction, while potentially increasing the risk of concomitant periprosthetic joint infection (PJI). The aims of this study were to evaluate cobalt (Co) and chromium (Cr) levels generated in simulators from metal-on-polyethylene (MoP) and ceramic-on-polyethylene (CoP) constructs, and determine their impact on native tissues and PJI risk through evaluation of human adipose-derived mesenchymal stem cells (AMSCs) and Staphylococcus epidermidis isolates. Methods. Ten hip simulator constructs were assembled with 36-mm high-offset femoral heads, highly cross-linked polyethylene liners, and titanium stems. Five constructs used CoCr femoral heads and five used ceramic. Constructs were submerged in bovine serum (BS) and run for 1,000,000 cycles. Samples of BS were collected and evaluated for CoCr concentration. Various concentrations of CoCr were chosen for further assessment of cytotoxicity and growth impact on AMSCs and S. epidermidis and compared to inert SiO2. Results. After 1,000,000 cycles, mean MoP and CoP Co concentration was 2264 ng/mL and 0.6 ng/mL, respectively (p<0.001). Mean MoP and CoP Cr concentration was 217 ng/mL and 4.3 ng/mL, respectively (p<0.001). Mean MoP Co:Cr ratio was 10. Co nanoparticles were significantly more toxic to human AMSCs than control SiO2 in a dose-response manner (p<0.001). S. epidermidis growth was not significantly impacted by Co concentrations derived from the simulators. Conclusions. MoP constructs built in ideal conditions generated substantial CoCr debris, highlighting a baseline risk with these implants that may be exacerbated by host factors or imperfect surgical technique. Evaluation of impact on AMSCs suggests that debris levels produced under ideal conditions can be cytotoxic. Additionally, these concentrations did not potentiate or inhibit S. epidermidis growth, suggesting elevated PJI rates with ALTR may be related to other factors potentially associated with tissue necrosis. For any tables or figures, please contact the authors directly

Introduction. Dislocation is one of the leading causes of revision after primary total hip arthroplasty (THA). Polyethylene wear is one of the risk factors for late dislocations (>2 years). It can induce an inflammatory response resulting in distension and thinning of the pseudocapsule, predisposing the hip to dislocation. Alternatively, eccentric seating of the femoral head in a worn out socket may result in an asymmetric excursion arc predisposing the hip to impingement, levering out and dislocation. Highly cross linked polyethylene has a significantly lower wear rate as compared to conventional polyethylene. Incidence of late dislocations has been shown to be significantly greater with conventional polyethylene bearings as compared to ceramic bearings. However, there is no literature comparing the risk of dislocation between ceramic- on- ceramic (CoC) bearings with metal/ceramic- on- cross linked polyethylene (M/CoP) bearings and this was the aim our study. Methods. Data regarding revision for dislocation after primary THA for osteoarthritis (OA) between September 1999 and December 2013 was obtained from the Australian Orthopaedic Association National Joint Replacement Registry (AOA NJRR). Revision risk for dislocation was compared between CoC, CoP, and MoP bearings. Only those THAs with 28 mm, 32 mm, or 36 mm heads were included in the study. Results. The numbers at risk (0 years) in the CoC, CoP, and MoP groups were 53,648; 23,746; and 90,040 THAs respectively. The overall revision (dislocation)/100 observed years was 0.13. Revision rate/100 observed years in the CoC, CoP, and MoP groups was 0.12, 0.12, and 0.16 respectively. The cumulative percentage revision for dislocation (CPRD) for the three bearing types is shown in figure 1. The CPRD at 12 years in the CoC, CoP, and MoP groups was 0.9, 1.0 and 1.2 respectively. The rise in CPRD between 2 and 12 years (late dislocations) was 0.4, 0.6, and 0.6 in the CoC, CoP, and MoP groups respectively (Figure 1). The age and gender adjusted hazards ratio (HR) for revision for dislocation in CoC vs. CoP groups was 1.05 (p=0.684, 1month+); in MoP vs. CoP group was 1.45 (p<0.001, entire period) and MoP vs. CoC group was 1.55 (p<0.001, 6 month+). Computation of age and gender adjusted HR comparing the three bearing groups after stratification according to head sizes (28 mm, 32 mm and 36 mm) showed no significant difference in HR after 3 months (p≥0.061). Conclusion. The revision (dislocation)/100 observed years was greater in the MoP group as compared to CoC and CoP groups (MoP > CoC = CoP). The age and gender adjusted HR (revision for dislocation) was significantly greater in the MoP group as compared to CoC and CoP groups after 6 months. However, when the data was stratified according to head sizes, the age and gender adjusted HR was similar between the three bearing groups after 3 months. In conclusion, there is no significant difference in the risk of revision for dislocation between CoC, CoP, and MoP bearings after adjusting for age, gender, and head size after 3 months

Prosthetic joint infections (PJI) are a devastating consequence in total hip arthroplasties (THA) with both significant morbidity and sometimes mortality, posing a significant health economic burden. Studies, both clinical and in-vitro have suggested possible reduction in PJI with the use of ceramic bearings. We have investigated the relationship of ceramic-on-ceramic (CoC), ceramic-on-polyethylene (CoP) or metal-on-polyethylene (MoP) bearing surface in affecting outcome of revision surgery after primary THA using data collected from National Joint Registry for England and Wales, Northern Ireland and the Isle of Man between 2002 and 2016. We used a competing risk regression model to investigate predictors of each revision outcome, such as infection, dislocation, aseptic revision and all cause revisions. The results were adjusted for age, gender, ASA grade, BMI, indication for surgery, intraoperative complications and implant data. We identified 456,457 THA (228,786 MoP, 128,403 CoC and 99,268 CoP). In a multivariable model, the adjusted risk of revision for PJI was lower with CoC (OR-0.748, p<0.001) and CoP (OR-0.775, p<0.001) when compared to MoP bearing. Additionally there was also a significant reduction in the risk of all cause revision for CoC (OR-0.918, p=0.002) and CoP (0.806, p<0.001), bearings as compared with MoP. The protective effect of ceramic bearing was predominantly seen after two years of implantation with a significant (p<0.0001) reduction of revision for PJI in both CoC (by 42.8%) and CoP (by 41.3%) group. Similarly significant effect was seen for aseptic revision beyond two years and overall all cause revision rate beyond two years reduced by 21.6% for CoC and 27.1% for CoP (p<0.001). Within the limits of registry analysis, this study has demonstrated an association between the use of ceramic bearing and lower rates of revision for all cause revisions especially infection and aseptic loosening. This finding supports the use of ceramic bearings in THA

Introduction. Numerous studies have reported on clinically significant volumes of material loss and corrosion at the head-stem junction of metal-on-metal (MOM) hips; less is understood about metal-on-polyethylene (MOP) hips. We compared the effect of bearing type (MOM vs MOP) on taper material loss for a hip system of a single design (DePuy Pinnacle). Methods. We recruited retrieved MOM (n=30) and MOP (n=22) bearing hips that were consecutively received at our centre. We prospectively collected associated clinical and imaging data. We measured the severity of corrosion and volumes of material loss at each head taper surface and used multivariate statistical analysis to investigate differences between the two bearing types. Results. The median rate of material loss for the MOM and MOP groups was 0.81 mm. 3. /year (0.01–3.45) and 0.03 mm. 3. /year (0–1.07) respectively (p<0.001). 29 out of 30 MOM hips were revised for adverse metal reactions, compared with 1 out of 22 MOP hips. Discussion. MOP hips lost significantly less material from their taper junctions than MOM hips. We suggest that the metal-metal interaction at the bearing surface of MOM hips enhances the corrosive environment at the head-stem junction. Conclusion. Our results can reassure patients with MOP Pinnacle hips that they are unlikely to experience clinically significant problems related to material loss from the taper junction

INTRODUCTION. Metallic ion release may be related to bearing surface wear and thus serve as an indicator of in-vivo performance of metal on metal (MOM) articulations. OBJECTIVES. Compare large head MOM hip components with modular MOM and metal on polyethylene (MOP) to determine their relative effects on serum metal ion levels. METHODS. A prospective controlled trial to compare clinical, radiographic, and serum metal ion concentration (Co and Cr) results between the Large Head ASR XL System (MOM-1), the Ultamet Advanced Modularity System (MOM-2), and the Pinnacle Acetabular Cup System with polyethylene liner (MOP). We enrolled 151 consecutive patients (MOM-1 = 97, MOM-2 = 22, MOP = 32). Radiographs, clinical scores (Harris Hip and WOMAC), and serum ion level assessments (in Parts Per Billion - PPB) were performed pre-operatively and post-operatively (6, 12, and 24 months for all patients and 60 months for MOM-1). At 60 months, we compared WOMAC, Harris Hip scores and serum ion levels (Co and Cr) from MOM-1 (revisions excluded) to 24 month scores from MOM-2 and MOP. After revision, serum ion levels were measured at 1, 3, 6, and 12 months. RESULTS. In MOM-1, 11 patients had significantly elevated ion levels at all postoperative periods (Co AVG 130.35 PPB and Cr AVG 61.46 PPB) after 2 years. Excluding outliers and revised patients, average serum ion levels in the 86 remaining MOP-1 patients at 24 and 60 months were statistically higher than MOP and MOM-2 patients. However, this difference was not clinically relevant (no symptoms, no revisions, Co and Cr AVG below 5 PPB). Table 1. Nine hips (9.3%) in 8 MOM-1 patients required revision and serum ion levels decreased rapidly post-up, but have still not returned to baseline after 1 year. Serum ion levels were not significantly different between MOM-2 and MOP groups at any time. Clinical scores improved after surgery in all groups and continued to improve in MOM-2 and MOP patients after 2 years, but decreased slightly in the MOM-1 patients at 2 and 5 years. Average cup inclination angle did not differ significantly between the groups: MOM-1 50.2, MOM-2 47.8, and MOP 51.7. CONCLUSIONS. We are presenting 5 years of prospectively collected data comparing ion levels among 2 MOM and 1 MOP group, as well as post revision ion levels at 1 year. Average serum ion levels were elevated at all post-operative periods in the MOM-1 group, but this was attributable to significantly elevated levels in a subset of outliers that ultimately required revision. Excluding these outliers, there is a statistically significant but clinically irrelevant difference in post-operative ion levels between MOM-1 vs. MOM-2 and MOP. There was no radiographic evidence of component malposition or aseptic loosening in any group. MOM-2 and MOP performed comparatively across all variables. We present an algorithm to diagnose and manage patients with MOM THA (Yable 2.) and offer evidence that metal ion levels do decrease after revision. Table 3

Trunnionosis, due to mechanical wear and/or corrosion at the head stem taper junction, can occur in metal on polyethylene (MOP) hip implants. In some patients this results in severe soft tissue destruction or Adverse Reaction to Metal Debris (ARMD). The amount of material required to cause ARMD is unknown but analyses of retrieved hips may provide the answer to this clinically important question. We collected implants from 20 patients with failed hips with MOP bearings, revised due to ARMD. We collected clinical, imaging and blood test data. We graded the severity of taper corrosion (1 to 4), and quantified the volume of material loss from this junction. We compared our results with previous data collected for metal-on-metal (MOM) hips. The median time to revision of the MOP hips was 51.3 (23.1–56.4) months. All head tapers were moderately to severely corroded with a median corrosion score of 4. The median (range) of total material loss at the taper of the MOP hips was 3.9 mm. 3. (2.96 – 7.85 mm. 3. ) and the material loss rate was 1.4 mm. 3. / year (0.56 – 1.82). Comparison with MOM hips revealed no significant difference in taper material loss (p=0.7344) with a median rate of 0.81 mm. 3. / year (0.01–3.45). We are the first to quantify the volume of material loss at the head taper of hip implants with MOP bearings that were revised due to trunnionosis. This data indicates that a clinically significant dose of cobalt and chromium to induce ARMD is approximately 1.4 mm. 3. / year. We have identified a clinically significant volume of taper material loss in MOP hips

Background. Distal femoral replacements (DFR) are used in children for limb-salvage procedures after bone tumor surgery. These are typically modular devices involving a hinged knee axle that has peripheral metal-on-polyethylene (MoP) and central metal-on-metal (M-M) articulations. While modular connections and M-M surfaces in hip devices have been extensively studied, little is known about long-term wear or corrosion mechanisms of DFRs. Retrieved axles were examined to identify common features and patterns of surface damage, wear and corrosion. Methods. The cobalt chromium alloy axle components from 13 retrieved DFRs were cleaned and examined by eye and with a stereo microscope up to 1000× magnification. Each axle was marked into 6 zones for visual inspection: the proximal and distal views, and the middle (M-M) and 2 peripheral (MoP) zones. The approximate percentage of the following features were recorded per zone: polishing, abrasion or scratching, gouges or detectable wear, impingement wear (i.e. from non- intentional articulation), discoloration and pitting. Results. In each case, the middle M-M zones showed more damage features compared with peripheral MoP zones. Brown discoloration, presumably due to tribofilm deposits, was the predominant M-M area feature, particularly at the junction between the MoP and M-M zones. Higher magnification showed areas of polishing underlying the discoloration, suggesting repetitive removal of the surface metal and re-deposition of tribofilms (Fig 2B). 9 cases demonstrated reflective patches resembling “thumbprint” or “fish scale” markings, which, under higher magnification, showed signs of scratching and grooving in a radial pattern (Figs 2D, 3A). Pits were occasionally present but appeared to be from third-body damage as signs of corrosion were absent. Features that resembled carbides, sometimes with associated “comet” patterns of scratching were apparent under higher magnification in some areas. The MoP zones showed variable scratching, abrasion and wear polishing. The MoP to M-M junctional areas were demarcated by a distinct band corresponding, in some cases, to a narrow wear groove or gouge. 3 axles showed evidence of severe impingement wear on one proximal end. Discussion. This study of retrieved axle components demonstrated varying types of surface wear damage but no clear evidence of corrosion. This is presumably because these parts are in nearly constant motion during gait. Third-body damage may have resulted from the breakdown of surface carbides, leading to scratching, abrasion and wear polishing under high contact stress. Severe impingement wear presumably occurred after catastrophic damage to the polyethylene bushings, allowing eccentric loading and extensive metal wear. The components were revised for a range of clinical reasons including aseptic loosening and the need to expand the prosthesis during growth. With the exception of the few cases with severe impingement, it is unlikely that the wear features seen here contributed to the need for revision. While it was reassuring that corrosion was not a prominent feature of these modular M-M articulations, retrieval analysis of DFR components should be continued to confirm this finding, better document the in vivo wear processes and point to design features that might be improved for future patients. For any figures or tables, please contact the authors directly

This study assesses the incidence of noise in ceramic on ceramic (COC) bearings compared to metal on polyethylene (MOP) bearings. Noise after MOP implants has rarely been studied and they never been linked to squeaking. We have developed a noise characterising hip questionnaire and sent it along with the Oxford Hip Score (OHS) to 1000 patients; 509 respondents, 282 COC and 227 MOP; median age 63.7 (range 45–92), median follow up 2.9 years (range 6–156 months). 47 (17%) of the COC patients reported noise compared to 19 (8%) of the MOP patients (P=0.048). 9 COC and 4 MOP patients reported their hip noise as squeaking. We found the incidence of squeaking in the COC hips to be 3.2% compared to 1.8% in the MOP hips. Overall, 27% patients with noise reported avoiding recreational activities because of it and patient's with noisy hips scored on average 4 points less in the OHS (COC: P=0.04 and MOP: P =0.007). This is the first study to report squeaking from MOP hip replacements. We therefore believe the squeaking hip phenomenon is not exclusive to hard bearings. Surprisingly, only a small proportion of patients described nose from their as a ‘squeak’. Noisy hip implants may have social implications, and patients should be aware of this. We have shown a relationship between noise and a lower OHS. However, longer follow-up and further study is needed to link noise to a poorly functioning implant

The bearing surface is the critical element in determining the longevity of a total hip arthroplasty. Over the past decade problems associated with bearing surfaces and modular femoral tapers have had an impact on surgeon selection of both acetabular liners and modular femoral heads. The purpose of this study was to analyse THA bearing surface trends from 2007 through 2014 using a large national database. A retrospective review of the Nationwide Inpatient Sample (NIS) database was conducted from 2007 to 2014. All patients who underwent a primary THA were identified using International Classification of Diseases, 9th edition (ICD-9) procedure codes. Bearing surface data was extracted by identifying patients with ICD-9 procedure modifier codes. Patient and hospital characteristics were recorded for each patient. Descriptive statistics were employed to characterise bearing surface trends for the following bearing surfaces: metal on polyethylene (MoP); ceramic on polyethylene (CoP); ceramic on ceramic (CoC) and metal on metal (MoM). Univariate analysis was performed to identify differences between the bearing surface groups. During the study period, 2,460,640 primary THA discharges were identified, of which 1,059,825 (43.1%) had bearing surface data available for further analysis. The breakdown of the bearing surfaces used for these THAs were as follows: MoP − 49.1% (496,713); CoP − 29.1% (307,907); CoC − 4.2% (44,823); and MoM − 19.9% (210,381). MoM utilization peaked in 2008 with 51,033 cases representing 40.1% of THAs implanted that year. The usage steadily declined and by 2014 there were only 6,600 MoM cases representing only 4.0% of the THAs. From 2007 to 2014, the use of CoP bearing surfaces increased from 11,482 discharges (11.1% of cases) in 2007, to 83,300 discharges (50.8% of cases) in 2014. CoP utilization surpassed MoP in 2014. MoP accounted for 54.7% of discharges in 2011 and just 42.1% in 2014. During the study period, MoM bearing surface usage declined precipitously, while CoP surpassed MoP as the most prevalent bearing surface used in total hip arthroplasty patients. These changes in bearing surface usage over time were clearly influenced by concerns regarding high failure rates associated with MoM articulations and reports of taper corrosion associated with modular metal femoral heads

Ceramic-on-polyethylene (COP) bearings have traditionally been reserved for younger patients that were at high risk of polyethylene wear requiring revision. With the 1999 advent of highly crosslinked polyethylene (XLP), wear with XLP has not been a cause for revision. Simulator studies have not shown a difference in wear comparing COP to metal-on-polyethylene (MOP). Therefore, and considering the additional cost of COP, we have until recently not needed COP. However, a 2012 report of 10 cases that developed an adverse reaction to metal debris generated by head neck corrosion has resulted in COP becoming the most common bearing surface as reported by the American Joint Replacement Registry. This reactionary change has occurred despite the fact that we do not understand the cause, do not know the frequency, if it is more common in some implants than others, and we do not know the additional cost or markup of ceramic heads. One study reported a 3.2% revision prevalence caused by mechanically assisted crevice corrosion (MACC) at the head neck junction of a single manufacturer's implant. Other studies have estimated the frequency to be less than 5%. COST IS THE CONCERN in a value based healthcare environment. Models for and against the wholesale use of COP have been proposed and are based on variables that are unknown, including estimated frequency of the problem and the incrementally higher cost of a ceramic head. I use COP in younger patients that I believe will use their hip for more than 15 years. This is based on my personal experience. I have prospectively followed a series of MOP patients for 5 years and not seen cobalt elevations. I have placed new metal femoral heads on corroded femoral tapers without subsequent failure. I have evaluated the taper junctions of postmortem retrievals and found them virtually free of corrosion. A query of our institutional database for MOP primary hips identified 3012 cases between 2006–2017. Eighty revisions (2.7%) were identified. 2 of the 80 were for MACC representing 2.5% of revisions done on our own patients and 0.07% of our MOP cases. Further, evaluating our most recent all cause 350 revisions (7/2015–10/2017) there were 3 revisions for MACC (0.9%). Each one of us needs to EVALUATE OUR OWN PRACTICE AND MAKE AN EDUCATED, VALUE BASED DECISION whether or not to use COP in all patients

The aim of this study is to investigate whether Metal-on-Metal (MoM) implants result in more chromosome aberrations and increased blood metal ions post-operatively when compared to Metal-on-Polyethylene (MoP) implants. Metal-on-metal arthroplasties are being inserted in increasing numbers of younger patients due to the increased durability and reduced requirement for revision in these implants. Recent studies have raised many concerns over possible genotoxicity of MoM implants. This is a prospective study of patients who have undergone elective total hip replacement, they were selected and then randomised into two groups. Group A received a MoP implant and group B received a MoM implant. Patients are reviewed pre-operatively (control group), at 3 months, 6 months, 1 year and 2 years post-operatively. On each occasion blood tests are taken to quantify metal ion levels (chromium, cobalt, titanium, nickel and vanadium) using HR-ICPMS method and chromosome aberrations in T lymphocytes using 24 colour fluorescent in situ hybridisation (FISH). 53 patients have been recruited to date. 24 of whom had MoP prosthesis and 29 a MoM. 37 of these have had their one year follow-up with blood analysis and 14 have had 2 year follow up. Cobalt and chromium concentration increased during the first 6 months in both MoM and MoP groups, in the MoM group the chromium levels were twice that of MoP group and 12x that of the preoperative samples. Chromosome aberrations occurred in both groups. At 6 months both the MoM and MoP groups showed increase frequency of aneuploidy aberrations with further increases after one year. Structural damage in the form of translocations occurred in the MoM group after one year, but not in the MoP group, by two years there was a profound increase in translocations Preliminary results of this study show that the levels of chromium and cobalt are significantly higher in the MoM group compared to the MoP group. This corresponds to increases in chromosome aberrations in the groups with increases in structural chromosome damage after two years